Formation of Ag and Au Plasmonic Nanoparticles by Ion Implantation in Ga$_2$O$_3$ thin films
Gallium oxide (Ga$_2$O$_3$) is a wide-bandgap semiconductor with exceptional electrical and optical properties, making it a promising material for optoelectronic and sensing applications. In this work, we demonstrate for the first time the formation of plasmonic silver (Ag) and gold (Au) nanoparticles embedded in Ga$_2$O$_3$ thin films via ion implantation. Ga$_2$O$_3$ films deposited by RF sputtering on sapphire substrates were implanted with Ag or Au ions at 150 keV and a nominal fluence of 5 $\times$ 10$^{16}$ ions/cm$^2$, followed by thermal annealing between 200 and 700 °C. Rutherford backscattering spectrometry (RBS) measurements revealed saturation effects during implantation, resulting in lower incorporated fluences, as well as out-diffusion with post-implantation annealing. Transmission electron microscopy confirmed the formation of metallic nanoparticles with a distribution consistent with the metal profiles measured by RBS. Optical absorption measurements showed a pronounced localized surface plasmon resonance (LSPR) band in the Ag-implanted films, visible even in the as-implanted state and red-shifting with increasing annealing temperature, while Au-implanted films exhibited a distinct LSPR peak only after annealing at $\geq$500 °C. The observed LSPR shifts with annealing are attributed primarily to changes in the Ga$_2$O$_3$ matrix rather than a change in nanoparticle size. These results establish ion implantation as a viable approach for integrating plasmonic nanostructures into Ga$_2$O$_3$.