arXiv2026

Defect-controlled twin activation in crystallographically equivalent magnesium micropillars

Tensile twinning plays a central role in accommodating -axis plasticity in Mg. In bulk Mg, it typically shows a relatively deterministic response with a low critical stress, whereas in confined volumes it exhibits broad yield-stress distributions that complicate the prediction of small-scale mechanical behavior. Here, site-specific compression tests are performed on 4 $μ$m-diameter pillars fabricated in a parent Mg crystal and an adjacent {10-12} twin. The two regions share the same [11-20] compression axis but experienced different prior deformation histories, allowing the influence of the residual microstructural state to be examined at fixed crystallographic orientation. Among 27 pillars, most parent-region pillars yield near 300 MPa, whereas pillars from the twin region span approximately 30 to 300 MPa. Interrupted tests combined with cross-sectional EBSD link individual load drops to discrete twin formation and further show that a pillar containing a pre-existing twin yields at approximately 80 MPa through the migration of the existing twin boundary. Molecular dynamics simulations of 30 nm-diameter pillars resolve possible atomistic pathways at the nanoscale. The simulations illustrate how contact geometry and pre-existing twin embryos alter event selection, and how an activated twin advances rapidly, while coherent twin boundary migration proceeds through disconnection motion accompanied by crystallographically required atomic shuffles. The results attribute the experimental scatter to the local availability of embryos and mobile interfaces, such that the first plastic event is governed by the twinning pathway accessible from the local microstructural state rather than by a single characteristic critical stress. Deformation history can therefore strongly modify the distribution of first plastic events even when the loading orientation is fixed.

cond-mat.mtrl-sci↗

arXiv2026

Zonal dislocations in Laves phases: A coupled synchro-shear slip mechanism

Synchro-shear is the primary plastic deformation mechanism in Laves phases at elevated temperatures, mediated by synchro-Shockley partial dislocations-zonal dislocations that proceed via localized events such as kink-pair nucleation and propagation. Using atomistic simulations, we identified a novel slip mechanism in Laves phases, namely coupled synchro-shear slip, involving the synchronized glide of two synchro-Shockley partial dislocations on adjacent slip planes, leading to the formation of extrinsic stacking faults. High-resolution scanning transmission electron microscopy revealed the extended core structures consistent with coupled synchro-Shockley partial dislocations bounded by extrinsic stacking faults in C15 NbCr2 and their involvement in twinning. These results highlight the critical role of coupled synchro-shear slip in enabling phase transformations between Laves polytypes and in governing twinning behavior, providing new atomistic insight into the kinetic nature of plasticity in topologically close-packed intermetallic phases.

cond-mat.mtrl-sci↗

arXiv2025

Solute Co-Segregation Mechanisms at Low-Angle Grain Boundaries in Magnesium: A Combined Atomic-Scale Experimental and Modeling Study

Solute segregation at low-angle grain boundaries (LAGBs) critically affects the microstructure and mechanical properties of magnesium (Mg) alloys. In modern alloys containing multiple substitutional elements, understanding solute-solute interactions at microstructural defects becomes essential for alloy design. This study investigates the co-segregation mechanisms of calcium (Ca), zinc (Zn), and aluminum (Al) at a LAGB in a dilute AZX010 Mg alloy by combining atomic-scale experimental and modeling techniques. Three-dimensional atom probe tomography (3D-APT) revealed significant segregation of Ca, Zn, and Al at the LAGB, with Ca forming linear segregation patterns along dislocation arrays characteristic of the LAGB. Clustering analysis showed increased Ca-Ca pairs at the boundary, indicating synergistic solute interactions. Atomistic simulations and elastic dipole calculations demonstrated that larger Ca atoms prefer tensile regions around dislocations, while smaller Zn and Al atoms favor compressive areas. These simulations also found that Ca-Ca co-segregation near dislocation cores is energetically more favorable than other solute pairings, explaining the enhanced Ca clustering observed experimentally. Thermodynamic modeling incorporating calculated segregation energies and solute-solute interactions accurately predicted solute concentrations at the LAGB, aligning with experimental data. The findings emphasize the importance of solute interactions at dislocation cores in Mg alloys, offering insights for improving mechanical performance through targeted alloying and grain boundary engineering.

cond-mat.mtrl-sci↗

arXiv2025

Predicting Grain Boundary Segregation in Magnesium Alloys: An Atomistically Informed Machine Learning Approach

Grain boundary (GB) segregation in magnesium (Mg) substantially influences its mechanical properties and performance. Atomic-scale modelling, typically using ab-initio or semi-empirical approaches, has mainly focused on GB segregation at highly symmetric GBs in Mg alloys, often failing to capture the diversity of local atomic environments and segregation energies, resulting in inaccurate structure-property predictions. This study employs atomistic simulations and machine learning models to systematically investigate the segregation behavior of common solute elements in polycrystalline Mg at both 0 K and finite temperatures. The machine learning models accurately predict segregation thermodynamics by incorporating energetic and structural descriptors. We found that segregation energy and vibrational free energy follow skew-normal distributions, with hydrostatic stress, an indicator of excess free volume, emerging as an important factor influencing segregation tendency. The local atomic environment's flexibility, quantified by flexibility volume, is also crucial in predicting GB segregation. Comparing the grain boundary solute concentrations calculated via the Langmuir-McLean isotherm with experimental data, we identified a pronounced segregation tendency for Nd, highlighting its potential for GB engineering in Mg alloys. This work demonstrates the powerful synergy of atomistic simulations and machine learning, paving the way for designing advanced lightweight Mg alloys with tailored properties.

cond-mat.mtrl-sci↗

arXiv2024

Grain boundary segregation spectrum in basal-textured Mg alloys: From solute decoration to structural transition

Mg alloys are promising lightweight structural materials due to their low density and excellent mechanical properties. However, their limited formability and ductility necessitate improvements in these properties, specifically through texture modification via grain boundary segregation. While significant efforts have been made, the segregation behavior in Mg polycrystals, particularly with basal texture, remains largely unexplored. In this study, we performed atomistic simulations to investigate grain boundary segregation in dilute and concentrated solid solution Mg-Al alloys. We computed the segregation energy spectrum of basal-textured Mg polycrystals, highlighting the contribution from specific grain boundary sites, such as junctions, and identified a newly discovered bimodal distribution which is distinct compared to the conventional skew-normal distribution found in randomly-oriented polycrystals. Using a hybrid molecular dynamics/Monte Carlo approach, we simulated segregation behavior at finite temperatures, identifying grain boundary structural transitions, particularly the varied fraction and morphology of topologically close-packed grain boundary phases when changing thermodynamic variables. The outcomes of this study offer crucial insights into basal-textured grain boundary segregation and phase formation, which can be extended to other relevant Mg alloys containing topologically close-packed intermetallics.

cond-mat.mtrl-sci↗

arXiv2023

The Origin of Deformation Induced Topological Anisotropy in Silica Glass

Oxide glasses with a network structure are omnipresent in daily life. Often, they are regarded as isotropic materials; however, structural anisotropy can be induced through processing in mechanical fields and leads to unique materials properties. Unfortunately, due to the lack of local, atomic-scale analysis methods, the microscopic mechanisms leading to anisotropy remained elusive. Using novel analysis methods on glasses generated by molecular dynamics simulations, this paper provides a microscopic understanding of topological anisotropy in silica (SiO$_2$) glass under mechanical loads. The anisotropy observed in silica glass originates from a preferred orientation of SiO$_4$ tetrahedra at both short- and medium-range levels that can be controlled via the mode of mechanical loading. The findings elucidate the relation between the deformation protocol and the resulting anisotropic structure of the silica network (involving both persistent and transient effects), and thus provide important insight for the design of oxide glasses with tailored materials properties.

cond-mat.mtrl-sci↗

arXiv2023

Thermally activated nature of synchro-Shockley dislocations in Laves phases

Synchro-Shockley dislocations, as zonal dislocation, are the major carrier of plasticity in Laves phases at high temperatures. The motion of synchro-Shockley dislocations is composed of localized transition events, such as kink-pair nucleation and propagation, which possess small activation volumes, presumably leading to sensitive temperature and strain rate dependence on the Peierls stress. However, the thermally activated nature of synchro-Shockley dislocation motion is not fully understood so far. In this study, the transition mechanisms of the motion of synchro-Shockley dislocations at different shear and normal strain levels are studied. The transition processes of dislocation motion can be divided into shear-sensitive and -insensitive events. The external shear strain lowers the energy barriers of shear-sensitive events. Thermal assistance is indispensable in activating shear-insensitive events, implying that the motion of synchro-Shockley dislocations is prohibited at low temperatures.

cond-mat.mtrl-sci↗

arXiv2023

Unveiling the mechanisms of motion of synchro-Shockley dislocations in Laves phases

In Laves phases, synchroshear is the dominant basal slip mechanism. It is accomplished by the glide of synchro-Shockley dislocations. However, the atomic-scale mechanisms of motion of such zonal dislocations are still not well understood. In this work, using atomistic simulations, two 30\textdegree{} synchro-Shockley dislocations with different Burgers vectors and core structures and energies are identified. We demonstrate that nucleation and propagation of kink pairs is the energetically favorable mechanism for the motion of the synchro-Shockley dislocation (partial I). Vacancy hopping and interstitial shuffling are identified as two key mechanisms related to kink propagation and we investigated how vacancies and antisite defects assist kink nucleation and propagation, which is crucial for kink mobility. Additionally, we identified a mechanism of non-sequential atomic shuffling for the motion of the synchro-Shockley dislocation (partial II). These findings provide insights into the dependency on temperature and chemical composition of plastic deformation induced by zonal dislocations in Laves phases and the many related topologically close-packed phases.

cond-mat.mtrl-sci↗

arXiv2023

Features of a nano-twist phase in the nanolayered Ti3AlC2 MAX phase

Complex intermetallic materials known as MAX phases exhibit exceptional properties from both metals and ceramics, largely thanks to their nanolayered structure. With high-resolution scanning transmission electron microscopy supported by atomistic modelling, we reveal atomic features of a nano-twist phase in the nanolayered \MAX. The rotated hexagonal single-crystal is encompassed within basal symmetric twist interfaces similar to grain boundaries. In particular, we show that air-oxidation at \SI{1000}{\celsius} can form a twisted phase that leads to the formation of interfacial dislocation networks with screw characters or to severe interfacial reconstructions. Additionally, we explore the contribution of disclinations to the representation by continuum models of the stress field generated by such nano-twist defect in the \MAX{} bulk phase. The occurrence of this unexpected defect is expected to impact the physical response of this nanolayered-based material as such supports property-by-design approaches.

cond-mat.mtrl-sci↗

arXiv2023

Atomistic insights into the inhomogeneous nature of solute segregation to grain boundaries in magnesium

In magnesium alloys with multiple substitutional elements, solute segregation at grain boundaries (GBs) has a strong impact on many important material characteristics, such as GB energy and mobility, and therefore, texture. Although it is well established that GB segregation is inhomogeneous, the variation of GB solute composition for random boundaries is still not understood. In the current study, atomic-scale experimental and simulation techniques were used to investigate the compositional inhomogeneity of six different GBs. Three-dimensional atom probe tomography results revealed that GB solute concentration of Nd in Mg varies between 2 to 5 at.%. This variation was not only seen for different GB orientations but also within the GB plane. Correlated atomistic simulations suggest that the inhomogeneous segregation behavior observed experimentally stems from local atomic rearrangements within the GBs and introduce the notion of potential excess free volume in the context of improving the prediction of per-site segregation energies.

cond-mat.mtrl-sci↗

arXiv2023

On the temperature and chemical dependency of prismatic stacking faults in C14 Laves phases

Activation of non-basal slip is essential in improving the deformability of hexagonal crystals. However, the mechanism of non-basal slip remains largely unknown, especially for complex intermetallics such as Laves phases. In this work, the prismatic slip systems of C14 Laves crystals and possible metastable states along the slip paths are assessed using atomistic simulations. Multiple prismatic stacking fault states with the same lattice pattern but different site occupancies and chemical distributions are identified at different inter-atomic layers, temperatures and chemical compositions. The formation of energetically favorable prismatic stacking faults involves short-range diffusion which implies the thermally activated nature of prismatic slip. The outcomes of this work advance the understanding of temperature and chemical-dependent non-basal slip in Laves phases and can be extended to other topologically close-packed phases.

cond-mat.mtrl-sci↗

arXiv2023

Tailoring the plasticity of topologically close-packed phases via the crystals' fundamental building blocks

Brittle topologically close-packed precipitates form in many advanced alloys. Due to their complex structures little is known about their plasticity. Here, we present a strategy to understand and tailor the deformability of these complex phases by considering the Nb-Co μ-phase as an archetypal material. The plasticity of the Nb-Co μ-phase is controlled by the Laves phase building block that forms parts of its unit cell. We find that between the bulk C15-NbCo$_2$ Laves and Nb-Co μ-phase, the interplanar spacing and local elastic modulus of the Laves phase building block change, leading to a strong reduction in hardness and elastic modulus, as well as a transition from synchroshear to crystallographic slip. Furthermore, as the composition changes from Nb$_6$Co$_7$ to Nb$_7$Co$_6$, the Co atoms in the triple layer are substituted such that the triple layer of the Laves phase building block becomes a slab of pure Nb, resulting in inhomogeneous changes in elasticity and a transition from crystallographic slip to a glide-and-shuffle mechanism. These findings open opportunities to purposefully tailor the plasticity of these topologically close-packed phases in bulk, but at the atomic scale of interplanar spacing and local shear modulus of the fundamental crystal building blocks in their large unit cells.

cond-mat.mtrl-sci↗

arXiv2021

Atomistic aspects of load transfer and fracture in CNT-reinforced aluminium

This paper describes atomistic simulations of deformation and fracture of Al reinforced with carbon nanotubes (CNTs). We use density functional theory (DFT) to understand the energetics of Al-graphene interfaces and gain reference data for the parameterization of Al-C empirical potentials. We then investigate the load transfer between CNTs and Al and its effect on composite strengthening. To this end, we perform uniaxial tensile simulations of an Al crystal reinforced with CNTs of various volume fractions. We also study the interaction of the embedded CNTs with a crack. We show that the interaction between CNTs and Al is weak such that, under tensile loading, CNTs can easily slide inside the Al matrix and get pulled out from the cracked surface. This effect is almost independent of CNT length and volume fraction. Little load transfer and consequently no crack bridging are observed during the simulation of pristine CNTs threading the crack surfaces. CNTs that are geometrically fixated inside Al, on the other hand, can increase the fracture stress and enhance plastic dissipation in the matrix. CNTs located in front of a growing crack blunt the crack and induce plastic deformation of the Al matrix. Depending on the CNT orientation, these processes can either increase or decrease the failure stress of the composite.

cond-mat.mtrl-sci↗

arXiv2021

Laves phase crystal analysis (LaCA): Atomistic identification of lattice defects in C14 and C15 topologically close-packed phases

The identification of defects in crystal structures is crucial for the analysis of atomistic simulations. Many methods to characterize defects that are based on the classification of local atomic arrangement are available for simple crystalline structures. However, there is currently no method to identify both, the crystal structures and internal defects of topologically close-packed (TCP) phases such as Laves phases. We propose a new method, Laves phase Crystal Analysis (LaCA), to characterize the atomic arrangement in Laves crystals by interweaving existing structural analysis algorithms. The new method can identify the polytypes C14 and C15 of Laves phases, typical crystallographic defects in these phases, and common deformation mechanisms such as synchroshear and non-basal dislocations. Defects in the C36 Laves phase are detectable through deviations from the periodic arrangement of the C14 and C15 structures that make up this phase. LaCA is robust and extendable to other TCP phases.

cond-mat.mtrl-sci↗

arXiv2021

Exploring the transfer of plasticity across Laves phase interfaces in a dual phase magnesium alloy

The mechanical behaviour of Mg-Al alloys can be largely improved by the formation of an intermetallic Laves phase skeleton, in particular the creep strength. Recent nanomechanical studies revealed plasticity by dislocation glide in the (Mg,Al)$_2$Ca Laves phase, even at room temperature. As strengthening skeleton, this phase remains, however, brittle at low temperature. In this work, we present experimental evidence of slip transfer from the Mg matrix to the (Mg,Al)$_2$Ca skeleton at room temperature and explore associated mechanisms by means of atomistic simulations. We identify two possible mechanisms for transferring Mg basal slip into Laves phases depending on the crystallographic orientation: a direct and an indirect slip transfer triggered by full and partial dislocations, respectively. Our experimental and numerical observations also highlight the importance of interfacial sliding that can prevent the transfer of the plasticity from one phase to the other.

cond-mat.mtrl-sci↗

arXiv2020

Assessment and optimization of the fast inertial relaxation engine (FIRE) for energy minimization in atomistic simulations and its implementation in LAMMPS

In atomistic simulations, pseudo-dynamics relaxation schemes often exhibit better performance and accuracy in finding local minima than line-search-based descent algorithms like steepest descent or conjugate gradient. Here, an improved version of the fast inertial relaxation engine (FIRE) and its implementation within the open-source code LAMMPS is presented. It is shown that the correct choice of time integration scheme and minimization parameters is crucial for performance.

physics.comp-ph↗

arXiv2019

Atomistic Simulations of Basal Dislocations Interacting with Mg$_{17}$Al$_{12}$ Precipitates in Mg

The mechanical properties of Mg-Al alloys are greatly influenced by the complex intermetallic phase Mg$_{17}$Al$_{12}$, which is the most dominant precipitate found in this alloy system. The interaction of basal edge and 30$^\text{o}$ dislocations with Mg$_{17}$Al$_{12}$ precipitates is studied by molecular dynamics and statics simulations, varying the inter-precipitate spacing ($L$), and size ($D$), shape and orientation of the precipitates. The critical resolved shear stress $τ_c$ to pass an array of precipitates follows the usual $\ln((1/D + 1/L)^{-1})$ proportionality. In all cases but the smallest precipitate, the dislocations pass the obstacles by depositing dislocation segments in the disordered interphase boundary rather than shearing the precipitate or leaving Orowan loops in the matrix around the precipitate. An absorbed dislocation increases the stress necessary for a second dislocation to pass the precipitate also by absorbing dislocation segments into the boundary. Replacing the precipitate with a void of identical size and shape decreases the critical passing stress and work hardening contribution while an artificially impenetrable Mg$_{17}$Al$_{12}$ precipitate increases both. These insights will help improve mesoscale models of hardening by incoherent particles.

cond-mat.mtrl-sci↗

arXiv2019

Basal Slip in Laves Phases: the Synchroshear Dislocation

Two different mechanisms have been reported in previous ab initio studies to describe basal slip in complex intermetallic Laves phases: synchroshear and undulating slip. To date, no clear answer has been given on which is the energetically favourable mechanism and whether either of them could effectively propagate as a dislocation. Using classical atomistic simulations supported by ab initio calculations, the present work removes the ambiguity and shows that the two mechanisms are, in fact, identical. Furthermore, we establish synchroshear as the mechanism for propagating dislocations within the basal plane in Laves phases.

cond-mat.mtrl-sci↗