Effect of 200 MeV Ag15+ ion irradiation on structural and electrical transport properties of Fe3O4 thin films

Thin films of Fe3O4 have been deposited on single crystal MgO (100) and Si (100) substrates using pulsed laser deposition. Films grown on MgO substrate are epitaxial with c-axis orientation whereas, films on Si substrate are highly <111> oriented. Film thicknesses are 150 nm. These films have been irradiated with 200 MeV Ag ions. We study the effect of the irradiation on structural and electrical transport properties of these films. The fluence value of irradiation has been varied in the range of 5 x 1010 ions/cm2 to1 x 1012 ions/cm2. We compare the irradiation induced modifications on various physical properties between the c-axis oriented epitaxial film and non epitaxial but <111> oriented film. The pristine film on Si substrate shows Verwey transition (TV) close to 125 K, which is higher than generally observed in single crystals (121 K). After the irradiation with the 5 x 1010 ions/cm2 fluence value, TV shifts to 122 K, closer to the single crystal value. However, with the higher fluence (1 x 1012 ions/cm2) irradiation, TV again shifts to 125 K.

cond-mat.mtrl-sci↗

arXiv2009

Structural, electrical and magnetic properties of Mo1-xFexO2 (x=0-0.05) thin films grown by pulsed laser ablation

We report the growth of undoped and Fe (2 and 5 at. percentage) doped molybdenum oxide thin films on c-plane of sapphire substrate using pulsed laser ablation. X-ray diffraction results show that the films are oriented in (100) direction and have monoclinic structure based on MoO2 phase as also supported by Raman spectroscopy. The x-ray photoelectron spectroscopy reveals chemical state of Fe is +2, which favors the substitutional occupancy of Fe ion in the MoO2 matrix. The room temperature resistivity of all the films are very low (approx.100 microohm-cm). The Fe doped samples show ferromagnetic behavior at room temperature.

cond-mat.mtrl-sci↗

arXiv2009

Electrical and magnetic transport properties of Fe3O4 thin films on GaAs (100) substrate

Thin films of magnetite (Fe3O4) are grown on single crystal GaAs (100) substrate by pulsed laser deposition. X ray diffraction (XRD) result shows the (111) preferred orientation of the Fe3O4 film and x-ray photoelectron spectroscopy confirm the presence of single phase Fe3O4 in the film. The electrical transport property of the film shows the characteristic Verwey transition at 122 K and below 110 K, the transport follows variable range hopping type conduction mechanism. The film shows room temperature magnetization hysteresis loop suggesting the ferrimagnetic behavior of the film with saturation magnetization value close to 470 emu/cc.

cond-mat.mtrl-sci↗

arXiv2008

Effect of strain on the electronic structure of La0.7Ca0.3MnO3

The effect of substrate strain on the electronic valence band structure of La0.7Ca0.3MnO3 thin films has been investigated. For this purpose La0.7Ca0.3MnO3 thin films have been simultaneously grown on SrTiO3 and LaAlO3 substrates using pulsed laser deposition technique. These samples were characterized by x-ray diffraction, x-ray reflectivity, core level x-ray photoelectron spectroscopy, and scanning electron microscopy measurements. Our experiments confirmed that all these samples have same chemical composition but different strain configuration. The electronic structure of these samples is probed through valence band spectroscopy measurements on Indus-1 synchrotron x-ray source. We observe that strain has large effect on the valence band electronic structure of La0.7Ca0.3MnO3. The results are explained on the basis of strain induced orbital occupancy and change in the crystal field splitting due to Mn-O bond length.

cond-mat.str-el↗

arXiv2008

Origin of resistivity minima at low temperature in ferromagnetic metallic manganites

The resistivity and magnetoresistance measurements were carried out on thin film of La0.7Ca0.3MnO3 to investigate the possible origin of low temperature resistivity minimum observed in these samples. We observed large hysteresis in the magnetoresistance at low temperature; 5K and the sample current I has large effect on resistivity minima temperature. The observation of hysteresis at low temperatures suggests the presence of inhomogeneity at low temperatures. These in-homogeneities consist of regions of different resistive phases. It appears that the high resistive phase prevents the tunneling of charge carriers between two low resistive regions and thus giving rise to the resistivity minimum in these samples.

cond-mat.str-el↗

arXiv2008

Dispersion of Resonant Raman Peaks of CO and OH in SnO2, Mo1-x FexO2 Thin Films and SiO2 bulk glass

Resonance Raman (RR) peaks of and stretching modes and their higher harmonics have been observed superimposed on photoluminescence (PL) spectrum of thin films. Commercial fluorine doped thin films deposited by sputtering on glass and thin films deposited on Si by laser ablation have been studied. The dispersions of CO and OH stretching RR modes are ~ 600 cm-1/eV and 800 cm-1 respectively. The dispersion of the third harmonic of CO stretching mode is ~ 2000 cm-1/eV. Similar dispersion of RR peak of stretching modes and higher harmonics superimposed on PL spectra has been observed in Mo1-xFexO2 thin films and SiO2 bulk glass. Large dispersion of RR peaks seems to be a common property of oxides with impurities of and .

cond-mat.mtrl-sci↗

arXiv2003

Optical band edge shift of anatase cobalt-doped titanium dioxide

We report on the optical properties of magnetic cobalt-doped anatase phase titanium dioxide Ti_{1-x}Co_{x}O_{2-d} films for low doping concentrations, 0 <= x <= 0.02, in the spectral range 0.2 to 5 eV. For well oxygenated films (d << 1) the optical conductivity is characterized by an absence of optical absorption below an onset of interband transitions at 3.6 eV and a blue shift of the optical band edge with increasing Co concentration. The absence of below band gap absorption is inconsistent with theoretical models which contain midgap magnetic impurity bands and suggests that strong on-site Coulomb interactions shift the O-band to Co-level optical transitions to energies above the gap.

cond-mat.str-el↗

arXiv2003

Co-doped LaLa1-xSrxTiO3-d : A Diluted Magnetic Oxide System with High Curie Temperature

Ferromagnetism is observed at and above room temperature in pulsed laser deposited epitaxial films of Co-doped Ti-based oxide perovskite (La1-xSrxTiO3-d). The system has the characteristics of an intrinsic diluted magnetic semiconductor (metal) at low concentrations (<~ 2 %), but develops inhomogeneity at higher cobalt concentrations. The films range from being opaque metallic to transparent semiconducting depending on the oxygen pressure during growth and are yet ferromagnetic.

cond-mat.str-el↗

arXiv2003

High Temperature Ferromagnetism with Giant Magnetic Moment in Transparent Co-doped SnO2-d

Occurrence of room temperature ferromagnetism is demonstrated in pulsed laser deposited thin films of Sn1-xCoxO2-d (x<0.3). Interestingly, films of Sn0.95Co0.05O2-d grown on R-plane sapphire not only exhibit ferromagnetism with a Curie temperature close to 650 K, but also a giant magnetic moment of about 7 Bohr-Magneton/Co, not yet reported in any diluted magnetic semiconductor system. The films are semiconducting and optically highly transparent.

cond-mat↗