arXiv2009

Nanostructural Superconducting Materials for Fault Current Limiters and Cryogenic Electrical Machines

Materials of the Y-Ba-Cu-O (melt-textured YBa2Cu3O7-d-based materials or MT-YBCO) and Mg-B-O (MgB2-based materials) systems with high superconducting performance, which can be attained due to the formation of regularly distributed nanostructural defects and inhomogenities in their structure can be effectively used in cryogenic technique, in particular in fault current limiters and electrical machines (electromotors, generators, pumps for liquid gases, etc.). The developed processes of high-temperature (900-800 oC) oxygenation under elevated pressure (16 MPa) of MT-YBCO and high-pressure (2 GPa) synthesis of MgB2-based materials allowed us to attain high SC (critical current densities, upper critical fields, fields of irreversibility, trapped magnetic fields) and mechanical (hardness, fracture toughness, Young modulus) characteristics. It has been shown that the effect of materials properties improvement in the case of MT-YBCO was attained due to the formation of high twin density (20-22 micron-1), prevention of macrockracking and reduction (by a factor of 4.5) of microcrack density, and in the case of MgB2-based materials due to the formation of oxygen-enriched as compared to the matrix phase fine-dispersed Mg-B-O inhomogenities as well as inclusions of higher borides with near-MgB12 stoichiometry in the Mg-B-O matrix (with 15-37 nm average grain sizes). The possibility is shown to obtain the rather high Tc (37 K) and critical current densities in materials with MgB12 matrix (with 95 percent of shielding fraction as calculated from the resistant curve).

cond-mat.supr-con↗

arXiv2009

Effect of higher borides and inhomogeneity of oxygen distribution on critical current density of undoped and doped magnesium diboride

The effect of doping with Ti, Ta, SiC in complex with synthesis temperature on the amount and distribution of structural inhomogeneities in MgB2 matrix of high-pressuresynthesized-materials (2 GPa) which can influence pining: higher borides (MgB12) and oxygen-enriched Mg-B-O inclusions, was established and a mechanism of doping effect on jc increase different from the generally accepted was proposed. Near theoretically dense SiC-doped material exhibited jc= 1000000 A/sq. cm in 1T field and Hirr =8.5 T at 20 K. The highest jc in fields above 9, 6, and 4 T at 10, 20, and 25 K, respectively, was demonstrated by materials synthesized at 2 GPa, 600 oC from Mg and B without additions (at 20 K jc= 100 A/sq. cm in 10 T field). Materials synthesized from Mg and B taken up to 1:20 ratio were superconductive. The highest jc (60000 A/sq. cm at 20 K in zero field, Hirr= 5 T) and the amount of SC phase (95.3 percents of shielding fraction), Tc being 37 K were demonstrated by materials having near MgB12 composition of the matrix. The materials with MgB12 matrix had a doubled microhardness of that with MgB2 matrix (25 GPa and 13.08 GPa, at a load of 4.9 N, respectively).

cond-mat.supr-con↗

arXiv2008

The effect of the noncentral impurity-matrix interaction upon the thermal expansion and polyamorphism of solid CO-C60 solutions at low temperatures

Orientational glasses with CO molecules occupying 26% and 90% of the octahedral interstitial sites in the C60 lattice have been investigated by the dilatometric method in a temperature interval of 2.5 - 23 K. At temperatures 4 - 6 K the glasses undergo a first-order phase transition which is evident from the hysteresis of the thermal expansion and the maxima in the temperature dependences of the linear thermal expansion coefficients, and the thermalization times of the samples. The effect of the noncentral CO-C60 interaction upon the thermal expansion and the phase transition in these glasses was clarified by comparing the behavior of the properties of the CO-C60 and N2-C60 solutions.

cond-mat.dis-nn↗