Konrad Kwatek

Publications and source records attributed to Konrad Kwatek.

6 recordsLinked to original sources

arXiv2026

Effects of high-pressure synthesis on phase formation and superconducting properties of PrFeAsO1-xFx

Motivated by recent reports of enhanced superconducting performance in several families of iron-based superconductors (IBS) processed by high-pressure (HP) synthesis, we investigate the influence of high gas pressure and high-temperature synthesis (HP-HTS) process on the structural, microstructural, electrical transport, and magnetic properties of Pr-based oxypnictide PrFeAsO1-xFx (Pr1111) using the processing conditions of 0.5 GPa for 1 h previously optimized for other IBS families. Representative underdoped (x = 0.2), optimal doped (x = 0.3), and overdoped (x = 0.5) compositions from the ambient-pressure electronic phase diagram of Pr1111 are selected to evaluate its composition-dependent effects of HP-HTS. The results demonstrate that HP-HTS enhances fluorine incorporation, improves phase formation, and produces a denser microstructure with improved grain connectivity in the underdoped and optimal doped compositions. Magnetic measurements reveal increased in the superconducting transition temperature (Tc) of ~1 K for x = 0.2 and ~6 K for x = 0.3, whereas only a marginal improvement in the critical current density is observed. Electrical resistivity measurements of the underdoped composition show a slight increase in Tc accompanied by a broader resistive transition, indicating residual structural inhomogeneity. In contrast, the overdoped composition exhibits increased impurity phase segregation, accompanied by suppression of superconductivity. These results demonstrate that the effectiveness of HP-HTS in Pr1111 is strongly composition dependent and governed by the interplay among fluorine incorporation, phase stability, and microstructural evolution, highlighting the need for further optimization of the HP-HTS processing conditions.

cond-mat.supr-con↗

arXiv2026

Tuning Superconductivity by Isovalent Antimony Substitution in PrFeAs(O,F)

We investigate the effects of isovalent Sb substitution at the As site in fluorine-doped PrFeAs1-xSbxO0.7F0.3 (x = 0 to 1.0) through structural, Raman spectroscopy, density functional theory (DFT), transport, magnetotransport, and magnetic measurements. The superconducting transition temperature decreases gradually from ~48 K for the parent compound to ~44 K up to x = 0.3, followed by a rapid suppression at higher Sb concentrations due to increasing disorder and secondary phase formation. Raman spectroscopy and DFT reveal lattice expansion and pronounced softening of pnictogen related vibrational modes upon Sb substitution. Magnetotransport measurements up to 9 T show enhanced upper critical fields and increased vortex activation energy for moderate Sb doping, indicating stronger vortex pinning. However, the critical current density remains low because of poor intergranular connectivity. The results demonstrate a crossover from an electronically tuned superconducting state to a disorder-dominated regime in isovalently substituted iron pnictides.

cond-mat.supr-con↗

arXiv2026

Effect of Mn Substitution on Superconductivity in PrFeAs(O,F): Role of Magnetic Impurities

We investigate Mn substitution at the Fe site in PrFe1-xMnxAsO0.7F0.3 (0 to 0.1) using structural, Raman, density functional theory (DFT), transport, and magnetic measurements. X-ray diffraction and Raman analyses confirm preferential Mn incorporation into the FeAs planes, accompanied by lattice expansion and suppression of Fe-related vibrational modes. Electrical transport reveals a systematic decrease of the superconducting transition temperature from 48 K (x = 0) to complete suppression at x = 0.1, together with low-temperature resistivity upturns evolving toward insulating-like behavior. Magnetization and magnetotransport measurements show degradation of superconducting coherence, critical current density, upper critical field, and vortex activation energy with increasing Mn content. The results demonstrate that Mn acts as an efficient magnetic impurity, strongly perturbing the electronic and magnetic environment of the FeAs layers. Comparative analysis indicates relatively enhanced robustness of superconductivity in the Pr-based system, highlighting the role of rare-earth-dependent electronic correlations in impurity effects.

cond-mat.supr-con↗

arXiv2026

Complete electronic phase diagram and enhanced superconductivity in fluorine-doped PrFeAsO1-xFx

Establishing a complete electronic phase diagram for REFeAsO (RE = rare earth, RE1111) ironbased superconductors has remained experimentally challenging. Here, we report a systematic investigation of PrFeAsO1-xFx over the full nominal fluorine-doping range 0 to 1 and construct the first comprehensive electronic phase diagram for this system. The evolution from the nonsuperconducting parent compound to the fluorine-rich limit reveals a broad dome shaped superconducting region. Structural refinement demonstrates a systematic lattice contraction with increasing fluorine content (x), corroborated by Raman spectroscopy through softening of the Pr(A1g) phonon mode and hardening of the Fe(B1g) mode, confirming effective fluorine incorporation at the oxygen sites. The maximum superconducting transition temperature (Tc) reaches up to 52.3 K, approximately 5 K higher than previous reports for Pr1111. Magnetotransport measurements yield large upper critical fields Hc2(0) exceeding 100 T, while analysis of resistive transition broadening reveals thermally activated flux flow with a crossover from single-vortex to collective pinning regimes. Specific-heat measurements exhibit a reduced jump deltaC/γTc < 1.43, reflecting strong superconducting fluctuations and multiband pairing. These results establish clear structure property correlations and provide a unified description of superconductivity across the entire doping range of the Pr1111 system.

cond-mat.supr-con↗

arXiv2025

Effect of spark plasma sintering on the superconducting properties of Sm-based oxypnictide

We optimize the superconducting properties of Sm-based oxypnictide (Sm1111: SmFeAsO0.80F0.20) by using the Spark Plasma Sintering (SPS) technique under various synthesis conditions, including heating temperatures ranging from 600 to 1000 °C for durations of 5 to 30 minutes at the applied pressure of 45 MPa. All prepared bulks are characterized by structural and microstructural analysis as well as transport and magnetic measurements to conclude our findings. SmFeAsO0.80F0.20 bulks are also prepared using the conventional synthesis process at ambient pressure (CSP) and the high gas pressure and high temperature (HP-HTS) methods at 500 MPa, which exhibit a superconducting transition temperature (Tc) of ~54 K. Interestingly, the SPS process of SmFeAsO0.80F0.20 increases the sample densities up to 97-98% and confirms the optimized synthesis conditions of 900°C for 5-10 min; however, the increased sintering temperature or duration reduces Tc due to the possible evaporation of lighter elements, particularly fluorine. Furthermore, the SPS technique is unable to reduce the observed impurity phases for the Sm1111, which is similar to the CSP and HP-HTS processes. A slight increment in the Jc by the SPS process is observed due to the enhancement of sample density. A comparative analysis of Sm1111 superconductors prepared by SPS is performed with CSP and HP-HTS processes, suggesting that an increased sample density is ineffective on the superconducting properties in the presence of the impurity phases. This finding can be beneficial for the fundamental and applied research of iron-based superconductor (FBS).

cond-mat.supr-con↗

arXiv2025

Synthesis and characterizations of arsenic doped FeSe bulks

FeSe(11) family has a simple crystal structure belonging to iron-based superconductors (FBS) and has many stable phases including hexagonal and tetragonal structures, but only the tetragonal phase exhibits the superconductivity. In this study, we have investigated the effects of chemical pressure induced by As-doping at Se-sites in the FeSe system by preparing a series of FeSe1-xAsx (x = 0.005, 0.01, 0.02, 0.05, 0.1, and 0.2) bulks. A broad characterization has been performed on these samples using structural, microstructural, transport, and magnetic measurements. The obtained lattice parameters are increased by As-doping, which suggests the successful insertion of As at Se-sites into the tetragonal lattice for low doping contents up to 5%, whereas the higher As-substitution appears in the form of the FeAs impurity phase. The temperature dependence of the resistivity of all samples has similar behaviour and depicts the highest onset transition temperature of around 11.5 K, but the zero resistivity is not reached until the measured temperature of 7 K, which could be due to the presence of the impurity phases. Our study suggests that a dopant with a large ionic radius, i.e., Arsenic, promotes the formation of the hexagonal phase of the 11 family and is effective for a small amount of doping level for the superconducting properties, whereas higher As-doping levels reduce the superconducting properties.

cond-mat.supr-con↗