arXiv2010

Magneto-optical study of Ba(Fe$_{1-x}$T$_{x}$)$_2$As$_2$ (T=Co, Ni) single crystals irradiated with heavy-ions

Optimally doped single crystals of Ba(Fe$_{1-x}$T$_x$)$_2$As$_2$ (T=Co, Ni) were irradiated with 1.4 GeV $^{208}$Pb$^{56+}$ ions at fluences corresponding to matching fields of $B_ϕ=0.1, 0.5, 1$ and 2 T. Magneto-optical imaging has been used to map the distribution of the magnetic induction in the irradiated samples. The imaging is complemented by the magnetization measurements. The results show a substantial enhancement of the apparent critical current densities as revealed by the much larger Bean penetration fields and an increase of the hysteretic magnetization. However, the effect depends on the compound, temperature and applied magnetic field. In \FeCo crystals, at 15 K and low fields, the enhancement appears to scale with the irradiation dose at a rate of about 0.27 MA$\cdot$cm$^{-2}$T$^{-1}$, whereas in \FeNi crystals, higher irradiation doses are less effective. Our results suggest that moderate irradiation with heavy ions is a an effective way to \emph{homogeneously} enhance the current-currying capabilities of pnictide superconductors.

cond-mat.supr-con↗

arXiv2009

Three-dimensional nodal superconducting gap in single crystals Ba(Fe$_{1-x}$Ni$_x$)$_2$As$_2$

The London penetration depth, $λ$, is directly related to the density, $n_{s}$, of the Cooper pairs ($λ^{2}\propto 1/n_{s}$) and its variation with temperature provides valuable insight into the pairing mechanism. Here we study the evolution with doping of the temperature dependence of the in-plane ($λ_{ab}$) and out-of-plane ($λ_{c}$) penetration depths in single crystals of electron-doped Ba(Fe$_{1-x}$Ni$_x$)$_2$As$_2$. As is the case for other pnictides, $λ(T) \sim T^n$ over the whole doping range and this behavior extends down to at least $T=T_c/100$, setting a very small upper limit on the gap minimum. Furthermore, in the overdoped regime: 1) the exponent $n$ becomes substantially smaller than 2, which is incompatible with the models that explain power-law behavior to be due to scattering; 2) the exponent $n$ becomes anisotropic, with $λ_{c}(T)$ showing a clear $T$-linear behavior over a large temperature interval. These findings suggest that in the overdoped regime the superconducting gap in iron-based pnictide superconductors develops nodal structure, which unlike in the cuprates, cannot be understood within a two-dimensional picture.

cond-mat.supr-con↗

arXiv2009

Intrinsic pinning on structural domains in underdoped single crystals of Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$

Critical current density was studied in single crystals of Ba(Fe$_{1-x}$Co$_x$)$_2$As$_2$ for the values of $x$ spanning the entire doping phase diagram. A noticeable enhancement was found for slightly underdoped crystals with the peak at $x = 0.058$. Using a combination of polarized-light imaging, x-ray diffraction and magnetic measurements we associate this behavior with the intrinsic pinning on structural domains in the orthorhombic phase. Domain walls extend throughout the sample thickness in the direction of vortices and act as extended pinning centers. With the increasing $x$ domain structure becomes more intertwined and fine due to a decrease of the orthorhombic distortion. This results in the energy landscape with maze-like spatial modulations favorable for pinning. This finding shows that iron-based pnictide superconductors, characterized by high values of the transition temperature, high upper critical fields, and low anisotropy may intrinsically have relatively high critical current densities.

cond-mat.supr-con↗

arXiv2009

Structural phase transition in Ba(Fe0.973Cr0.027)2As2 single crystals

We present thermodynamic, structural and transport measurements on Ba(Fe0.973Cr0.027)2As2 single crystals. All measurements reveal sharp anomalies at ~ 112 K. Single crystal x-ray diffraction identifies the structural transition as a first order, from the high-temperature tetragonal I4/mmm to the low-temperature orthorhombic Fmmm structure, in contrast to an earlier report.

cond-mat.mtrl-sci↗

arXiv2009

Phase diagrams of Ba(Fe(1-x)TMx)2As2 (TM = Rh, Pd) single crystals

Single crystalline Ba(Fe(1-x)TMx)2As2 (TM = Rh, Pd) series have been grown and characterized by structural, thermodynamic and transport measurements. These measurements show that the structural/magnetic phase transitions, found in pure BaFe2As2 at 134 K, are suppressed monotonically by the doping and that superconductivity can be stablized over a dome-like region. Temperature-composition (T-x) phase diagrams based on electrical transport and magnetization measurements are constructed and compared to those of the Ba(Fe(1-x)TMx)2As2 (TM = Co, Ni) series. Despite the generic difference between 3d and 4d shells and the specific, conspicuous differences in the changes to the unit cell parameters, the effects of Rh doping are exceptionally similar to the effects of Co doping and the effects of Pd doping are exceptionally similar to the effects of Ni doping. These data show that whereas the structural / antiferromagnetic phase transition temperatures can be parameterized by x and the superconducting transition temperature can be parameterized by some combination of x and e, the number of extra electrons associated with the TM doping, the transition temperatures of 3d- and 4d- doped BaFe2As2 can not be simply parameterized by the changes in the unit cell dimensions or their ratios.

cond-mat.supr-con↗

arXiv2009

Effect of pressure on transport and magnetotransport properties in CaFe2As2 single crystals

The effects of pressure generated in a liquid medium, clamp, pressure cell on the in-plane and c-axis resistance, temperature-dependent Hall coefficient and low temperature, magnetoresistance in CaFe2As2 are presented. The T - P phase diagram, including the observation of a complete superconducting transition in resistivity, delineated in earlier studies is found to be highly reproducible. The Hall resistivity and low temperature magnetoresistance are sensitive to different states/phases observed in CaFe2As2. Auxiliary measurements under uniaxial, c-axis, pressure are in general agreement with the liquid medium clamp cell results with some difference in critical pressure values and pressure derivatives. The data may be viewed as supporting the potential importance of non-hydrostatic components of pressure in inducing superconductivity in CaFe2As2.

cond-mat.supr-con↗

arXiv2009

Muon Spin Rotation Measurement of the Magnetic Field Penetration Depth in Ba(Fe0.93 Co0.07)2 As2 : Evidence for Multiple Superconducting Gaps

We have performed transverse field muon spin rotation measurements of single crystals of Ba(Fe$_{0.93}$Co$_{0.07})_2$As$_2$ with the applied magnetic field along the $\hat{c}$ direction. Fourier transforms of the measured spectra reveal an anisotropic lineshape characteristic of an Abrikosov vortex lattice. We have fit the $μ$SRSR spectra to a microscopic model in terms of the penetration depth $λ$ and the Ginzburg-Landau parameter $κ$. We find that as a function of temperature, the penetration depth varies more rapidly than in standard weak coupled BCS theory. For this reason we first fit the temperature dependence to a power law where the power varies from 1.6 to 2.2 as the field changes from 200G to 1000G. Due to the surprisingly strong field dependence of the power and the superfluid density we proceeded to fit the temperature dependence to a two gap model, where the size of the two gaps is field independent. From this model, we obtained gaps of $2Δ_1=3.7k_BT_c$ and $2Δ_2=1.6k_BT_c$, corresponding to roughly 6 meV and 3 meV respectively.

cond-mat.supr-con↗

arXiv2009

Influence of Magnetism on Phonons in CaFe2As2 Via Inelastic X-ray Scattering

In the iron pnictides, the strong sensitivity of the iron magnetic moment to the arsenic position suggests a significant relationship between phonons and magnetism. We measured the phonon dispersion of several branches in the high temperature tetragonal phase of CaFe2As2 using inelastic x-ray scattering on single-crystal samples. These measurements were compared to ab initio calculations of the phonons. Spin polarized calculations imposing the antiferromagnetic order present in the low temperature orthorhombic phase dramatically improve agreement between theory and experiment. This is discussed in terms of the strong antiferromagnetic correlations that are known to persist in the tetragonal phase.

cond-mat.supr-con↗

arXiv2009

Itinerant magnetic excitations in antiferromagnetic CaFe2As2

Neutron scattering measurements of the magnetic excitations in single crystals of antiferromagnetic CaFe2As2 reveal steeply dispersive and well-defined spin waves up to an energy of 100 meV. Magnetic excitations above 100 meV and up to the maximum energy of 200 meV are however broader in energy and momentum than the experimental resolution. While the low energy modes can be fit to a Heisenberg model, the total spectrum cannot be described as arising from excitations of a local moment system. Ab-initio calculations of the dynamic magnetic susceptibility suggest that the high energy behavior is dominated by the damping of spin waves by particle-hole excitations.

cond-mat.supr-con↗

arXiv2009

Complete pressure dependent phase diagrams for SrFe2As2 and BaFe2As2

The temperature dependent electrical resistivity of single crystalline SrFe2As2 and BaFe2As2 has been measured in a liquid medium, modified Bridgman anvil cell for pressures in excess of 75 kbar. These data allow for the determination of the pressure dependence of the higher temperature, structural / antiferromagnetic phase transitions as well as the lower temperature superconducting phase transition. For both compounds the ambient pressure, higher temperature structural / antiferromagnetic phase transition can be fully suppressed with a dome-like region of zero resistivity found to be centered about its critical pressure. Indeed, qualitatively, the temperature dependence of the resistivity curves closest to the critical pressures are the closest to linear, consistent with possible quantum criticality. For pressures significantly higher than the critical pressure the zero resistivity state is suppressed and the low temperature resistivity curves asymptotically approach a universal, low temperature manifold. These results are consistent with the hypothesis that correlations / fluctuations associated with the ambient-pressure, high-temperature, tetragonal phase have to be brought to low enough temperature to allow superconductivity, but if too fully suppressed can lead to the loss of the superconducting state.

cond-mat.supr-con↗

arXiv2009

Quasiparticle Heat Transport in Ba$_{1-x}$K$_x$Fe$_2$As$_2$: Evidence for a k-dependent Superconducting Gap without Nodes

The thermal conductivity $κ$ of the iron-arsenide superconductor Ba$_{1-x}$K$_x$Fe$_2$As$_2$ ($T_c \simeq$ 30 K) was measured in single crystals at temperatures down to $T \simeq 50$ mK ($\simeq T_c$/600) and in magnetic fields up to $H = 15$ T ($\simeq H_{c2}$/4). A negligible residual linear term in $κ/T$ as $T \to 0$ shows that there are no zero-energy quasiparticles in the superconducting state. This rules out the existence of line and in-plane point nodes in the superconducting gap, imposing strong constraints on the symmetry of the order parameter. It excludes d-wave symmetry, drawing a clear distinction between these superconductors and the high-$T_c$ cuprates. However, the fact that a magnetic field much smaller than $H_{c2}$ can induce a residual linear term indicates that the gap must be very small on part of the Fermi surface, whether from strong anisotropy or band dependence, or both.

cond-mat.supr-con↗

arXiv2009

Decoupling of the superconducting and magnetic (structural) phase transitions in electron-doped BaFe2As2

Study and comparison of over 30 examples of electron doped BaFe2As2 for transition metal (TM) = Co, Ni, Cu, and (Co/Cu mixtures) have lead to an understanding that the suppression of the structural/antiferromagnetic phase transition to low enough temperature in these compounds is a necessary condition for superconductivity, but not a sufficient one. Whereas the structural/antiferromagnetic transitions are suppressed by the number of TM dopant ions (or changes in the c-axis) the superconducting dome exists over a limited range of values of the number of electrons added by doping (or values of the {a/c} ratio). By choosing which combination of dopants are used we can change the relative positions of the upper phase lines and the superconducting dome, even to the extreme limit of suppressing the upper structural and magnetic phase transitions without the stabilization of low temperature superconducting dome.

cond-mat.supr-con↗

arXiv2009

Direct imaging of the structural domains in iron pnictides AFe2As2 (A = Ca, Sr, Ba)

The parent compounds of recently discovered iron-arsenide superconductors, $A$Fe$_2$As$_2$ with alkaline earth $A$=Ca, Sr, Ba, undergo simultaneous structural and magnetic phase transitions at a temperature $T_{SM}$. Using a combination of polarized light microscopy and spatially resolved high-energy synchrotron X-ray diffraction we show that the orthorhombic distortion leads to the formation of 45$^o$-type structural domains in all parent compounds. Domains penetrate through the sample thickness in the $c$- direction and are not affected by crystal defects such as growth terraces. The domains form regular stripe patterns in the plane with a characteristic dimension of 10 to 50 $μm$. The direction of the stripes is fixed with respect to the tetragonal (100) and (010) directions but can change by 90$^o$ on thermal cycling through the transition. This domain pattern may have profound implications for intrinsic disorder and anisotropy of iron arsenides.

cond-mat.supr-con↗

arXiv2009

Competition and coexistence of antiferromagnetism and superconductivity in underdoped Ba(Fe0.953Co0.047)2As2

Neutron and x-ray diffraction studies show that the simultaneous first-order transition to an orthorhombic and antiferromagnetic (AFM) ordered state in BaFe2As2 splits into two transitions with Co doping. For Ba(Fe0.953Co0.047)2As2, a tetragonal-orthorhombic transition occurs at TS = 60 K, followed by a second-order transition to AFM order at TN = 47 K. Superconductivity (SC) occurs in the orthorhombic state below TC = 15 K and coexists with AFM. Below TC, the static Fe moment is reduced and a 4 meV spin gap develops indicating competition between coexisting SC and AFM order.

cond-mat.supr-con↗

arXiv2009

Resistivity Anisotropy of $AE$Fe$_2$As$_2$ ($AE$ =Ca, Sr, Ba): direct versus Montgomery technique measurements

The anisotropy of electrical resistivity was measured in parent compounds of the iron-arsenic high temperature superconductors, AEFe2As2 with Alkali Earth elements AE=Ca,Sr, Ba. Measurements were performed using both the Montgomery technique and direct resistivity measurements on samples cut along principal crystallographic directions. The anisotropy ratio γ_ρ=ρ_c/ρ_a is well below 10 for all compounds in the whole temperature range studied (4 to 300 K), in notable contrast to previous reports. The anisotropy at room temperature increases from about 2 in Ca, to about 4 in Sr and Ba. In all compounds the resistivity ratio decreases on cooling through the structural/antiferromagnetic transition temperature T_{SM}, with the change mainly coming from stronger variation in ρ_a as compared with ρ_c. This suggests that the transitions stronger affect the two-dimensional parts of the Fermi surface. We compare our experimental observations with band structure calculations, and find similar trend in the evolution of anisotropy with the size of AE ion. Our results show that the electronic structure of the iron pnictides has large contribution from three-dimensional areas of the Fermi surface.

cond-mat.supr-con↗

arXiv2009

Non-exponential London penetration depth in Ba$_{1-}$K$_{x}$Fe$_{2}$As$_{2}$ single crystals

We have studied the in- and out-of-plane magnetic penetration depths in the hole- doped iron based superconductor Ba$_{1-x}$K$_{x}$Fe$_{2}$As$_{2}$ ($T_{c}\approx$ 30K). The study was performed on single crystals grown from different fluxes and we find that the results are nearly the same. The in-plane London penetration depth $λ_{ab}$ does not show exponential saturation at low temperature, as would be expected from a fully gapped superconductor. Instead, $λ_{ab}(T)$ shows a power-law behavior, $λ\propto T^{n}$ ($n\approx 2$), down to $T\approx 0.02 T_{c}$, similar to the electron doped Ba(Fe$_{1-x}$Co$_{x}$)$_{2}$As$_{2}$. The penetration depth anisotropy $γ_λ=λ_{c}(T)/λ_{ab}(T)$ increases upon cooling, opposite to the trend observed in the anisotropy of the upper critical field, $γ_ξ=H_{c2}^{\perp c}(0)/H_{c2}^{\parallel c}(0)$. These are universal characteristics of both the electron and hole doped 122 systems, suggesting unconventional superconductivity. The behavior of the in-plane superfluid density $ρ_{ab}(T)$ is discussed in light of existing theoretical models proposed for the iron pnictides superconductors.

cond-mat.supr-con↗

arXiv2009

Electronic structure of CaFe2As2: Contribution of itinerant Fe 3d-states to the Fermi Level

We present density functional theory (DFT) calculations and a full set of X-ray spectra (resonant inelastic X-ray scattering and X-ray photoelectron spectra) measurements of single crystal CaFe2As2. The experimental valence band spectra are consistent with our DFT calculations. Both theory and experiment show that the Fe 3d-states dominate the Fermi level and hybridize with Ca 3d-states. The simple shape of Xray photoelectron (XPS) Fe 2p-core level spectrum (without any satellite structure typical for correlated systems) suggests itinerant character of the Fe 3d-electrons. Based on the similarity of the calculated and experimental Fe 3d-states distribution in LaOFeAs and CaFe2As2 we conclude that superconductivity in the FeAs-systems can be described within a minimal model, taking into account only Fe 3d-bands close to the Fermi level.

cond-mat.supr-con↗

arXiv2009

Doping dependent Irreversible Magnetic Properties of Ba(Fe1-xCox)2As2 Single Crystals

We discuss the irreversible magnetic properties of self-flux grown Ba(Fe1-xCox)2As2 single crystals for a wide range of concentrations covering the whole phase diagram from the underdoped to the overdoped regime, x=0.038, 0.047, 0.058, 0.071, 0.074, 0.10, 0.106 and 0.118. Samples were characterized by a magneto-optical method and show excellent spatial uniformity of the superconducting state. The overall behavior closely follows classical Bean model of the critical state. The field-dependent magnetization exhibits second peak at a temperature and doping - dependent magnetic field, Hp. The evolution of this fishtail feature with doping is discussed. Magnetic relaxation is time-logarithmic and unusually fast. Similar to cuprates, there is an apparent crossover from collective elastic to plastic flux creep above Hp. At high fields, the field dependence of the relaxation rate becomes doping independent. We discuss our results in the framework of the weak collective pinning and show that vortex physics in iron-based pnictide crystals is much closer to high-Tc cuprates than to conventional s-wave (including MgB2) superconductors.

cond-mat.supr-con↗