Synthesis of Bulk Superconducting LiNbO$_2$ Crystals through CaH$_2$ Reduction

We have synthesized layered superconducting LiNbO$_2$ crystals through a bulk phase transformation from LiNbO$_3$ single crystals via CaH$_2$ reduction. As the Nb valence is reduced from 5+ to 3+, the material undergoes a structural transformation to the resulting product, LiNbO$_2$, which is accompanied by metallic behavior and a superconducting transition, Tc onset, as high as 14.4 K. Secondary ion mass spectroscopy (SIMS) and X-ray photoelectron spectroscopy (XPS) show that the resulting phase is hole-doped through de-lithiation during the reduction. Magnetization and AC susceptibility measurements from a tunnel diode resonator confirm the bulk nature of superconductivity with a superconducting volume fraction of approximately 77% and an upper critical field approaching 26 T. Our study demonstrates extreme hydride reduction as an effective method to induce phase transformations with non-topotactic pathways and can be used to synthesize bulk materials with exotic properties.

cond-mat.supr-con↗

arXiv2020

Layering of magnetic nanoparticles at amorphous magnetic templates with perpendicular anisotropy

We reveal the assembly of monodisperse magnetite nanoparticles of sizes 5 nm, 15 nm and 25 nm from dilute water-based ferrofluids onto an amorphous magnetic template with out-of-plane anisotropy. From neutron reflectometry experiments we extract density profiles and show that the particles self-assemble into layers at the magnetic surface. The layers are extremely stable against cleaning and rinsing of the substrate. The density of the layers is determined by and increases with the remanent magnetic moment of the particles.

cond-mat.soft↗

arXiv2014

Determination of the effective transverse coherence of the neutron wave packet as employed in reflectivity investigations of condensed matter structures Part I: Measurements

The primary purpose of this investigation is to determine the effective coherent extent of the neutron wave packet transverse to its mean propagation vector k, when it is prepared in a typical instrument used to study the structure of materials in thin film form via specular reflection. There are two principal reasons for doing so. One has to do with the fundamental physical interest in the characteristics of a free neutron as a quantum object while the other is of a more practical nature, relating to the understanding of how to interpret elastic scattering data when the neutron is employed as a probe of condensed matter structure on an atomic or nanometer scale. Knowing such a basic physical characteristic as the neutron's effective transverse coherence can dictate how to properly analyze specular reflectivity data obtained for material film structures possessing some amount of in-plane inhomogeneity. In this study we describe a means of measuring the effective transverse coherence length of the neutron wave packet by specular reflection from a series of diffraction gratings of different spacings. Complementary non-specular measurements of the widths of grating reflections were also performed which corroborate the specular results. (Part I principally describes measurements interpreted according to the theoretical picture presented in Part II.) Each grating was fabricated by lift-off photo-lithography patterning of a nickel film (approximately 1000 Angstroms thick) formed by physical vapor deposition on a flat silicon crystal surface. The grating periods ranged from 10 microns (5 microns Ni stripe, 5 microns intervening space) to several hundred microns. The transverse coherence length, modeled as the width of the wave packet, was determined from an analysis of the specular reflectivity curves of the set of gratings.

cond-mat.mtrl-sci↗