arXiv2005

Ion-beam induced 1D to 3D periodic transformation in nanostructured multilayers

Ion-irradiation-induced modifications of a periodic Pt/C multilayer system containing Fe impurity have been analyzed by transmission electron microscopy (TEM). The multilayer stack with 16 Pt/C layer pairs (period 4.23 nm) was fabricated on a glass substrate. A 2 MeV Au$^{2+}$ ion beam was rastered on the sample to obtain uniformly irradiated strips with fluences from 1$\times10^{14}$ to 1$\times10^{15}$ $ions/cm^2$. Ion-irradiation has been found to cause preferential migration of Fe towards Pt layers [Nucl. Instr. Methods Phys. Res. B212 (2003) 530]. Cross-sectional transmission electron microscopy (XTEM) shows considerable atomic redistribution for irradiation at the highest ion fluence (1$\times10^{15}$ $ions/cm^2$). Individual entities in this structure is like a cluster. Periodic multilayers have periodicity only in the direction normal to the multilayer surface. However, Fourier transform of the XTEM images of the sample irradiated at the highest-fluence shows new off-normal Fourier components of superlattice periodicities arising due to ion irradiation. With a proper understanding of this phenomenon it may be possible to fabricate three dimensional periodic structures of nanoclusters.

cond-mat.mtrl-sci↗

arXiv2004

Electron and Phonon Confinement and New Surface Phonon Modes in CdSe-CdS Core-Shell Nanocrystals

Optical and vibrational properties of bare and CdS shelled CdSe nanocrystalline particles are investigated. To confirm the formation of such nanocrystals in our samples we estimate their average particle sizes and size distributions using TEM measurements. From the line profile analysis of the images the core-shell structure in the particles has been confirmed. The blue shift in optical absorption spectra, analyzed using theoretical estimates based on the effective bond order model, establishes the electron confinement in the nanoparticles. Unique characteristics of the nanocrystals (which are absent in the corresponding bulk material), such as confinement of optical phonons and the appearance of surface phonons, are then discussed. Making use of the dielectric response function model we are able to match the experimental and theoretical values of the frequencies of the surface phonons. We believe that our studies using optical probes provide further evidence on the existence of core-shell structures in CdSe-CdS type materials.

cond-mat.mtrl-sci↗

arXiv2004

Growth of silver nanoclusters embedded in soda glass matrix

Temperature-controlled-growth of silver nanoclusters in soda glass matrix is investigated by low-frequency Raman scattering spectroscopy. Growth of the nanoclusters is ascribed to the diffusion-controlled precipitation of silver atoms due to annealing the silver-exchanged soda glass samples. For the first time, Rutherford backscattering measurements performed in this system to find out activation energy for the diffusion of silver ions in the glass matrix. Activation energy for the diffusion of silver ions in the glass matrix estimated from different experimental results is found to be consistent.

cond-mat.mtrl-sci↗

arXiv2003

Height preference and strain in Ag islands on Si(111)-(7x7)

Growth and strain behavior of thin Ag films on Si substrate have been investigated by scanning tunneling microscopy, cross-sectional transmission electron microscopy and high resolution x-ray diffraction studies. Ag islands formed on Si at room temperature growth show strongly preferred heights and flat top. At low coverage, islands containing two atomic layers of Ag are overwhelmingly formed. At higher coverages island height distribution shows strong peaks at relative heights corresponding to an even number of Ag atomic layers. This appears to be a quantum size effect. Hexagonal disc-like islands with flat top are formed upon annealing. The annealed film shows two closely-spaced Ag(111) diffraction peaks - one weak and broad and the other narrow and more intense. The intense peak corresponds to a shorter Ag(111) planar spacing compared to the bulk value. This can be explained in terms of changes in the Ag lattice during the heating-cooling cycle due to thermal expansion coefficient mismatch between Ag and Si.

cond-mat.mtrl-sci↗

arXiv1994

Shape Transition in the Epitaxial Growth of Gold Silicide in Au Thin Films on Si(111)

Growth of epitaxial gold silicide islands on bromine-passivated Si(111) substrates has been studied by optical and electron microscopy, electron probe micro analysis and helium ion backscattering. The islands grow in the shape of equilateral triangles up to a critical size beyond which the symmetry of the structure is broken, resulting in a shape transition from triangle to trapezoid. The island edges are aligned along $Si[110]$ directions. We have observed elongated islands with aspect ratios as large as 8:1. These islands, instead of growing along three equivalent [110] directions on the Si(111) substrate, grow only along one preferential direction. This has been attributed to the vicinality of the substrate surface.

cond-mat↗