arXiv2019

Electrical conductivity in extremely disordered molybdenum oxynitrides thin films

We report on the influence of the chemical composition on the electronic properties of molybdenum oxynitrides thin films grown by reactive sputtering on Si (100) substrates at room temperature. The partial pressure of Ar was fixed at 90 %, and the remaining 10 % was adjusted with mixtures N$_2$:O$_2$ (varying from pure N$_2$ to pure O$_2$). The crystalline and electronic structures and the electrical transport of the films depend on the chemical composition. Thin films grown using oxygen mixtures up 2 % have gamma-Mo$_2$N phase and display superconductivity. The superconducting critical temperature T$_c$ reduces from ~ 6.8 K to below 3.0 K as the oxygen increases. On the other hand, films grown using oxygen mixtures richer than 2 % are mostly amorphous. The electrical transport shows a semiconductor-like behavior with variable-range hopping conduction at low temperatures. The analysis of the optical properties reveals that the samples have not a defined semiconductor band gap, which can be related to the high structural disorder and the excitation of electrons in a wide range of energies

cond-mat.mtrl-sci↗

arXiv2018

Synthesis of nanocrystalline d-MoN by thermal annealing of amorphous thin films grown on (100) Si by reactive DC sputtering at room temperature

We report on the synthesis and characterization of nanocrystalline delta-MoN by crystallization of amorphous thin films grown on (100) Si by reactive sputtering at room temperature. Films with chemical composition MoN were grown using a deposition pressure of 5mTorr with a reactive mixture of Ar/(Ar+N2)=0.5. The as-grown films display mostly amorphous structure. Nanocrystalline delta-MoN phase is obtained after annealing at temperatures above 600 °C. The superconducting critical temperature Tc depends on film thickness. Thick films (170 nm) annealed at 700 °C for 30 min display a Tc = 11.2 K (close to the one reported for bulk specimens: 13 K), which is gradually suppressed to 7.2 K for 40 nm thick delta-MoN films. Our results provide a simple method to synthesize superconducting nitride thin films on silicon wafers with Tc above the ones observed for conventional superconductors such as Nb.

cond-mat.mtrl-sci↗

arXiv2017

Effect of the nitrogen-argon gas mixtures on the superconductivity properties of reactively sputtered molybdenum nitride thin films

We report on the superconducting properties of molybdenum nitride thin films grown by reactive DC sputtering at room temperature with a N2:Ar mixture. Thin films grown using 5 % N2 concentration display Tc = 8 K, which is gradually reduced and abruptly disappears for 40 % N2 concentration. This suppression can be associated with changes in the nitrogen stoichiometry from Mo2N to MoN. Our results provide an effective and simple path to prepare Mo2Nx thin films with tunable Tc, which is relevant for the investigation of the fundamental properties and for technological applications.

cond-mat.mtrl-sci↗

arXiv2017

Effect of mixed pinning landscapes produced by 6 MeV Oxygen irradiation on the resulting critical current densities J$_c$ in 1.3 $μ$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductors grown by co-evaporation

We report the influence of crystalline defects introduced by 6 MeV $^{16}$O$^{3+}$ irradiation on the critical current densities J$_c$ and flux creep rates in 1.3 $μ$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductor produced by co-evaporation. Pristine films with pinning produced mainly by random nanoparticles with diameter close to 50 nm were irradiated with doses between 2x10$^{13}$ cm$^{-2}$ and 4x10$^{14}$ cm$^{-2}$. At temperatures below 40 K with the magnetic field applied parallel (H//c) and at 45° (H//45°) to the c-axis, the in-field J$_c$ dependences can be significantly improved by irradiation. For doses of 1x10$^{14}$ cm$^{-2}$ the J$_c$ values at $μ$$_0$H = 5 T are doubled without affecting significantly the J$_c$ at small fields. Analyzing the flux creep rates as function of the temperature in both magnetic field configurations, it can be observed that the irradiation suppresses the peak associated with double-kink relaxation and increases the flux creep rates at intermediate and high temperatures. Under 0.5 T, the flux relaxation for H//c and H//45° in pristine films presents characteristic glassy exponents $μ$ = 1.63 and $μ$ = 1.45, respectively. For samples irradiated with 1x10$^{14}$ cm$^{-2}$, these values drop to $μ$ = 1.45 and $μ$ =1.24, respectively.

cond-mat.supr-con↗