arXiv2003

Formation and mobility of oxygen vacancies in RuSr2GdCu2O8

Oxygen vacancies are introduced in the RuO2 and possibly CuO2 planes of RuSr2GdCu2O8 by annealing in vacuum above 600 K. The diffusive jumps of the O vacancies are accompanied by a reorientation of the local distortion, and are probed by measuring the elastic energy loss and modulus versus temperature at 1-10 kHz. An intense acoustic absorption peak develops near 670 K at 1 kHz and finally stabilizes after heating up to 920 K in vacuum. The analysis of the peak shows a barrier for the O diffusion of ~1.4 eV, and a slowing down of Curie-Weiss type, with Tc = 400-470 K, due to the interaction among the O vacancies. A secondary peak is attributed to O vacancies trapped at defects in the RuO2 planes, or to vacancies in the CuO2 planes. No sign of structural phase transformation is found up to 920 K.

cond-mat.supr-con↗

arXiv2002

Effect of annealing on the physical properties of RuSr2GdCu2O8 sintered samples and a discussion about magnetic measurements performed by SQUID magnetometer

In this paper we present the physical characterization of sintered RuSr2GdCu2O8 samples prepared with different procedures. In particular we show how the physical properties are affected by the final step, which is one week annealing in flowing Oxygen, and how extensively the annealing procedure affects the visibility of the superconducting behaviour. Moreover, we analyse the complexity of the d.c. magnetic measurements performed on such type of samples below the superconducting transition and the possibility to decode them.

cond-mat.supr-con↗

arXiv2002

Angular dependence of magnetoresistivity in c-oriented MgB2 thin film

The anisotropy of MgB2 is still under debate: its value, strongly dependent on the sample and on the measuring method, ranges between 1.2 and 13. In this work we present our results on a MgB2 c-oriented superconducting thin film. To evaluate the anisotropy, we followed two different approaches. Firstly, magnetoresistivity was measured as a function of temperature at selected magnetic fields applied both parallel and perpendicular to the c-axis; secondly, we measured magnetoresistivity at selected temperatures and magnetic fields, varying the angle q between the magnetic field and the c-axis. The anisotropy estimated from the ratio between the upper critical fields parallel and perpendicular to the c-axis and the one obtained in the framework of the scaling approach within the anisotropic Ginzburg-Landau theory are different but show a similar trend in the temperature dependence. The obtained results are compared and discussed in the light of the two-band nature of MgB2. A comparison between critical fields in thin films and single crystal is also performed.

cond-mat.supr-con↗

arXiv2002

Synthesis effects on the magnetic and superconducting properties of RuSr2GdCu2O8

A systematic study on the synthesis of the Ru-1212 compound by preparing a series of samples that were annealed at increasing temperatures and then quenched has been performed. It results that the optimal temperature for the annealing lies around 1060-1065 C; a further temperature increase worsens the phase formation. Structural order is very important and the subsequent grinding and annealing improves it. Even if from the structural point of view the samples appear substantially similar, the physical characterization highlight great differences both in the electrical and magnetic properties related to intrinsic properties of the phase as well as to the connection between the grains as inferred from the resistive and the Curie Weiss behaviour at high temperature as well as in the visibility of ZFC anf FC magnetic signals.

cond-mat.supr-con↗

arXiv2001

Synthesis and characterization of superconducting RuSr2GdCu2O8

We report on structural, electrical and magnetic properties of RuSr2GdCu2O8 samples made by systematic synthesis work so that they differ from one onether in number of annealings and sintering temperature. Our aim is to highlight the different behaviours as a consequence of the thermal treatments. In particular, we deal with the onset of superconductivity in relation to the homogenisation process, and its influence on resistivity, structural and magnetic ordering. Finally, the problems related to the magnetic measurements due to the superimposition of different magnetic states are examined.

cond-mat.supr-con↗

arXiv2001

Magnetic characterization of sintered MgB2 samples: effect of the substitution or doping with Li, Al and Si

Powdered and sintered MgB2 samples have been characterized through magnetic measurements performed from T = 5 K up to few degrees above the transition temperature of about 39 K. We found that the sintered samples behave as well-connected bodies, showing no trace of granularity. In order to obtain the critical current density value Jc the Critical State Model has been therefore employed in a straightforward way. With the aim either to decrease the electron mean free path or to increase its Jc we have attempted to introduce defects in the MgB2 structure by different procedures: substitution of Lithium on the Magnesium site and doping of the precursor Boron powders with Aluminum and Silicon. The best result in terms of Jc has been achieved by Silicon doping that, moreover, does not significantly affect the transition temperature.

cond-mat.supr-con↗

arXiv2001

Large transport critical currents in unsintered MgB2 superconducting tapes

The Powder-In-Tube process has been employed to fabricate tape-like conductors with a strong metallic sheath and based on the newly discovered MgB2 superconducting phase. Long superconducting tapes have been prepared by packing reacted MgB2 powders inside pure Ag, Cu and Ni tubes which are then cold worked by drawing and rolling. Such tapes have shown transport properties as good as bulk MgB2 samples sintered in high pressure and high temperature conditions. At 4.2 K, the highest critical current density of 100000 A/cm2 has been achieved on Nickel-sheathed single-filament conductors. A direct correlation between the sheath tensile strength and the critical current of the unsintered tape has been observed.

cond-mat.supr-con↗

arXiv1997

The Crossover beteween Aslamazov-Larkin and Short Wavelength Fluctuations Regimes in HTS Conductivity Experiments

We present paraconductivity (AL) measurements in three different high temperature superconductors: a melt textured $YBa_2Cu_3O_7$ sample, a $Bi_2Sr_2CaCu_2O_8$ epitaxial thin film and a highly textured $Bi_2Sr_2Ca_2Cu_3O_{10}$ tape. The crossovers between different temperature regimes in excess conductivity have been analysed. The Lawrence-Doniach (LD) crossover, which separates the 2D and 3D regimes, shifts from lower to higher temperatures as the compound anisotropy decreases. Once the LD crossover is overcome, the fluctuation conductivity of the three compounds shows the same universal behaviour: for $ε=\ln T/T_c > 0.23$ all the curves bend down according to the $1/ε^3$ law. This asymptotic behaviour was theoretically predicted previously for the high temperature region where the short wavelength fluctuations (SWF) become important.

cond-mat↗