arXiv2025

Direct observation of the compression behavior of polystyrene microbeads in a diamond anvil cell

The pressure dependence of the bulk modulus of glassy polystyrene (PS) was measured in the relatively high-pressure regime, up to 6 GPa, at ambient temperature. For the measurements, PS microbeads were immersed in a pressure medium consisting of a mixture of methanol and ethanol, and the sample was placed in a diamond anvil cell capable of generating high and hydrostatic pressure. The volume change of the PS beads was observed under an optical microscope. The results demonstrated that the volume change in this study is consistent with an equation of state determined from the earlier studies in the low-pressure range up to 0.2 GPa. The bulk modulus was obtained as the derivative of the microbead volume with respect to pressure, and compared with the earlier data obtained from Brillouin spectroscopy.

cond-mat.soft↗

arXiv2019

Hydrogen-Storing Salt NaCl(H$_2$) Synthesized at High Pressure and High Temperature

X-ray diffraction and Raman scattering measurements, and first-principles calculations are performed to search for the formation of NaCl-hydrogen compound. When NaCl and H$_{2}$ mixture is laser-heated to above 1500 K at pressures exceeding 40 GPa, we observed the formation of NaClH$_{\textit{x}}$ with $\textit{P}$6$_{3}$/$\textit{mmc}$ structure which accommodates H$_{2}$ molecules in the interstitial sites of NaCl lattice forming ABAC stacking. Upon the decrease of pressure at 300 K, NaClH$_\textit{x}$ remains stable down to 17 GPa. Our calculations suggest the observed NaClH$_{\textit{x}}$ is NaCl(H$_{2}$). Besides, a hydrogen-richer phase NaCl(H$_{2}$)$_{4}$ is predicted to become stable at pressures above 40 GPa.

cond-mat.mtrl-sci↗