arXiv2010

Morphology Characterization of Argon-Mediated Epitaxial Graphene on C-face SiC

Epitaxial graphene layers were grown on the C-face of 4H- and 6H-SiC using an argon-mediated growth process. Variations in growth temperature and pressure were found to dramatically affect the morphological properties of the layers. The presence of argon during growth slowed the rate of graphene formation on the C-face and led to the observation of islanding. The similarity in the morphology of the islands and continuous films indicated that island nucleation and coalescence is the growth mechanism for C-face graphene.

cond-mat.mtrl-sci↗

arXiv2009

Epitaxial Graphene Growth on SiC Wafers

An in vacuo thermal desorption process has been accomplished to form epitaxial graphene (EG) on 4H- and 6H-SiC substrates using a commercial chemical vapor deposition reactor. Correlation of growth conditions and the morphology and electrical properties of EG are described. Raman spectra of EG on Si-face samples were dominated by monolayer thickness. This approach was used to grow EG on 50 mm SiC wafers that were subsequently fabricated into field effect transistors with fmax of 14 GHz.

cond-mat.mtrl-sci↗

arXiv2009

Correlating Raman Spectral Signatures with Carrier Mobility in Epitaxial Graphene: A Guide to Achieving High Mobility on the Wafer Scale

We report a direct correlation between carrier mobility and Raman topography of epitaxial graphene (EG) grown on silicon carbide (SiC). We show the Hall mobility of material on the Si-face of SiC [SiC(0001)] is not only highly dependent on thickness uniformity but also on monolayer strain uniformity. Only when both thickness and strain are uniform over a significant fraction (> 40%) of the device active area does the mobility exceed 1000 cm2/V-s. Additionally, we achieve high mobility epitaxial graphene (18,100 cm2/V-s at room temperature) on the C-face of SiC [SiC(000-1)] and show that carrier mobility depends strongly on the graphene layer stacking. These findings provide a means to rapidly estimate carrier mobility and provide a guide to achieve very high mobility in epitaxial graphene. Our results suggest that ultra-high mobilities (>50,000 cm2/V-s) are achievable via the controlled formation of uniform, rotationally faulted epitaxial graphene.

cond-mat.mtrl-sci↗