arXiv2021

Singular angular magnetoresistance and sharp resonant features in a high-mobility metal with open orbits, ReO3

We report high-resolution angular magnetoresistance (AMR) experiments performed on crystals of ReO$_3$ with high mobility (90,000 cm$^2$/Vs at 2 K) and extremely low residual resistivity (5-8 n$Ω$cm). The Fermi surface, comprised of intersecting cylinders, supports open orbits. The resistivity $ρ_{xx}$ in a magnetic field $B$ = 9 T displays a singular pattern of behavior. With $\bf E\parallel \hat{x}$ and $\bf B$ initially $\parallel\bf\hat{z}$, tilting $\bf B$ in the longitudinal $k_z$-$k_x$ plane leads to a steep decrease in $ρ_{xx}$ by a factor of 40. However, if $\bf B$ is tilted in the transverse $k_y$-$k_z$ plane, $ρ_{xx}$ increases steeply by a factor of 8. Using the Shockley tube integral approach, we show that, in ReO$_3$, the singular behavior results from the rapid conversion of closed to open orbits, resulting in opposite signs for AMR in orthogonal planes. The floor values of $ρ_{xx}$ in both AMR scans are identified with specific sets of open and closed orbits. Also, the "completion angle" $γ_c$ detected in the AMR is shown to be an intrinsic geometric feature that provides a new way to measure the Fermi radius $k_F$. However, additional sharp resonant features which appear at very small tilt angles in the longitudinal AMR scans are not explained by the tube integral approach.

cond-mat.mtrl-sci↗

arXiv2021

NbIr$_2$B$_2$ and TaIr$_2$B$_2$ -- new low symmetry noncentrosymmetric superconductors with strong spin orbit coupling

Superconductivity was first observed more than a century ago, but the search for new superconducting materials remains a challenge. The Cooper pairs in superconductors are ideal embodiments of quantum entanglement. Thus, novel superconductors can be critical for both learning about electronic systems in condensed matter and for possible application in future quantum technologies. Here two previously unreported materials, NbIr$_2$B$_2$ and TaIr$_2$B$_2$, are presented with superconducting transitions at 7.2 and 5.2 K, respectively. They display a unique noncentrosymmetric crystal structure, and for both compounds the magnetic field that destroys the superconductivity at 0 K exceeds one of the fundamental characteristics of conventional superconductors (the Pauli limit), suggesting that the superconductivity may be unconventional. Supporting this experimentally based deduction, first-principle calculations show a spin split Fermi surface due to the presence of strong spin-orbit coupling. These materials may thus provide an excellent platform for the study of non-BCS superconductivity in intermetallic compounds.

cond-mat.supr-con↗

arXiv2020

Widely Spaced Planes of Magnetic Dimers in the Ba6Y2Rh2Ti2O17-δ Hexagonal Perovskite

We report the synthesis and initial characterization of Ba6Y2Rh2Ti2O17-δ, a previously unreported material with a hexagonal symmetry structure. Face-sharing RhO6 octahedra form triangular planes of Rh2O9 dimers that are widely separated in the perpendicular direction. The material displays a small effective magnetic moment, due to the Rh ions present, and a negative Curie-Weiss temperature. The charge transport and optical band gaps are very similar, near 0.16 eV. A large upturn in the heat capacity at temperatures below 1 K, suppressed by applied magnetic fields larger than {μ0H = 2 Tesla, is observed. A large T-linear term in the specific heat (γ=166 mJ/mol f.u-K2) is seen, although the material is insulating at low temperatures. These results suggest the possibility of a spin liquid ground state in this material.

cond-mat.str-el↗

arXiv2020

Low Temperature Structural Phase Transition in the Perovskite Ba2CaMoO6

Ba2CaMoO6 was synthesized by solid state method. The crystal structure adopts cubic Fm-3m space group at room temperature with lattice parameters of 8.378231(5) {angstroms}. Upon cooling, Ba2CaMoO6 was determined to have a structural phase transition to tetragonal I4/m (a=5.905763(6) {angstroms} and c=8.38817(1) {angstroms}) around 200 K. The phase transition was probed structurally by synchrotron and neutron diffraction and thermodynamically by specific heat and differential scanning calorimetry measurement. This structural phase transition will deepens our understanding of the perovskite family especially the formation of perovskites that break corner sharing networks.

cond-mat.mtrl-sci↗

arXiv2020

Structure, Magnetism and First Principles Modeling of the Na0.5La0.5RuO3 Perovskite

High purity polycrystalline Na0.5La0.5RuO3 was synthesized by a solid state method, and its properties were studied by magnetic susceptibility, heat capacity and resistivity measurements. We find it to be a tetragonal perovskite, in contrast to an earlier report, with random La/Na mixing. With a Curie-Weiss temperature of -231 K and effective moment of 2.74 uB/mol-Ru, there is no magnetic ordering down to 1.8 K. A broad hump at 1.4 K in the heat capacity, however, indicates the presence of a glassy magnetic transition, which we attribute to the influence of the random distribution of Na and La on the perovskite A sites. Comparison to CaRuO3, a structurally ordered ruthenate perovskite with similar properties, is presented. First-principle calculations indicate that the Na-La distribution determines the local magnetic exchange inter-actions between Ru ions, favoring either antiferromagnetic or ferromagnetic coupling when the local environment is Na or La rich. Thus our data and analysis suggest that mixing cations with different charges and sizes on the A site in this perovskite results in magnetic frustration through a balance of local magnetic exchange interactions.

cond-mat.str-el↗

arXiv2020

Hexagonal Perovskites as Quantum Materials

Hexagonal oxide perovskites, in contrast to the more familiar perovskites, allow for face-sharing of metal-oxygen octahedra or trigonal prisms within their structural frameworks. This results in dimers, trimers, tetramers, or longer fragments of chains of face-sharing octahedra in the crystal structures, and consequently in much shorter metal-metal distances and lower metal-oxygen-metal bond angles than are seen in the more familiar perovskites. The presence of the face-sharing octahedra can have a dramatic impact on magnetic properties of these compounds, and dimer-based materials, in particular, have been the subjects of many quantum-materials-directed studies in materials physics. Hexagonal oxide perovskites are of contemporary interest due to their potential for geometrical frustration of the ordering of magnetic moments or orbital occupancies at low temperatures, which is especially relevant to their significance as quantum materials. As such, several hexagonal oxide perovskites have been identified as potential candidates for hosting the quantum spin liquid state at low temperatures. In our view, hexagonal oxide perovskites are fertile ground for finding new quantum materials. This review briefly describes the solid state chemistry of many of these materials.

cond-mat.str-el↗

arXiv2019

Long-range and local crystal structures of the Sr1-xCaxRuO3 Perovskites

The crystal structures of the Sr1-xCaxRuO3 perovskites are investigated using both long range and local structural probes. High resolution synchrotron powder X-ray diffraction characterization at ambient temperature shows that the materials are orthorhombic to high precision, and we support previous work showing that Ca2+ substitution for Sr2+ primarily changes the tilting of rigid corner-sharing RuO6 octahedra at their shared oxygen vertices. X-ray pair distribution function analysis for SrRuO3, CaRuO3 and one intermediate composition show them to be locally monoclinic, and no long range or local phase transitions are observed between 80 and 300 K for materials with intermediate compositions. High-resolution transmission electron microscopy shows that the Sr/Ca distribution is random at the nanoscale. We plot magnetic characteristics such as the ferromagnetic Tc, Curie-Weiss theta, effective moment, and ambient temperature susceptibility vs. the octahedral tilt and unit cell volume.

cond-mat.mtrl-sci↗

arXiv2018

The trimer-based spin liquid candidate Ba4NbIr3O12

Ba4NbIr3O12, a previously unreported material with a triangular planar geometry of Ir3O12 trimers, is described. Magnetic susceptibility measurements show no magnetic ordering down to 1.8 K despite the Curie-Weiss temperature of -13 K. The material has a very low effective magnetic moment of 0.80 μB/f.u. To look at the lower temperature behavior, the specific heat (Cp) was measured down to 0.35 K; it shows no indication of magnetic ordering and fitting a power law to Cp vs. T below 2 K yields the power α = 3/4. Comparison to the previously unreported trimer compound made with the 4d element Rh in place of the 5d element Ir, Ba4NbRh3O12, is presented. The analysis suggests that Ba4NbIr3O12 is a candidate spin liquid material.

cond-mat.str-el↗

arXiv2018

A Spin Glass State in Ba3TiRu2O9

The magnetic properties of Ba3TiRu2O9 , whose crystal structure is based on stacked triangular planar lattices of MO6 dimers and single MO6 octahedra, are reported. The system is magnetically disturbed by a substantial amount of Ti/Ru chemical disorder. The Weiss temperature and effective magnetic moment were found to be -29.5 K and 1.82 μB/f.u. respectively, and a bifurcation in the zero field cooled and field cooled magnetic susceptibility is observed below 4.7 K, suggesting that this is a compositionally-disordered spin-glass system. The material is a semiconductor with an activation energy for charge transport of approximately 0.14 eV.

cond-mat.str-el↗

arXiv2018

Trimers of MnO6 octahedra and ferrimagnetism of Ba4NbMn3O12

Ba4NbMn3O12 is reported, synthesized by a solid state method in air. The crystal structure, determined by performing refinements on room temperature powder X-ray diffraction data by the Rietveld method, consists of Mn3O12 trimers in the configuration of three face-sharing MnO6 octahedra, with the trimers arranged in triangular planes. An effective moment of 4.82 μB/f.u is observed and competing antiferromagnetic and ferromagnetic interactions between Mn ions are inferred from the Weiss temperature of -4 K and the ferrimagnetic ordering transition of approximately 42 K. Ba4NbMn3O12 is a semiconductor with a transport activation energy of 0.37 eV.

cond-mat.str-el↗

arXiv2018

A Geometrically Frustrated Trimer-Based Mott Insulator

The crystal structure of Ba4NbRu3O12 is based on triangular planes of elongated Ru3O12 trimers oriented perpendicular to the plane. We report that it is semiconducting, that its Weiss temperature and effective magnetic moment are -155 K and 2.59 μB/f.u. respectively, and that magnetic susceptibility and specific heat data indicate that it exhibits magnetic ordering near 4 K. The presence of a high density of low energy states is evidenced by a substantial Sommerfeld-like T-linear term (gamma = 31(2) mJ/mole-K^2) in the specific heat. Electronic structure calculations reveal that the electronic states at the Fermi Energy reside on the Ru3O12 trimers and that the calculated density of electronic states is high and continuous around the Fermi Energy - in other words density functional theory calculates the material to be a metal. Our results imply that Ba4NbRu3O12 is a geometrically frustrated trimer-based Mott insulator.

cond-mat.str-el↗