arXiv2008

Magnetic Circular Dichroism spectroscopy in epitaxial La0.7Sr0.3MnO3 thin films

Magneto optic measurements are a very powerful tool for investigating the polarization of a conduction band as a function of temperature and are used here to study the polarization of the mobile electrons in 50nm LSMO (x=0.3) strained thin films grown epitaxially on single crystalline (001) LaAlO3 (LAO) and (001) lattice matched substrate (LSAT). The magnetic circular dichroism (MCD) has been investigated in magnetic fields up to 0.5 T and over a temperature range (10 to 450 K). The MCD spectra of both the films show a peak at the band gap at around 3 eV and the peak is found to be shifted towards lower energy side with the increase of temperature. A separate polaron peak (well known in insulating samples) appears at lower energy (about 1.8 eV) with the increase of temperature in all these metallic films. The rapid decrease in conduction band polarization in the film on LAO has strong implications for the use of these manganites in room temperature spintronics.

cond-mat.str-el↗

arXiv2007

Two magnetic regimes in doped ZnO corresponding to a dilute magnetic semiconductor and a dilute magnetic insulator

Films of ZnO doped with magnetic ions, Mn and Co and, in some cases, with Al have been fabricated with a very wide range of carrier densities. Ferromagnetic behaviour is observed in both insulating and metallic films, but not when the carrier density is intermediate. Insulating films exhibit variable range hopping at low temperatures and are ferromagnetic at room temperature due to the interaction of the localised spins with static localised states. The magnetism is quenched when carriers in the localised states become mobile. In the metallic (degenerate semiconductor) range, robust ferromagnetism reappears together with very strong magneto-optic signals and room temperature anomalous Hall data. This demonstrates the polarisation of the conduction bands and indicates that, when ZnO is doped into the metallic regime, it behaves as a genuine magnetic semiconductor.

cond-mat.mtrl-sci↗