Gate-tunable electronic properties of epitaxial Bi (111) films using a printable hexagonal boron nitride ionogel

Achieving effective electrostatic control of carrier transport in semimetals remains challenging due to strong screening and multiband effects. We report efficient low voltage top gated control of electronic transport in epitaxial Bi (111) thin films grown on GaAs (111) substrates using a printable hexagonal boron nitride ionogel. Magnetotransport measurements reveal pronounced nonlinear Hall conductivities arising from multiband electron and hole contributions. Remarkably, the application of a small gate voltage (less than 0.4 V in magnitude) leads to a systematic evolution of the low field Hall conductivity slope and the electron-hole compensation point. The response to gate voltage depends upon thickness and temperature. The observed behavior cannot be explained by a conventional Fermi level shift with rigid bands and instead indicates a non rigid band response associated with multiband effects and a gat tunable Rashba spin orbit coupling. Our results establish printable ionogel gating as a powerful approach to tune multiband transport in topological semimetals.

cond-mat.mtrl-sci↗

arXiv2025

Synthesis and transport properties of epitaxial Bi (111) films on GaAs (111) substrates

In recent decades, the growth of ultrathin epitaxial bismuth (Bi) films on various substrates has garnered interest due to their unique electronic properties. We report upon the growth and electrical transport properties of epitaxial Bi (111) films in the thickness range of 5-32 nm deposited directly on GaAs (111) substrates, without a buffer layer. The quality of Bi films is found to depend on conditions for substrate treatment using Ar+ ion-milling and annealing. Substrates milled at low ion beam currents display poor surface reconstruction after annealing, which hinders the growth of high-quality films. In contrast, substrates milled under optimized conditions led to reconstructed surfaces upon annealing, resulting in epitaxial Bi films with predominantly single-domain orientation. Although epitaxial films formed in both cases, transport measurements indicated significantly higher conductivity for films grown on optimally treated substrates. Measurements at low temperatures suggest that the transport properties are dominated by a surface state with high mobility electrons. Magneto-transport measurements suggest that conductivity and mobility improve progressively with increasing film thickness. For the thinnest 5 nm film, a hole-like state emerges, presumably as the electron-like state is gapped out. These results provide a robust methodology for growing high-quality epitaxial Bi films on GaAs (111) and offer insights into their unique transport properties, and our ability to tune them.

cond-mat.mtrl-sci↗