arXiv2004

Strongly enhancend anisotropic upper critical field in carbon substituted MgB2: impact of Fermi surface changes

The upper critical field Hc2||c(0) of 85 kOe in Mg(B0.94C0.06)2 single crystals, determined from torque measurements, is more than twice as large as that one of 31 kOe in unsubstituted MgB2. Anisotropy of Hc2 increases from about 3.4 near Tc, the value close to that in MgB2, to about 4 at low temperature, the value considerably lower than that in MgB2. The corresponding Hc2||ab(0) of about 330-350 kOe is likely close to the maximum enhancement due to C substitution. The position of a sharp peak in the irreversible torque Hmax was found to be shifted to lower reduced fields H/Hc2 in comparison to its position in unsubstituted MgB2, indicating increasing disorder. The enhancement of Hc2 can be explained as a disorder effect only if the main result of disorder is to make the p bands more dirty while not affecting the s bands as much. In addition to disorder and weakened electron-phonon coupling, the impact of the Fermi level shifting into a region with lower s Fermi velocities has to be taken into account in the analysis of Hc2 data as well.

cond-mat.supr-con↗

arXiv2003

MgB2 and Mg1-xAlxB2 single crystals: high-pressure growth and physical properties

Single crystals of MgB2 have been grown with a high-pressure cubic anvil technique. They grow via the peritectic decomposition of the MgNB9 ternary nitride. The crystals are of a size up to 2x1x0.1mm3 with a weight up to 230 micrograms. Typically they have transition temperatures between 38 and 38.6 K with a width of 0.3-0.5 K. Investigations of the P-T phase diagram prove that the MgB2 phase is stable at least up to 2190C at high hydrostatic pressure in the presence of Mg vapor under high pressure. Substitution of aluminum for magnesium in single crystals leads to stepwise decrease of Tc. This indicates a possible appearance of superstructures or phases with different Tc's. The upper critical field decreases with Al doping.

cond-mat.supr-con↗

arXiv2003

Anisotropic properties of MgB2 by torque magnetometry

Anisotropic properties of superconducting MgB2 obtained by torque magnetometry are compared to theoretical predictions, concentrating on two issues. Firstly, the angular dependence of Hc2 is shown to deviate close to Tc from the dependence assumed by anisotropic Ginzburg-Landau theory. Secondly, from the evaluation of torque vs angle curves it is concluded that the anisotropy of the penetration depth gamma_lambda has to be substantially higher at low temperature than theoretical estimates, at least in fields higher than 0.2 T.

cond-mat.supr-con↗

arXiv2003

Two band superconductivity in MgB2: basic anisotropic properties and phase diagram

Magnesium diboride MgB2 has been an extraordinarily hot research topic since the discovery of superconductivity below 40 K, due to the vast amount of unusual properties originating from the involvement in superconductivity of two sets of bands that are of a different dimensionality. We review, with a strong focus on results obtained by torque magnetometry, how this leads to a complex behavior of the anisotropic superconducting state properties. The different dimensionality of the two sets of bands is manifested in the upper critical field Hc2 anisotropy, which was found to strongly decrease with increasing temperature. While the angular dependence of Hc2 follows roughly the predictions of anisotropic Ginzburg-Landau theory AGLT, small, but systematic deviations were observed near Tc. This, and the temperature dependent anisotropy, witness a breakdown of the AGLT description of MgB2, even close to Tc. Theoretical calculations are in qualitative agreement with the observed angle dependence, but suggest a much lower penetration depth anisotropy at low temperatures. Reversible torque vs angle curves in the mixed state indicate that the penetration depth anisotropy in intermediate fields has to be higher than currently available theoretical estimates. The observed field dependent effective anisotropies can be accounted for qualitatively by the faster depression of superconductivity in the more isotropic bands by the applied field. The vortex matter phase diagram is drawn, based on measurements of the reversible and irreversible torque in the mixed state. In the irreversible torque, a peak effect (PE) was observed in fields of about 0.85 Hc2. History effects of the critical current density in the PE region suggest that the PE signifies an order-disorder transition of vortex matter.

cond-mat.supr-con↗

arXiv2003

Single crystal growth and properties of MgB2 and Mg(B1-xCx)2

Single crystals of MgB2 and Mg(B1-xCx)2 have been grown using cubic anvil technique. Tc values vary in a wide range (39-9 K) with carbon content varying from 0 up to 16%. Using SiC as the precursor leads to C and not to Si substituted crystals. Micro-hardness measurements performed on MgB2 single crystals give average value of 1100 kg/mm2.

cond-mat.supr-con↗

arXiv2003

On the effect of heterovalent substitutions in ruthenocuprates

We discuss the properties of superconducting derivatives of the RuSr2GdCu2O8 (1212-type) ruthenocuprate, for which heterovalent doping has been achieved through partial substitution of Cu ions into the RuO2 planes (Ru1-xSr2GdCu2+xO8-d, 0 Ru doping achieved in these phases is found to decrease the temperature for magnetic ordering as well the volume fraction of the magnetic phase.

cond-mat.supr-con↗

arXiv2003

Single crystal growth of MgB2 and thermodynamics of Mg-B-N system at high pressure

Single crystals of MgB2 have been grown at high pressure via the peritectic decomposition of MgNB9. The crystals are of a size up to 1.5x0.9x0.2 mm3 with a weight up to 0.23 mg, and typically have transition temperatures between 37 and 39 with a width of 0.3-0.5 K. Investigations of the P-T phase diagram prove that the MgB2 phase is stable at least up to 2190 C at high hydrostatic pressure in the presence of Mg vapor under high pressure. Small variations of Tc are caused by doping with metal elements from the precursor or annealing of defects during the crystal growth process.

cond-mat.supr-con↗

arXiv2002

Disorder-induced Phase Transition of Vortex Matter in MgB2

Measurements of single crystalline MgB2 with torque magnetometry in fields up to 90 kOe reveal a sharp peak in the irreversible torque at about 0.85 Hc2. In the region between peak onset and maximum, pronounced history effects occur. Angle and temperature dependence of the characteristic peak fields track those of Hc2. The features observed suggest that the peak marks a disorder-induced phase transition of vortex matter between a quasi-ordered Bragg glass and a highly-disordered glass.

cond-mat.supr-con↗

arXiv2002

Anisotropy of the superconducting state properties and phase diagram of MgB2 by torque magnetometry on single crystals

The angular and temperature dependence of the upper critical field Hc2 in MgB2 was determined from torque magnetometry measurements on single crystals. The Hc2 anisotropy gamma_H was found to decrease with increasing temperature, in disagreement with the anisotropic Ginzburg-Landau theory, which predicts that the gamma_H is temperature independent. This behaviour can be explained by the two band nature of superconductivity in MgB2. An analysis of measurements of the reversible torque in the mixed state yields a field dependent effective anisotropy gamma_eff, which can be at least partially explained by different anisotropies of the penetration depth and the upper critical field. It is shown that a peak effect in fields of about 0.85 Hc2 is a manifestation of an order-disorder phase transition of vortex matter. The H-T phase diagram of MgB2 for H//c correlates with the intermediate strength of thermal fluctuations in MgB2, as compared to those in high and low Tc superconductors.

cond-mat.supr-con↗

arXiv2002

Magnetism and superconductivity in Ru(1-x)Sr2RECu(2+x)O(8-d) (RE=Gd, Eu) and RuSr2Gd(1-y)Ce(y)Cu2O8 compounds

We discuss the properties of new superconducting compositions of Ru(1-x)Sr2RECu(2+x)O(8-d) (RE=Gd, Eu) ruthenocuprates that were synthesized at 600 atm. of oxygen at 1080 C. By changing ratio between the Ru and Cu, the temperature of superconducting transition (Tc) raises up to Tc max=72 K for x=0.3, 0.4. The hole doping achieved along the series increases with Cu->Ru substitution. For x different than x=0, Tc can be subsequently tuned between Tc max and 0 K by changing oxygen content in the compounds. The magnetic characteristics of the RE=Gd and Eu based compounds are interpreted as indicative of constrained dimensionality of the superconducting phase. Muon spin rotation experiments reveal the presence of the magnetic transitions at low temperatures (Tm=14-2 K for x=0.1-0.4) that can originate in the response of Ru/Cu sublattices. RuSr2Gd(1-y)Ce(1-y)Cu2O8 (0 Gd substitution. Properties of these two series allow us to propose phase diagram for 1212-type ruthenocuprates that links their properties to the hole doping achieved in the systems. Non-superconducting single-phase RuSr2GdCu2O8 and RuSr2EuCu2O8 are reported and discussed in the context of the properties of substituted compounds.

cond-mat.supr-con↗

arXiv2002

MgB2 single crystals: high pressure growth and anisotropic properties

Single crystals of MgB2 with a size up to 1.5x0.9x0.2 mm3 have been grown with a high pressure cubic anvil technique. The crystal growth process is very peculiar and involves an intermediate nitride, namely MgNB9. Single crystals of BN and MgB2 grow simultaneously by a peritectic decomposition of MgNB9. Magnetic measurements in fields of 1-5 Oe show sharp transitions to the superconducting state at 37-38.6 K with width of ~0.5 K. The high quality of the crystals allowed the accurate determination of magnetic, transport and optical properties as well as scanning tunnelling spectroscopy (STS) and decoration studies. Investigations of crystals with torque magnetometry show that Hc2//c is very low (24 kOe at 15 K), while Hc2//ab increases up to 140 kOe at 15 K. The upper critical field anisotropy gamma = Hc2//ab/ Hc2//c was found to be temperature dependent (decreasing from 6 at 15 K to 2.8 at 35 K). The effective anisotropy gamma_eff, as calculated from reversible torque data near Tc, is field dependent (increasing roughly linearly from 2 in zero field to 3.7 in 10 kOe). The temperature and field dependence of the anisotropy can be related to the double gap structure of MgB2 with a large two-dimensional gap and small three-dimensional gap, the latter being rapidly suppressed in a magnetic field. Torque magnetometry investigations show a pronounced peak effect, indicating an order-disorder transition of vortex matter. Decoration experiments and STS visualise a hexagonal vortex lattice. STS spectra evidence two gaps (3 meV/6 meV) with direction dependent weight. Magneto-optic investigations with H//c show a clear signature of the smaller of the two gaps, disappearing in fields higher than Hc2//c.

cond-mat.supr-con↗

arXiv2002

Comment on "Superconducting anisotropy and evidence for intrinsic pinning in single crystalline MgB2"

In a recent paper [Phys. Rev. B 66, 012501 (2002)], torque data measured on a MgB2 single crystal in fields from 10 to 60 kOe at 10 K were presented. The authors obtained the anisotropy gamma by fitting a theoretical expression to the data and concluded that the anisotropy is field independent gamma \approx 4.3. They also reported the observation of "intrinsic pinning", which they take as experimental evidence for the occurence of superconductivity in the boron layers. In this comment, we discuss the range of validity of the theoretical expression used by the authors and show that the conclusion of a field independent anisotropy does not hold. Furthermore, we present torque data measured on two crystals of MgB2, establishing the extrinsic nature of the peak in the irreversible torque observed in some crystals.

cond-mat.supr-con↗

arXiv2002

Temperature and field dependence of the anisotropy of MgB2

The anisotropy gamma of the superconducting state of high quality single-crystals of MgB2 was determined, using torque magnetometry with two different methods. The anisotropy of the upper critical field was found to be temperature dependent, decreasing from gamma = 6 at 15 K to 2.8 at 35 K. Reversible torque data near Tc reveal a field dependent anisotropy, increasing nearly linearly from gamma = 2 in zero field to 3.7 in 10 kOe. The unusual temperature dependence is a true bulk property and can be explained by non-local effects of anisotropic pairing and/or the wave vector dependence of the effective mass tensor.

cond-mat.supr-con↗

arXiv2002

Substitution effect of Zn and Cu in MgB2 on Tc and structure

The investigation of Zn substitution in MgB2 polycrystalline samples shows that about 0.1 Zn can be substituted in the structure of Mg deficient samples while it can not be substituted in stoichiometric MgB2. As a result of the isovalent Zn substitution into the Mg position of Mg deficient samples the a and c lattice constants increase by about 0.17% and 0.2% respectively. Susceptibility measurements show a slight lowering of Tc by about 0.5 K for 0.05 Zn, which decreases to 0.2 K for 0.1 Zn substitution. Investigation of the pressure derivative of Tc shows dp/dTc = -0.15 K/kbar independent of Zn content. Substitution of Cu leads to multiphase samples without any changes of lattice constants, which indicates that Cu does not enter the structure of MgB2. The Cu substitution broadens the superconducting transition considerably, while the onset remains unchanged.

cond-mat.supr-con↗

arXiv2001

Critical Currents and Order-Disorder Phase Transition in the Vortex States of YBa2Cu4O8 with Chemically Introduced Disorder

A series of YBa_{2-x}Sr_xCu_4O_8 single crystals was measured to study the influence of site disorder on the transition line Hss(T) between quasi-ordered vortex lattice and highly disordered vortex glass, as well as on the maximum critical current density within the glass phase, jcmax. When 32% of Ba is replaced by Sr, jcmax is an order of magnitude higher than in the unsubstituted compound. In contrast, the transition field Hss first drops by a factor of about five with a substitution of just 10% of Sr for Ba, and then remains approximately constant for higher Sr contents. Our results indicate that in very clean systems the order-disorder transition is affected very strongly by any crystallographic disorder, while above a certain threshold it is relatively robust with respect to additional disorder. In all substituted crystals Hss monotonically decreases with an increase of temperature.

cond-mat.supr-con↗