arXiv2009

Electrical and magnetic transport properties of Fe3O4 thin films on GaAs (100) substrate

Thin films of magnetite (Fe3O4) are grown on single crystal GaAs (100) substrate by pulsed laser deposition. X ray diffraction (XRD) result shows the (111) preferred orientation of the Fe3O4 film and x-ray photoelectron spectroscopy confirm the presence of single phase Fe3O4 in the film. The electrical transport property of the film shows the characteristic Verwey transition at 122 K and below 110 K, the transport follows variable range hopping type conduction mechanism. The film shows room temperature magnetization hysteresis loop suggesting the ferrimagnetic behavior of the film with saturation magnetization value close to 470 emu/cc.

cond-mat.mtrl-sci↗
arXiv2006

Anomalous lattice expansion of RuSr2Eu1.5Ce0.5Cu2O10(Ru-1222) magneto superconductor: A low temperature X-ray diffraction study

This is the first report of the observation of the onset of excess volume and also of the strain along the a-axis near the magnetic ordering temperature in Ru-1222 superconductor, and indicates a coupling between the lattice and the magnetism in this system. Magnetization, magneto transport and thermoelectric power measurements being carried out on the same sample are also reported.

cond-mat.supr-con↗
arXiv2005

Field induced first order antiferromagnetic to ferromagnetic transition in Al-doped CeFe$_2$: a calorimetric investigation

Field variation of heat capacity at fixed temperatures is investigated to identify the origin of the field induced first order phase transition in polycrystalline Ce(Fe$_{0.094}$Al$_{0.04}$)$_2$ sample. The heat capacity at 4.5K and 3.5K shows hysteresis in different field cycles and the virgin curve stays outside the envelope curve. This is analogous to the magnetization and magneto-resistance behavior observed in this system, where the amount of hysteresis, and the magnitude of zero-field irreversibility are attributed to the degree of supercooling/superheating, and the extent of kinetic arrest of the reverse transition from ferro- to antifrromagnetic state in field reducing cycle respectively. However, contrary to the magnetization and magneto-resistance, in heat capacity both these features have decreased with reducing temperature signifying the importance of structural contribution.

cond-mat.str-el↗