arXiv2026

Diamond Diode for Extreme Venus Environments

A diamond Schottky PIN diode (SPIND) with the highest reported current density to date of ~116 kA/cm2 is demonstrated carrying a total current of ~1.3 A through a 50 micron wide pseudo-vertical diode structure. The diamond SPIND also provides a maximum power handling capacity of 1.85 MW/cm2 and a low specific on-resistance Ron,S of 0.05 mOhm-cm2 at a forward bias of ~16 V. The diamond SPIN diode also shows excellent rectification characteristics with a current on-off ratio of ~6e12. An analytical model including thermionic emission and space charge limited current is presented together with Silvaco ATLAS TCAD simulations, to accurately reproduce the experimental J-V characteristics using multiple single trap levels and other physical models emulating a real device. Theoretical analysis from the analytical models in conjunction with ATLAS simulations shows that further improvement in the device turn on voltage and Ron,S can be achieved by reducing the defect density and contact resistance in order to approach the ultimate performance in the Mott-Gurney space charge limited current regime

cond-mat.mtrl-sci↗

arXiv2021

Effects of Proton Irradiation on Hole Carrier Transport in Hydrogen-Terminated Diamond Surfaces

In this letter, we report the effects of irradiating hydrogen-terminated diamond surfaces with protons. We study the electrical behavior of the two-dimensional hole gas that forms on the diamond surface as a result of hydrogen-termination. Four diamond samples, two of which were passivated with Al2O3 and the other two unpassivated, were irradiated with 2 MeV protons at two fluences, 0.5x10^14 and 1.0x10^14 /cm^2. The hole conductivity degraded at a higher proton fluence, which is attributed to the reduction of the mobility caused by enhanced hole scattering. Both passivated and unpassivated samples exhibited a reduction in the mobility, which can be explained by charging effects of the Al2O3 (for the passivated samples) and degradation of the hydrogen-terminated surface (for the unpassivated samples). To our knowledge, this is the first reported data on 2 MeV proton tolerance of hydrogen-terminated diamond surfaces.

cond-mat.mtrl-sci↗

arXiv2020

Analysis of the Mobility-Limiting Mechanisms of the Two-Dimensional Hole Gas on Hydrogen-Terminated Diamond

Here we present an analysis of the mobility-limiting mechanisms of a two-dimensional hole gas on hydrogen-terminated diamond surfaces. The scattering rates of surface impurities, surface roughness, non-polar optical phonons, and acoustic phonons are included. Using a Schrodinger/Poisson solver, the heavy hole, light hole, and split-off bands are treated separately. To compare the calculations with experimental data, Hall-effect structures were fabricated and measured at temperatures ranging from 25 to 700 K, with hole sheet densities ranging from 2 to 6$\times10^{12}\;\text{cm}^{-2}$ and typical mobilities measured from 60 to 100 cm$^{2}$/(V$\cdot$s) at room temperature. Existing data from literature was also used, which spans sheet densities above 1$\times10^{13}\;\text{cm}^{-2}$. Our analysis indicates that for low sheet densities, surface impurity scattering by charged acceptors and surface roughness are not sufficient to account for the low mobility. Moreover, the experimental data suggests that long-range potential fluctuations exist at the diamond surface, and are particularly enhanced at lower sheet densities. Thus, we propose a second type of surface impurity scattering which is caused by disorder related to the C-H dipoles.

physics.app-ph↗