Longitudinal spin-relaxation in nitrogen-vacancy centers in electron irradiated diamond

We present systematic measurements of longitudinal relaxation rates ($1/T_1$) of spin polarization in the ground state of the nitrogen-vacancy (NV$^-$) color center in synthetic diamond as a function of NV$^-$ concentration and magnetic field $B$. NV$^-$ centers were created by irradiating a Type 1b single-crystal diamond along the [100] axis with 200 keV electrons from a transmission electron microscope with varying doses to achieve spots of different NV$^-$ center concentrations. Values of ($1/T_1$) were measured for each spot as a function of $B$.

quant-ph↗

arXiv2011

Time-resolved spectroscopy of exciton states in single crystals, single crystalline films and powders of YAlO_3 and YAlO_3:Ce

Luminescence characteristics of single crystals (SC), single crystalline films (SCF), powders and ceramics of YAlO_3 and YAlO_3:Ce have been studied at 4.2-300 K under photoexcitation in the 4-20 eV energy range and X-ray excitation. The origin and structure of defects responsible for various exciton-related emission and excitation bands have been identified. The ~5.6 eV emission of YAlO_3 SCF is ascribed to the self-trapped excitons. In YAlO_3 SC, the dominating 5.63 eV and 4.12 eV emissions are ascribed to the excitons localized at the isolated antisite defect Y^{3+}_Al and at the Y^{3+}_{Al} defect associated with the nearest-neighbouring oxygen vacancy, respectively. Thermally stimulated release of electrons, trapped at these defects, takes place at 200 K and 280 K, respectively. The formation energies of various Y^{3+}_{Al}-related defects are calculated. The presence of Y_{Al} antisite-related defects is confirmed by NMR measurements. The influence of various intrinsic and impurity defects on the luminescence characteristics of Ce^{3+} centers is clarified.

cond-mat.mtrl-sci↗