Impact of organic capping layer on the magnetic anisotropy of ultrathin Co films

Using combined magnetometry and ferromagnetic resonance studies, it is shown that introduction of a hydrocarbon cover layer leads to an increase of the contribution of the surface anisotropy to the effective magnetic anisotropy energy of hexagonal close-packed 0001 cobalt films, largely enhancing the perpendicular anisotropy. Due to a weak electronic interaction of the organic molecules with the Co atoms, an increase of surface anisotropy could be explained by the presence of an electric field at the organic-material/Co interface and by modification of surface atoms charge configuration.

cond-mat.mtrl-sci↗

arXiv2017

MgO thickness-induced spin reorientation transition in Co0.9Fe0.1/MgO/Co0.9Fe0.1 structure

The magnetic anisotropy (MA) of Mo/Au/Co0.9Fe0.1/Au/MgO(0.7 - 3 nm)/Au/Co0.9Fe0.1/Au heterostructure has been investigated at room temperature as a function of MgO layer thickness (tMgO). Our studies show that while the MA of the top layer does not change its character upon variation of tMgO, the uniaxial out-of-plane MA of the bottom one undergoes a spin reorientation transition at tMgO of about 0.8 nm, switching to the regime where the coexistence of in- and out-of-plane magnetization alignments is observed. The magnitudes of the magnetic anisotropy constants have been determined from ferromagnetic resonance and dc-magnetometry measurements. The origin of MA evolution has been attributed to a presence of an interlayer exchange coupling (IEC) between Co0.9Fe0.1 layers through the thin MgO film.

cond-mat.mtrl-sci↗