Analysis of Nb3Sn surface layers for superconducting RF cavity applications

We present an analysis of the Nb3Sn surface layers grown on a bulk niobium (Nb) coupon prepared at the same time and by the same vapor diffusion process used to make Nb3Sn coatings on 1.3 GHz cavities. Tunneling spectroscopy reveals a well-developed, homogeneous superconducting density of states at the surface with a gap value distribution centered around 2.7 meV and superconducting critical temperature (Tc) up to 16.3 K. Scanning Electron microscopy (STEM) performed on cross section of the sample's surface region shows a 2 microns thick Nb3Sn surface layer. The elemental composition map exhibits a Nb over Sn ratio of 3 and reveals the presence of buried sub-stoichiometric regions that have a ratio f 5. Synchrotron x-ray diffraction experiments indicate a polycrystalline Nb3Sn film and confirm the presence of Nb rich regions that occupy about a third of the coating volume. These low Tc regions could play an important role in the dissipation mechanism occurring during RF tests of Nb3Sn-coated cavities and open the way for further improving a very promising alternative to pure Nb cavities for particle accelerators.

cond-mat.supr-con↗

arXiv2014

Nitrogen-Doped 9-Cell Cavity Performance in a Test Cryomodule for LCLS-II

The superconducting RF linac for LCLS-II calls for 1.3 GHz 9-cell cavities with an average intrinsic quality factor Q0 of 2.7x10^10 at 2 K and 16 MV/m accelerating gradient. Two niobium 9-cell cavities, prepared with nitrogen-doping at Fermilab, were assembled into the Cornell Horizontal Test Cryomodule (HTC) to test cavity performance in a cryomodule that is very similar to a full LCLS-II cryomodule. The cavities met LCLS-II specifications with an average quench field of 17 MV/m and an average Q0 of 3x10^10. The sensitivity of the cavities' residual resistance to ambient magnetic field was determined to be 0.5 nOhm/mG during fast cool down. In two cool downs, a heater attached to one of the cavity beam tubes was used to induce large horizontal temperature gradients. Here we report on the results of these first tests of nitrogen-doped cavities in cryomodule, which provide critical information for the LCLS-II project.

physics.acc-ph↗