arXiv2016

Exceptional magneto-electric coupling and spontaneous electric polarization in anti-ferromagnet Co4Nb2O9

Synthesis and extensive structural, pyroelectric, magnetic, dielectric and magneto-electric characterizations are reported for polycrystalline Co4Nb2O9 towards unraveling the multiferroic state especially in reference to the magnetic spin flop transition. Magnetic measurements confirm the Co4Nb2O9 becomes antiferromagnetic (AFM) at around 28 K but no clear evidence for spin-flop effect was found. Associated with the magnetic phase transition, a sharp peak in pyroelectric current indicates the appearance of the strong magneto-electric coupling below Neel temperature (TN) with a large coupling constant upto 17.8 uC/m^2T. Using temperature oscillation technique, we establish Co4Nb2O9 to be a genuine multiferroic with spontaneous electric polarization in the anti-ferromagnetic state.

cond-mat.mtrl-sci↗

arXiv2014

Effect of dilution of both A- and B- sites on the multiferroic properties of spinal Mott insulators

The structural, magnetic, electrical and transport properties of FeV2O4, by doping Li and Cr ions respectively in A and B sites, have been studied. Dilution of A-site by Li doping increases the ferri-magnetic ordering temperature and decreases the ferroelectric transition temperature. This also decreases the V-V distances which in effect increases the A-V coupling. This increased A-V coupling dominates over the decrease in A-V coupling due to doping of non-magnetic Li. On the other hand, Cr doping increases the ferri-magnetic ordering temperature but does not alter the ferroelectric transition temperature which is due to the fact that the polarization origin to the presence of almost non-substituted regions.

cond-mat.str-el↗

arXiv2014

Improper Ferroelectricity in Helicoidal Antiferromagnet Cu3Nb2O8

Cu3Nb2O8 is an unusual multiferroic compound that undergoes a series of magnetic ordering at low temperatures. Concurrent development of electric polarization has been reported at TN1 ~25 K corresponding to a non-collinear helicoidal ordering (Phys. Rev. Lett. 107, 137205 (2011)). But questions remain on the microscopic origin of such phenomena. In this communication, we report a detailed study of induced polar ordering in Cu3Nb2O8 by performing polarization, magnetization, dielectric constant and heat capacity measurements over a broad range of temperature and magnetic field. The dielectric constant shows suppression in the magnetic field but it does not shift to lower temperature with the application of external field. The appearance of magneto-dielectric effect signifies the contribution of q-dependent magnetic correlation function with enhanced weightage in the presence of magnetic field. This magnetic correlation function is associated with the ferro-axial vector and our overall results support this mechanism for the observation of muliferroicity in Cu3Nb2O8.

cond-mat.str-el↗

arXiv2014

Magnetic entropy change and critical exponents in double perovskite Y2NiMnO6

We report on the magnetic entropy change and the critical exponents in the double perovskite manganite Y2NiMnO6 with a ferromagnetic to paramagnetic transition TC=85K. For a magnetic field change of 80kOe, a maximum magnetic entropy change -6.57 J /kg K is recorded around TC. The corresponding relative cooling power (134 J / kg) is appreciable towards potential application as a magnetic refrigerant. The critical exponents, beta and gamma satisfy well to values derived for a 3D Heisenberg ferromagnet.

cond-mat.mtrl-sci↗

arXiv2013

Evidence for Multiferroic Characteristics in NdCrTiO5

We report NdCrTiO5 to be an unusual multiferroic material with large magnetic field dependent electric polarization. While magneto-electric coupling in this two magnetic sub-lattice oxide is well established, the purpose of this study is to look for spontaneous symmetry breaking at the magnetic transition. The conclusions are based on extensive magnetization, dielectric and polarization measurements around its antiferromagnetic ordering temperature of 18K. Room temperature X-ray diffraction pattern of NdCrTiO5 reveals that the sample is single phase with an orthorhombic crystal structure that allows linear magneto-electric coupling. DC magnetization measurement shows magnetization downturn at 11K together with a small kink corresponding to the Co+3 sub-lattice ordering at ~18K. An anomaly in dielectric constant is observed around the magnetic ordering temperature that increases substantially with increasing magnetic field. Through detailed pyroelectric current measurements at zero magnetic field, particularly as a function of thermal cycling, we establish that NdCrTiO5 is a genuine multiferroic material that is possibly driven by collinear magneto-striction.

cond-mat.mtrl-sci↗

arXiv2013

Magnetism driven ferroelectricity above liquid nitrogen temperature in Y2CoMnO6

We report multiferroic behavior in double perovskite Y2CoMnO6 with ferroelectric transition temperature Tc = 80K. The origin of ferroelectricity is associated with magnetic ordering of Co2+ and Mn4+ moments in a up-up-down-down arrangement. The saturation polarization and magnetization are estimated to be 65 uC/m2 and 6.2 Bohr magneton/f.u. respectively. The magnetoelectric coupling parameter, on the other hand, is small as a 5 Tesla field suppresses the electric polarization by only ~8%. This is corroborated with observed hysteretic behaviour at 5K that remains unsaturated even upto 7 Tesla. A model based on exchange-striction is proposed to explain the observed high temperature ferroelectricity.

cond-mat.mtrl-sci↗

arXiv2013

Appearance of superconductivity in new BiS2 based layered LaO0.5F0.5BiS2

We report here synthesis, structural, DC magnetization, and transport studies of new BiS2 based layered LaO0.5F0.5BiS2 superconductor [1]. The sample was synthesized by conventional solid state route via vacuum encapsulation technique at 800oC for 12h. LaO0.5F0.5BiS2 crystallizes in tetragonal P4/nmm space group with lattice parameters a = 4.0703(5)Å, c = 13.3902(4)Å. Bulk superconductivity is confirmed with superconducting transition temperature (Tc) of 2.7K by DC magnetization measurements. The Isothermal magnetization (MH) measurements showed closed loops with clear signatures of flux pinning and irreversible behavior. The resistivity measurements confirmed an onset Tc of 2.7K. The magneto-transport ρ(T,H) measurements showed a resistive broadening and decrease in Tc (ρ=0) to lower temperatures with increasing magnetic field. The magnetic phase diagram involving upper critical and irreversibility fields as a function of temperature has been ascertained. Our DC magnetization and electrical transport measurements confirm the appearance of bulk superconductivity in LaO0.5F0.5BiS2 superconductor.

cond-mat.supr-con↗