arXiv2024

Competition between the modification of intrinsic superconducting properties and the pinning landscape under external pressure in CaKFe$_4$As$_4$ single crystals

Measurements of low field magnetization, trapped flux magnetization and 5 K flux creep in single crystal of CaKFe$_4$As$_4$ under pressure up to 7.5 GPa in a diamond pressure cell are presented. The observed evolution of the temperature dependence of the self-field critical current and slowing down of the base temperature flux creep rate are explained within the two sources of pinning hypothesis involving presence of CaKFe$_4$As$_4$ intergrowths suggested in the literature. Above the half collapsed tetragonal structural transition under pressure, where superconductivity is non-bulk or absent, critically diminished or no diamagnetism and flux trapped magnetization were observed.

cond-mat.supr-con↗

arXiv2023

Tuning vortex critical velocity in Mo$_2$N thin films via striped magnetic domain configuration

We report on the impact of the magnetic domain stripe configuration on the critical velocity of vortices in superconducting/ferromagnetic bilayers. Using a 23 nm thick Mo$_2$N film, covered by a 48 nm FePt layer with tunable nanosized striped domains, we demonstrate that flux instability at low magnetic fields depends on the orientation of the stripes. When the stripes are perpendicular to the applied current and act as vortex guides, the velocity values reach 5 km/s, duplicating those found when configured parallel to the current, creating winding vortex paths. Our results indicate that vortex critical velocities can be tuned by configuring different domain structures, providing a platform to understand vortex dynamics in superconducting microstrips.

cond-mat.supr-con↗

arXiv2019

Superconductivity in nanocrystalline tungsten thin films growth by sputtering in a nitrogen-argon mixture

We report on the structural and superconducting properties of nanocrystalline tungsten thin films growth by sputtering at room temperature with an N2:Ar mixture (N2 from 3% to 50%). The crystalline phases were identified by comparing pristine and thermal annealed thin films. For N2/(Ar+N2) mixtures between 3 and 10 %, the films display nanocrystalline beta-W phase. Coexistence of beta-W and W2N phases are observed for gas mixtures with N2 between 20 % and 40%. A detailed study of the superconducting properties as function of the thickness was performed for W films growth with 8 % N2 mixtures. For this concentration, the nitrogen atoms increase the disorder at the nanoscale reducing the grain size and avoiding the crystallization of alpha-W. The superconducting critical temperature (Tc = 4.7 K) is thickness independent for films thicker than ~ 17 nm. Below this thickness, the Tc value decreases systematically being 3.1 K for 4 nm thick films. Our study provides a simple method for the fabrication of nanocrystalline beta-W thin films with potential applications in superconducting devices.

cond-mat.mtrl-sci↗