Angular Dependence of X-ray Absorption Spectrum for Field-aligned Fe-based Superconductors

Anisotropic Fe K-edge and As K-edge X-ray absorption near edge spectrum (XANES) measurements on superconducting (T_c = 52 K) (Sm_{0.95}La_{0.05})FeAs(O_{0.85}F_{0.15}) field-aligned microcrystalline powder are presented. The angular dependence of Fe pre-edge peak (dipole transition of Fe-1s electrons to Fe-3d/As-4p hybrid bands) relative to the tetragonal ab-plane of aligned powder indicates larger density of state (DOS) along the c-axis, and is consistent with the LDA band structure calculation. The anisotropic Fe K-edge spectra exhibit a chemical shift to lower energy compared to FeO which are closely related to the itinerant character of Fe^{2+}-3d^6 orbitals. The anisotropic As K-edge spectra are more or less the mirror images of Fe K-edge due to the symmetrical Fe-As hybridiztion in the FeAs layer. Angular dependence of As main peak (dipole transition of As-1s electrons to higher energy hybrid bands) was observed suggesting character of As-4d e_g orbitals.

cond-mat.supr-con↗

arXiv2008

Anisotropic magnetic and superconducting properties of aligned weak-ferromagnetic superconductor RuSr$_2$RCu$_2$O$_8$ (R = rare earths)

The powder alignment method is used to investigate the anisotropic physical properties of the weak-ferromagnetic superconductor system RuSr2RCu2O8 (R = Pr, Nd, Sm, Eu, Gd, Gd0.5Dy0.5). The RuSr2GdCu2O8 cuprate is a weak-ferromagnetic superconductor with a magnetic ordering of Ru moments at TN(Ru) = 131 K, a superconducting transition in the CuO2 layers at Tc = 56 K, and a low temperature Gd antiferromagnetic ordering at TN(Gd) = 2.5 K. Due to weak magnetic anisotropy of this tetragonal system, highly c-axis aligned microcrystalline powder (diameter ~ 1-10 $μ$m) in epoxy can be obtained only for R = Eu and Gd through the field-rotation powder alignment method where c-axis is perpendicular to the aligned magnetic field Ba = 0.9 T and parallel to the rotation axis. For smaller rare earth compound R = Gd0.5Dy0.5, powder alignment can be achieved using the simple field powder alignment method where c-axis is partially aligned along the aligned magnetic field. The anisotropic temperature dependence of magnetic susceptibility for the c-axis aligned powders exhibit weak anisotropy with $χ_{c} > χ_{ab}$ at room temperature due to anisotropic rare earth, Eu and Gd, contribution and crossover to $χ_{c} < χ_{ab}$ below 190 K where strong Ru anisotropic short-range exchange interaction overtakes the rare earth contribution. Anisotropic diamagnetic superconducting intragrain shielding signal of aligned microcrystalline RuSr2GdCu2O8 powder-in-epoxy below vortex lattice melting temperature at 39 K in 1-G field is much weaker than the intergrain polycrystalline bulk sample signal due to the small grain size (d ~ 1-10 $μ$m), long penetration depth ($λ_{ab}$ ~ 0.55 $μ$m, $λ_{c}$ ~ 0.66 $μ$m) and the two-dimensional (2D) character of CuO2 layers.

cond-mat.supr-con↗