Cold dwell behaviour of Ti$_6$Al alloy: Understanding load shedding using digital image correlation and crystal plasticity simulations

Digital image correlation (DIC) and crystal plasticity simulation were utilised to study cold dwell behaviour in a coarse grain Ti-6Al alloy at 3 different temperatures up to 230 C. Strains extracted from large volume grains were measured during creep by DIC and were used to calibrate the crystal plasticity model. The values of critical resolved shear stresses (CRSS) of the two main slip systems (basal and prismatic) were determined as a function of temperature. Stress along paths across the boundaries of two grain pairs, (1) a `rogue' grain pair and (2) a `non-rogue' grain pair, were determined at different temperatures. Load shedding was observed in the `rogue' grain pair, where a stress increment during the creep period was found in the `hard' grain. At elevated temperatures, 120 C was found to be the worst-case scenario as the stress difference at the grain boundaries of these two grain pairs were found to be the largest among the three temperatures. This can be attributed to the fact that the strain rate sensitivity of both prismatic and basal slip systems is at its greatest in this worst-case scenario temperature.

cond-mat.mtrl-sci↗

arXiv2020

An in-situ synchrotron diffraction study of stress relaxation in titanium: Effect of temperature and oxygen on cold dwell fatigue

There is a long-standing technological problem in which a stress dwell during cyclic loading at room temperature in Ti causes a significant fatigue life reduction. It is thought that localised time dependent plasticity in soft grains favourably oriented for easy plastic slip leads to load shedding and an increase in stress within a neighbouring hard grain poorly oriented for easy slip. Quantifying this time dependent plasticity process is key to understand the complex cold dwell fatigue problem. Knowing the effect of operating temperature and oxygen content on cold dwell fatigue will be beneficial for future alloy design to address this problem. In this work, synchrotron X-ray diffraction during stress relaxation experiments was used to characterise the time dependent plastic behaviour of two commercially pure titanium samples (grade 1 and grade 4) with different oxygen content at 4 different temperatures (room temperature, 75C, 145C and 250C). Lattice strains were measured by tracking the diffraction peak shift from multiple crystallographic plane families (21 diffraction rings) as a function of their orientation with respect to the loading direction. Critical resolved shear stress, activation energy and activation volume were established for both prismatic and basal slip as a function of temperature and oxygen content by fitting a crystal plasticity finite element model to the lattice strain relaxation responses measured along the loading axis for five strong reflections. Higher strain rate sensitivity was found to lead to higher plasticity during cold dwell.

cond-mat.mtrl-sci↗