Zero-bias conductance peak observed in Au/FeSe0.3Te0.7 ramp-type junctions and its implication on the superconducting order parameter

Based upon the currently predominant theory of Fe-based superconductors, the order parameter symmetry is the nodaless s\pm-wave. Andreev conductance involving normal metals and such superconductors does not have a zero bias conductance peak (ZBCP) except maybe for a very narrow range of a junction-dependent fitting parameter. We have measured differential conductance of the in-plane boundary junctions between Au and superconducting FeSe0.3Te0.7 films. The Au/FeSe0.3Te0.7 ramp-type junctions are fabricated with the bias current direction along the <110> axis of the epitaxial FeSe0.3Te0.7 film. We have always observed a pronounced ZBCP as well as some gap-like features in the conductance spectra of all samples studied, thus our experimental results suggest not the s\pm-wave theory but the possible existence of a nodal point around 45° in at least one of the gaps in FeSe0.3Te0.7 superconductor.

cond-mat.supr-con↗

arXiv2009

Crystal orientation and thickness dependence of superconductivity on tetragonal FeSe1-x thin films

Superconductivity was recently found in the simple tetragonal FeSe structure. Recent studies suggest that FeSe is unconventional, with the symmetry of the superconducting pairing state still under debate. To tackle these problems, clean single crystals and thin films are required. Here we report the fabrication of superconducting beta-phase FeSe1-x thin films on different substrates using a pulsed laser deposition (PLD) technique. Quite interestingly, the crystal orientation, and thus, superconductivity in these thin films is sensitive to the growth temperature. At 320C, films grow preferably along c-axis, but the onset of superconductivity depends on film thickness. At 500C, films grow along (101), with little thickness dependence. These results suggest that the low temperature structural deformation previously found is crucial to the superconductivity of this material.

cond-mat.supr-con↗

arXiv2000

Energy loss of fast quarks in nuclei

We report an analysis of the nuclear dependence of the yield of Drell-Yan dimuons from the 800 GeV/c proton bombardment of $^2H$, C, Ca, Fe, and W targets. Employing a new formulation of the Drell-Yan process in the rest frame of the nucleus, this analysis examines the effect of initial-state energy loss and shadowing on the nuclear-dependence ratios versus the incident proton's momentum fraction and dimuon effective mass. The resulting energy loss per unit path length is $-dE/dz = 2.32 \pm 0.52\pm 0.5$ GeV/fm. This is the first observation of a nonzero energy loss of partons traveling in nuclear environment.