arXiv2026

Specific features of the magnetic-field dependences of electrical resistivity in Bi--Mn solid solutions with low Mn content

For the first time, the field dependences of the magnetoresistance of a textured polycrystalline Bi$_{88.08}$Mn$_{11.92}$ sample were investigated in the $H \perp I$ and $H \parallel I$ configurations, and the results were compared with those previously obtained for the solid solution Bi$_{95.69}$Mn$_{3.69}$Fe$_{0.62}$ with a lower manganese concentration. It was demonstrated that the magnetoresistance field dependencies for Bi$_{88.08}$Mn$_{11.92}$ differ significantly from those of Bi$_{95.69}$Mn$_{3.69}$Fe$_{0.62}$ below 100 K, becoming nearly identical as the temperature approaches room temperature. It was established that the maximum relative magnetoresistance values for Bi$_{88.08}$Mn$_{11.92}$ are observed at a magnetic field of 90 kOe and a temperature of 100 K in both the $H \perp I$ and $H \parallel I$ configurations, amounting to 3170\% and 380\%, respectively. These values are significantly lower than those previously reported for the solid solution containing less manganese (Bi$_{95.69}$Mn$_{3.69}$Fe$_{0.62}$), which were 3877\% and 742\%, respectively. Analysis of the results indicates that differences in field dependence among the studied materials are associated with varying amounts of magnetic $\alpha$-BiMn. The anomalous magnetoresistance behavior, as compared with that of pure bismuth, is attributed to the influence of internal magnetism on electrical transport within the bismuth matrix of the studied solid solutions.

cond-mat.mtrl-sci↗

arXiv2025

Study of fluctuation conductivity in YBa$_2$Cu$_3$O$_7$--$\delta$ films in strong magnetic fields

We report the effect of the \emph{ab}-plane magnetic field $B$ up to $8\,\mathrm{T}$ on the resistivity $\rho(T)$ and fluctuation conductivity $\sigma'(T)$ in YBa$_2$Cu$_3$O$_{7-\delta}$ thin films. As expected, up to $\sim 2.5\,\mathrm{T}$ the magnetic field monotonously increases $\rho$, the width of the resistive transition $\Delta T_c$, and the coherence length along the $c$ axis, $\xi_c(0)$, but decreases both $T_c$ and the range of superconducting (SC) fluctuations $\Delta _{\mathrm{fl}}$. The fluctuation conductivity exhibits a crossover at characteristic temperature $T_0$ from the 3D Aslamazov--Larkin (AL) theory near $T_c$ to the 2D fluctuation theory of Maki--Thompson (MT). However, at $B = 3\,\mathrm{T}$, the MT term is completely suppressed, and above $T_0$ $\sigma'(T)$ is unexpectedly described by the fluctuation contribution of 2D AL, suggesting the formation of a two-dimensional vortex lattice in the film under the action of a magnetic field. At the same time, $\Delta T_{\mathrm{fl}}$ sharply increases by a factor of about 7, and $\xi_c(0)$ demonstrates a very unusual dependence on $T_c$ when $B$ increases above $3\,\mathrm{T}$. Our results demonstrate the possibility of the formation of a vortex state in YBCO and its evolution with increasing $B$.

cond-mat.supr-con↗

arXiv2025

Influence of strong electron irradiation on fluctuation conductivity and pseudogap in YBa$_2$Cu$_3$O$_7$--$\delta$ single crystals

The effect of high-energy electron irradiation on the temperature dependences of the resistivity $\rho(T)$, fluctuation conductivity (FLC), and pseudogap (PG) $\Delta^{*}(T)$ of YBa$_2$Cu$_3$O$_7$--$\delta$ (YBCO) single crystals without twins was studied. Irradiation causes a linear increase in $\rho(T)$ and a decrease in the superconducting transition temperature $T_c$ with dose $\phi$. For small $\phi$, the reduction of $T_c$ follows the Abrikosov--Gorkov (AG) pair-breaking theory, while for large $\phi$ it is described by the Emery--Kivelson (EK) model, where quantum phase fluctuations dominate. At $\phi_3 = 2.5 \times 10^{19}$ e/cm$^2$, which corresponds to the AG--EK crossover, the spacing between CuO$_2$ planes $d_{01}$, the coherence length $\xi_c(0)$, and the fluctuation region $T_{\mathrm{fl}}$ increase sharply, and the two-dimensional Maki--Thompson (2D--MT) contribution is replaced by the Aslamazov--Larkin (2D--AL) term. Surprisingly, no signatures of the crossover appear in $\rho(\phi)$ or $T_c(\phi)$. At the same $\phi_3$, a sharp rise in the pseudogap opening temperature $T^{*}$ and in $\Delta^{*}$ indicates a possible reduction of the density of states. With further increase in $\phi$, both PG parameters and their energy scale decrease markedly, and $\Delta^{*}(T)$ acquires an unusual form. However, at $\phi_5 = 5.6 \times 10^{19}$ e/cm$^2$, the temperature dependences of FLC and PG again show behavior typical of well-structured YBCO, regardless of defect density.

cond-mat.supr-con↗

arXiv2024

Evolution of the pseudogap temperature dependence in YBa$_2$Cu$_3$O$_{7-\delta}$ films under the influence of a magnetic field

The evolution of the temperature dependence of pseudogap $\Delta$*(T) in optimally doped (OD) YBa$_2$Cu$_3$O$_{7-\delta}$ (YBCO) films with $T_{c}$ = 88.7 K under the influence of a magnetic field $B$ up to 8 T has been studied in detail. It has been established that the shape of $\Delta$*(T) for various $B$ over the entire range from the pseudogap opening temperature $T$* to $T_{01}$, below which superconducting fluctuations occur, has a wide maximum at the BEC-BCS crossover temperature $T_{pair}$, which is typical for OD films and untwinned YBCO single crystals. $T$* was shown to be independent on $B$, whereas $T_{pair}$ shifts to the low temperature region along with increase of $B$, while the maximum value of $\Delta$*($T_{pair}$) remains practically constant regardless of $B$. It was revealed that as the field increases, the low-temperature maximum near the 3D-2D transition temperature $T_{0}$ is blurred and disappears at $B$ > 5 T. Moreover, above the Ginzburg temperature $T_{G}$, which limits superconducting fluctuations from below, at $B$ > 0.5 T, a minimum appears on $\Delta$*(T) at $T_{min}$, which becomes very pronounced with a further increase in the field. As a result, the overall value of $\Delta$*(T) decreases noticeably most likely due to pair-breaking affect of a magnetic field. A comparison of $\Delta$*(T) near $T_{c}$ with the Peters-Bauer theory shows that the density of fluctuating Cooper pairs actually decreases from < > $\approx$ 0.31 at $B$ = 0 to < > $\approx$ 0.28 in the field 8 T. The observed behavior of $\Delta$*(T) around $T_{min}$ is assumed to be due to the influence of a two-dimensional vortex lattice created by the magnetic field, which prevents the formation of fluctuating Cooper pairs near $T_{c}$.

cond-mat.supr-con↗

arXiv2022

Temperature dependence of upper critical fields and coherence lengths for optimally-doped $YBa_2Cu_3O_{7-\delta}$ thin films

We report the comprehensive comparative analysis of the upper critical magnetic fields $\mu_{0}H_{c2}(0)$ obtained within Ginzburg-Landau and Werthamer-Helfand-Hohenberg theories for optimally-doped $YBa_2Cu_3O_{7-\delta}$ thin films. For different orientations of the magnetic field, our calculations give 638 and 153 T for $\mu_{0}H_{c2}(0)$, H || ab and $\mu_{0}H_{c2}(0)$, H || c, respectively, when using $H_{c2}(0)$. For the first time, the temperature dependences of coherence lengths $\xi_{ab}(T)$ and $\xi_{c}(T)$ within proposed theories were determined using 50 and 90% criteria of the normal state resistivity value $\rho_{N}$. The Ginzburg-Landau 0.9$\rho_{N}$ approach gives $\xi_{ab}(0)$=11.8 A, and $\xi_{c}(0)$=3.0 A which are in a good agreement with literature data. The implications of very short coherence lengths in HTSCs are discussed.

cond-mat.supr-con↗

arXiv2021

Filamentary superconductivity of resistively-switched strontium titanate

SrTiO$_3$, although a wide gap insulator, has long been known to become metallic and superconducting at extremely low doping levels. This has given rise to questions concerning the coexistence or interdependence of metallicity, superconductivity, and the material's polar properties. This issue becomes especially intriguing in conjunction with the observation that filamentary metallicity can be induced by means of resistive switching at conditions well below relevant doping levels for homogeneous metallicity. In this study, we demonstrate that resistive switching can also be employed to generate superconductivity at the superconducting transition temperature of $T_c$ $\approx$ 0.2 K in SrTiO$_3$. By combining local characterization of the conductivity with theoretical analysis, we propose that the superconducting properties are associated with the electro-formation of columnar-like bundles with a diameter of 40-50 nm, consisting of metallic filaments surrounded by polar regions. We provide a theoretical model identifying the coexistence of metallic and polar regions as a prerequisite for the filamentary-like superconductivity observed.

cond-mat.supr-con↗

arXiv2020

Fluctuating Cooper pairs in FeSe at temperatures exceeding double Tc

Temperature dependencies of excess conductivity, Sigma', have been studied in detail for three FeSe_{0.94} textured polycrystalline samples prepared by partial melting and solid state reaction. It was revealed that both Sigma' and its temperature dependence are extremely sensitive to the method of sample preparation. Then, it was shown that in the range from the superconducting transition temperature Tc ~ 9 K up to the characteristic temperature T_01 ~ 19 K, Sigma'(T) obeys the classical fluctuation theories of Aslamazov-Larkin (AL) and Hikami-Larkin (Maki-Thompson (MT) term) pointing to the existence of fluctuating Cooper pairs in FeSe at temperatures exceeding double Tc. Like in cuprates, AL-MT crossover at T_0 < T_{01} is observed, which means the appearance of 3D-2D dimensional transition at this temperature. This allows us to determine the coherence length along the c-axis, Xi_c(0) ~ 3 A, and a set of additional samples' parameters, including the phase relaxation time, Tau_{Phi}, of fluctuating Cooper pairs, within a simple two-dimensional free-carrier picture. It was shown that Tau_{Phi} in FeSe coincides with that found for YBa2Cu3O7 suggesting that the nature of superconducting fluctuations is very similar for these high-temperature superconductors of different types.

cond-mat.supr-con↗

arXiv2019

BKT transition observed in magnetic and electric properties of YBa$_2$Cu$_3$O$_{7-\delta}$ single crystals

Superconductivity of YBa$_2$Cu$_3$O$_{7-\delta}$ single crystals was investigated in small magnetic fields. In magnetic measurements the superconducting transition for $\textbf{H} \| c$ appears 0.4 K higher than for $\textbf{H} \bot c$. In this temperature range superconductivity is two-dimensional and the total thickness of superconducting layers is about 0.83 of the sample thickness, which is a consequence of the occurrence of the quasi-insulating plane in the unit cell of the crystal structure. Resistivity in the \textit{ab}-plane and along the \textit{c}-axis was measured simultaneously. In these measurements two-dimensional superconductivity was observed in a temperature range of 0.6-0.8 K with the clear signs of the Berezinskii-Kosterlitz-Touless (BKT) transition which occurs approximately 0.15 K below $T_c$, the mean-field transition temperature.

cond-mat.supr-con↗

arXiv2018

Specific temperature dependence of pseudogap in YBa$_2$Cu$_3$O$_{7-\delta}$ nanolayers

The pseudogap (PG) derived from the analysis of the excess conductivity $\sigma'(T)$ in superlattices and double-layer films of $YBa_2Cu_3O_{7-\delta}$-$PrBa_2Cu_3O_{7-\delta}$(YBCO-PrBCO), prepared by pulsed laser deposition, is studied for the first time. The $\sigma'(T)$ analysis has been performed within the local-pair (LP) model based on the assumption of the paired fermion (LPs) formation in the cuprate high-$T_c$ superconductors (cuprates) below the representative temperature $T^*\gg T_c$ resulting in the PG opening. Within the model, the temperature dependencies of the PG, $\Delta^*(T)$, for the samples with different number of the PrBCO layers ($N_{Pr}$) were analyzed in the whole temperature range from $T^*$ down to $T_c$. Near $T_c$, excess conductivity was found to be perfectly described by the Aslamasov-Larkin and Hikami-Larkin (Maki-Thompson term) fluctuation theories, suggesting the presence of superconducting fluctuations in a relatively large (up to 15 K) temperature range above $T_c$. All sample parameters were found to change with increase of $N_{Pr}$, finally resulting in the appearance of the pronounced maximum of $\Delta^*(T)$ at high temperatures. The result is most likely due to increasing influence of the intrinsic magnetism of PrBCO ($\mu_{Pr}\approx 4\,\mu_B$) and suggests the possibility to search in that way the change of interplay between the superconductivity and magnetism in cuprates.

cond-mat.supr-con↗

arXiv2015

Change of the charge modulation during superconducting transition in SmFeAsO(0.91)F(0.09) seen by 57Fe Mössbauer spectroscopy

Iron-based superconductor SmFeAsO(0.91)F(0.09) has been investigated by the 57Fe Moessbauer spectroscopy versus temperature with the special attention paid to the region of the superconducting transition at about 47 K. Modulation of the electron charge density was found. It leads to the development of the charge density wave (CDW) and electric field gradient wave (EFGW). The modulation of CDW is enhanced in the temperature region of the superconducting gap opening, while the amplitude of EFGW is partly suppressed within this temperature region. This effect is exactly opposite to the similar effect in Ba(0.6)K(0.4)Fe2As2 superconductor. Hence, it seems that d electrons contribute significantly to the Cooper pair formation in both compounds as EFGW is perturbed within the temperature region of the superconducting gap formation.

cond-mat.supr-con↗

arXiv2015

Fluctuation conductivity and possible pseudogap state in FeAs-based superconductor EuFeAsO(0.85)F(0.15)

The study of excess conductivity $\sigma'(T)$ in the textured polycrystalline FeAs-based superconductor $EuFeAsO_{0.85}F_{0.15}$ ($T_c = 11\, K$) prepared by the solid state synthesis is reported. The $\sigma'(T)$ analysis has been performed within the Local Pair (LP) model based on the assumption of the LP formation in cuprate high-$T_c$ superconductors (cuprates) below the pseudogap (PG) temperature $T^*\gg T_c$. Similarly to the cuprates, near $T_c$ $\sigma'(T)$ is adequately described by the 3D term of the Aslamasov-Larkin (AL) theory but the range of the 3D-AL fluctuations, $\Delta T_{3D}$, is relatively short. Above the crossover temperature $T_0 \approx 11.7\,K$ $\sigma'(T)$ is described by the 2D Maki-Thompson (MT) fluctuation term of the Hikami-Larkin (HL) theory. But enhanced 2D-MT fluctuation contribution, being typical for the magnetic superconductors, is observed. Within the LP model approach the PG parameter, $\Delta^*(T)$, was determined for the first time. $\Delta^*(T)$ shows the narrow maximum at $T_s \approx 160\,K$ followed by the linear drop down to $T_{SDW}=T_{NFe}\approx 133\,K$. Both small $\Delta T_{3D}$ and enhanced $\sigma'(T)$, including linear $\Delta^*(T)$ drop, are considered to be the evidence of the enhanced magnetic interaction in $EuFeAsO_{0.85}F_{0.15}$. Importantly, the slop of the linear $\Delta^*(T)$ and its length are found to be the same as observed for $SmFeAsO_{0.85}$. The results suggest both the similarity of magnetic interaction processes in different Fe-pnictides and applicability of the LP model approach to the $\sigma'(T)$ analysis even in magnetic superconductors.

cond-mat.supr-con↗

arXiv2013

High-pressure flux growth, structural, and superconducting properties of LnFeAsO (Ln = Pr, Nd, Sm) single crystals

Single crystals of the LnFeAsO (Ln1111, Ln = Pr, Nd, and Sm) family with lateral dimensions up to 1 mm were grown from NaAs and KAs flux at high pressure. The crystals are of good structural quality and become superconducting when O is partially substituted by F (PrFeAsO1-xFx and NdFeAsO1-xFx) or when Fe is substituted by Co (SmFe1-xCoxAsO). From magnetization measurements, we estimate the temperature dependence and anisotropy of the upper critical field and the critical current density of underdoped PrFeAsO0.7F0.3 crystal with Tc = 25 K. Single crystals of SmFe1-xCoxAsO with maximal Tc up to 16.3 K for x = 0.08 were grown for the first time. From transport and magnetic measurements we estimate the critical fields and their anisotropy, and find these superconducting properties to be quite comparable to the ones in SmFeAsO1-xFx with a much higher Tc of = 50 K. The magnetically measured critical current densities are as high as 109 A/m2 at 2 K up to 7 T, with indication of the usual fishtail effect. The upper critical field estimated from resistivity measurements is anisotropic with slopes of -8.7 T/K (H // ab-plane) and -1.7 T/K (H // c-axis). This anisotropy (= 5) is similar to that in other Ln1111 crystals with various higher Tc s.

cond-mat.supr-con↗

arXiv2011

Interplay between magnetism and superconductivity in EuFe(2-x)Co(x)As2 studied by 57Fe and 151Eu Mössbauer spectroscopy

The compound EuFe(2-x)Co(x)As2 was investigated by means of the 57Fe and 151Eu Moessbauer spectroscopy versus temperature (4.2 - 300 K) for x=0 (parent), x=0.34 - 0.39 (superconductor) and x=0.58 (overdoped). It was found that spin density wave (SDW) is suppressed by Co-substitution, however it survives in the region of superconductivity, but iron spectra exhibit some non-magnetic component in the superconducting region. Europium orders anti-ferromagnetically regardless of the Co concentration with the spin re-orientation from the a-axis in the parent compound toward c-axis with the increasing replacement of iron by cobalt. The re-orientation takes place close to the a-c plane. Some trivalent europium appears in EuFe(2-x)Co(x)As2 versus substitution due to the chemical pressure induced by Co-atoms and it experiences some transferred hyperfine field from Eu2+. Iron experiences some transferred field due to the europium ordering for substituted samples in the SDW and non-magnetic state both, while the transferred field is undetectable in the parent compound. Superconductivity coexists with the 4f-europium magnetic order within the same volume. It seems that superconductivity has some filamentary character in EuFe(2-x)Co(x)As2 and it is confined to the non-magnetic component seen by the iron Moessbauer spectroscopy.

cond-mat.supr-con↗

arXiv2011

Shape of spin density wave versus temperature in AFe2As2 (A=Ca, Ba, Eu): A Mössbauer study

Parent compounds AFe2As2 (A=Ca, Ba, Eu) of the 122 family of the iron-based superconductors have been studied by 57Fe Moessbauer spectroscopy in the temperature range 4.2 K - ~300 K. Spin density waves (SDW) have been found with some confidence. They are either incommensurate with the lattice period or the ratio of the respective periods is far away from ratio of small integers. SDW shape is very unconventional i.e. differs from the sinusoidal shape. Magnetic order starts with lowered temperature as narrow sheets of the significant electron spin density separated by areas with very small spin density. Magnetic sheets are likely to be ordered in the alternate anti-ferromagnetic fashion as the material as whole behaves similarly to collinear anti-ferromagnet. Further lowering of temperature simply expands sheet thickness leading to the near triangular SDW. Finally, sheets fill the whole available space and almost rectangular shape of SDW is reached. Substantial maximum amplitude of SDW appears at the temperature just below the magnetic onset temperature, and this maximum amplitude increases slightly with lowering temperature. The square root from the mean squared hyperfine field behaves versus temperature according to the universality class (1, 2), i.e., with the electronic spin space having dimensionality equal unity and the real space having dimensionality equal two. The more or less pronounced tail above transition temperature due to the development of incoherent SDW is seen.

cond-mat.supr-con↗

arXiv2011

Influence of the carbon substitution on the critical current density and AC losses in MgB2 single crystals

The DC magnetization and AC complex magnetic susceptibilities were measured for MgB2 single crystals, unsubstituted and carbon substituted with the composition of Mg(B_0.94C_0.06)2. The measurements were performed in AC and DC magnetic fields oriented parallel to the c-axis of the crystals. From the DC magnetization loops and the AC susceptibility measurements, critical current densities (Jc) were derived as a function of temperature and the DC and AC magnetic fields. Results show that the substitution with carbon decreases Jc at low magnetic fields, opposite to the well known effect of an increase of Jc at higher fields. AC magnetic losses were derived from the AC susceptibility data as a function of amplitude and the DC bias magnetic field. The AC losses were determined for temperatures of 0.6 and 0.7 of the transition temperature Tc, so close to the boiling points of LH2 and LNe, potential cooling media for magnesium diboride based composites. The results are analyzed and discussed in the context of the critical state model.

cond-mat.supr-con↗

arXiv2009

Influence of carbon on intraband scattering in Mg(B1-xCx)2

We report data on the Hall coefficient (RH) of the carbon substituted Mg(B1-xCx)2 single crystals with x in the range from 0 to 0.1. The temperature dependences of RH obtained for the substituted crystals differ systematically at low temperatures, but all of them converge to the value of 1.8 x 10^-10 m^3/C at room temperature. The RH(T) data together with results of the thermoelectric power and electrical resistivity measurements are interpreted within a quasi-classical transport approach, where the presence of four different conducting sheets is considered. The main influence of the carbon substitution on the transport properties in the normal state is associated with enhanced scattering rates, rather than modified concentration of charge carriers. Presumably the carbon substitution increases the electron-impurity scattering mainly in the pi band.

cond-mat.supr-con↗

arXiv2009

Enhancement of the Hall-Lorenz number in optimally doped YBa2Cu3O_7-d

Electronic heat transport in the normal state of a high-quality single crystal of optimally-doped superconductor YBa2Cu3O6.95 was studied by measurements of longitudinal and transverse transport coefficients. For the temperature range from 100 to 300 K, the Hall-Lorenz number (Lxy) depends weakly on temperature and is about two times larger than the Sommerfeld value of the Lorenz number Lo = (pi^2)/3. Our results can be interpreted using a Fermi liquid model when effects of the pseudogap that opens at the Fermi level are included. However, we find that the bipolaron model can also explain both the enhanced value and the weak temperature dependence of the Hall-Lorenz number.

cond-mat.supr-con↗

arXiv2008

Structural and Superconducting Properties of RbOs2O6 Single Crystals

Single crystals of RbOs2O6 have been grown from Rb2O and Os in sealed quartz ampoules. The crystal structure has been identified at room temperature as cubic with the lattice constant a = 10.1242(12) A. The anisotropy of the tetrahedral and octahedral networks is lower and the displacement parameters of alkali metal atoms are smaller than for KOs2O6, so the "rattling" of the alkali atoms in RbOs2O6 is less pronounced. Superconducting properties of RbOs2O6 in the mixed state have been well described within the London approach and the Ginzburg-Landau parameter kappa(0) = 31 has been derived from the reversible magnetization. This parameter is field dependent and changes at low temperatures from kappa = 22 (low fields) to kappa = 31 at H_{c2}. The thermodynamic critical field H_{c}(0) = 1.3 kOe and the superconducting gap 2delta/k_{B}T_{c} = 3.2 have been estimated. These results together with slightly different H_{c2}(T) dependence obtained for crystals and polycrystalline RbOs2O6 proof evidently that this compound is a weak-coupling BCS-type superconductor close to the dirty limit.

cond-mat.supr-con↗