arXiv2023

Characterisation of Corrosion Damage in T91/F91 steel exposed to Liquid Lead-Bismuth Eutectic

T91 samples were exposed to static liquid lead-bismuth eutectic (LBE) at 700°C for 250-500 hours in either an oxidising or reducing environment. Corrosion damage was characterised using electron microscopy techniques, which identified networks of LBE intrusion beneath LBE-wetted surfaces. Under reducing conditions these networks are uniformly distributed, while they appear patchier and deeper under oxidising conditions. The individual intrusions preferentially follow microstructural features, initially along prior-austenite grain boundaries, followed by penetration down martensite lath boundaries. Local depletion of Cr was observed within 4 μm of the intrusions and along intersecting boundaries, suggesting local Cr dissolution as the main corrosion mechanism.

cond-mat.mtrl-sci↗

arXiv2022

Effect of alloying on the microstructure, phase stability, hardness and partitioning behavior of a new dual-superlattice nickel-based superalloy

A novel y-y'-y" dual-superlattice superalloy, with promising mechanical properties up to elevated temperatures was recently reported. The present work employs state of the art chemical and spatial characterization techniques to study the effect systematic additions of Mo, W and Fe and variations in Nb and Al contents have on the phase fraction, thermal stability, elemental partitioning and mechanical properties. Alloys were produced through arc melting followed by heat treatment. Multi-scale characterization techniques and hardness testing were employed to characterize their microstructure, thermal stability and mechanical properties. Alterations in such properties or in elemental partitioning behaviour were then explained through thermodynamic modelling. A modest addition of 1.8 at.% Mo had a strong effect on the microstructure and thermal stability: it minimized microstructural coarsening during heat treatments while not significantly decreasing the y' solvus temperature. A reduction of Nb by 0.6 at.%, strongly reduced the y" volume fraction, without affecting the y' volume fraction. The reduced precipitate fraction led to a significant reduction in alloy hardness. Fe, added to achieve better processability and reduced material cost, decreased the y' solvus temperature and caused rapid microstructural coarsening during heat treatments, without affecting alloy hardness. A reduction of Al by 0.4 at.%, reduced the y' volume fraction and the y' solvus temperature, also without affecting alloy hardness. The addition of 0.9 at.% W decreased the y' solvus temperature but increased both precipitate volume fractions. These data will be invaluable to optimize current alloy design and to inform future alloy design efforts.

cond-mat.mtrl-sci↗

arXiv2020

Quantifying the effect of oxygen on micro-mechanical properties of a near-alpha titanium alloy

Atom probe tomography (APT), electron probe microanalysis (EPMA) and nanoindentation were used to characterise the oxygen-rich layer on an in-service jet engine compressor disc, manufactured from the titanium alloy TIMETAL 834. Oxygen ingress was quantified and related to changes in mechanical properties through nanoindentation studies. The relationship between oxygen concentration, microstructure, crystal orientation and hardness has been explored through correlative hardness mapping, EPMA and electron backscatter diffraction (EBSD). The role of microstructure on oxygen ingress has been studied and oxygen ingress along a potential alpha/ beta interface was directly observed on the nanoscale using APT.

cond-mat.mtrl-sci↗

arXiv2020

Atom probe characterisation of segregation driven Cu and Mn-Ni-Si co-precipitation in neutron irradiated T91 tempered-martensitic steel

The T91 grade and similar 9Cr tempered-martensitic steels (also known as ferritic-martensitic) are leading candidate structural alloys for fast fission nuclear and fusion power reactors. At low temperatures (300 to 400 $^\circ$C) neutron irradiation hardens and embrittles these steels, therefore it is important to investigate the origin of this mode of life limiting property degradation. T91 steel specimens were separately neutron irradiated to 2.14 dpa at 327 $^\circ$C and 8.82 dpa at 377 $^\circ$C in the Idaho National Laboratory Advanced Test Reactor. Atom probe tomography was used to investigate the segregation driven formation of Mn-Ni-Si-rich (MNSPs) and Cu-rich (CRP) co-precipitates. The precipitates increase in size and, slightly, in volume fraction at the higher irradiation temperature and dose, while their corresponding compositions were very similar, falling near the Si(Mn,Ni) phase field in the Mn-Ni-Si projection of the Fe-based quaternary phase diagram. While the structure of the precipitates has not been characterized, this composition range is distinctly different than that of the typically cited G-phase. The precipitates are composed of CRP with MNSP appendages. Such features are often observed in neutron irradiated reactor pressure vessel (RPV) steels. However, the Si, Ni, Mn, P and Cu solutes concentrations are lower in the T91 than in typical RPV steels. Thus, in T91 precipitation primarily takes place in solute segregated regions of line and loop dislocations. These results are consistent with the model for radiation induced segregation driven precipitation of MNSPs proposed by Ke et al. Cr-rich alpha prime ($α$') phase formation was not observed.

cond-mat.mtrl-sci↗

arXiv2015

Structural, electronic, and optical properties of $m$-plane InGaN/GaN quantum wells: Insights from experiment and atomistic theory

In this paper we present a detailed analysis of the structural, electronic, and optical properties of an $m$-plane (In,Ga)N/GaN quantum well structure grown by metal organic vapor phase epitaxy. The sample has been structurally characterized by x-ray diffraction, scanning transmission electron microscopy, and 3D atom probe tomography. The optical properties of the sample have been studied by photoluminescence (PL), time-resolved PL spectroscopy, and polarized PL excitation spectroscopy. The PL spectrum consisted of a very broad PL line with a high degree of optical linear polarization. To understand the optical properties we have performed atomistic tight-binding calculations, and based on our initial atom probe tomography data, the model includes the effects of strain and built-in field variations arising from random alloy fluctuations. Furthermore, we included Coulomb effects in the calculations. Our microscopic theoretical description reveals strong hole wave function localization effects due to random alloy fluctuations, resulting in strong variations in ground state energies and consequently the corresponding transition energies. This is consistent with the experimentally observed broad PL peak. Furthermore, when including Coulomb contributions in the calculations we find strong exciton localization effects which explain the form of the PL decay transients. Additionally, the theoretical results confirm the experimentally observed high degree of optical linear polarization. Overall, the theoretical data are in very good agreement with the experimental findings, highlighting the strong impact of the microscopic alloy structure on the optoelectronic properties of these systems.

cond-mat.mes-hall↗

arXiv2015

From solid solution to cluster formation of Fe and Cr in $α$-Zr

To understand the mechanisms by which Fe and Cr additions increase the corrosion rate of irradiated Zr alloys, a combination of experimental (atom probe tomography, x-ray diffraction and thermoelectric power measurements) and modelling (density functional theory) techniques are employed to investigate the non-equilibrium solubility and clustering of Fe and Cr in binary Zr alloys. Cr occupies both interstitial and substitutional sites in the α-Zr lattice, Fe favours interstitial sites, and a low-symmetry site that was not previously modelled is found to be the most favourable for Fe. Lattice expansion as a function of alloying concentration (in the dilute regime) is strongly anisotropic for Fe additions, expanding the $c$-axis while contracting the $a$-axis. Defect clusters are observed at higher solution concentrations, which induce a smaller amount of lattice strain compared to the dilute defects. In the presence of a Zr vacancy, all two-atom clusters are more soluble than individual point defects and as many as four Fe or three Cr atoms could be accommodated in a single Zr vacancy. The Zr vacancy is critical for the increased solubility of defect clusters, the implications for irradiation induced microstructure changes in Zr alloys are discussed.

cond-mat.mtrl-sci↗

arXiv2011

Direct observation of local K variation and its correlation to electronic inhomogeneity in (Ba1-xKx)Fe2As2 Pnictide

Local fluctuations in the distribution of dopant atoms are a suspected cause of nanoscale electronic disorder or phase separation observed within the pnictide superconductors. Atom probe tomography results present the first direct observations of dopant nano-clustering in a K-doped 122-phase pnictides. First-principles calculations suggest the coexistence of static magnetism and superconductivity on a lattice parameter length scale over a large range of doping concentrations. Collectively, our results provide evidence for a mixed scenario of phase coexistence and phase separation originating from variation of dopant atom experiments distroibutions.

cond-mat.supr-con↗