Rajeev Rawat — Page 2

arXiv2006

Magnetism, Upper critical field and Thermoelectric power of Magneto-Superconductor RuSr2Eu1.5Ce0.5Cu2O10

Magnetic susceptibility, M-H plot, magnetoresistance and thermoelectric power of the RuSr2Eu1.5Ce0.5Cu2O10 superconductor are measured. Values of the magnetic transition temperature Tmag, superconductivity transition temperature Tc, upper critical field Hc2, chemical potential mu, and energy width for electric conduction W(sigma) are obtained from these measurements. It has been found that Tmag = 140 K, Tc = 25 K (33 K) from susceptibility (magnetoresistance) measurements, Hc2 (0) > 32 T, mu = 8 meV, and W(sigma) = 58.5 meV. These values are compared with other ruthenate superconductors, and resulting physical information is discussed.

cond-mat.supr-con↗

arXiv2004

Induction of superconductivity in Y0.4Pr0.6Ba2-xSrxCu3O7 system with increasing Sr substitution

Samples of Y0.4Pr0.6Ba2-xSrxCu3O7 have been synthesized by a solid- state reaction route. The samples with x = 0.60 crystallize in an orthorhombic structure (with orthorhombic distortion decreasing with increasing x), while the samples with x=0.80 and 1.0 crystallize in a pseudo tetragonal structure. Resistance (R) measurements as a function of temperature (T) show that x = 0.0 sample is highly semiconducting with R2K/R300K ratio of ~ 65. This ratio decreases to only ~23 and 5 for x=0.20 and x=0.4 samples, respectively. Further, the x=0.60 sample shows onset of a broad superconducting transition temperature (Tconset) at around 20 K without achieving the TcR=0 state down to 2 K. The TcR=0 state is observed in x = 0.80 and 1.00 samples at around 5 and 14 K, respectively. Thermo-electric power (S), also exhibits TcS~0 state at around 11 K and 16 K, respectively for x = 0.8 and 1.00 samples. Thermo electric power at room temperature is positive and decreases with increasing x, indicating enhanced number of mobile holes. These results demonstrate that substitution of Sr at Ba-site systematically induces metallicity and eventually superconductivity in Y0.4Pr0.6Ba2-xSrxCu3O7 system. The results are explained on the basis of reduced Pr(4f) orbital hybridization with O(2p) in supercondu cting Cu-O2 planes, resulting in delocalization of the mobile carriers. The role of decreased Pr/Ba intermixing disorder is also considered.

cond-mat.supr-con↗

arXiv2003

Double metal-insulator transitions and MR in La(0.67)Ca(0.33)Mn(1-x)Ru(x)O(3) (x</=0.10): A qualitative understanding in light of possible magnetic phase separation

This paper is in continuation of our previous work on the structural, electrical and magnetic properties of Ru doped La(0.67)Ca(0.33)MnO(3) compounds (Ref.: L.Seetha Lakshmi et.al, J. Magn. Magn. Mater. 257, 195 (2003)). Here we report the results of magnetotransport measurements on La(0.67)Ca(0.33)Mn(1-x)Ru(x)O(3) (0<x< 0.1) compounds in the light of proposed magnetic phase separation.

cond-mat.str-el↗