Rajendra P. Dulal

Publications and source records attributed to Rajendra P. Dulal.

2 recordsLinked to original sources

arXiv2020

Molecular beam epitaxy growth of nonmagnetic Weyl semimetal LaAlGe thin film

Here, we report a detailed method of growing LaAlGe, a non-magnetic Weyl semimetal, thin film on silicon(100) substrates by molecular beam epitaxy and their structural and electrical characterizations. 50 nm thick LaAlGe films were deposited and annealed for 16 hours in situ at a temperature 793 K. As-grown high-quality films showed uniform surface topography and near ideal stoichiometry with a body-centered tetragonal crystal structure. Temperature-dependent longitudinal resistivity can be understood with dominant interband s-d electron-phonon scattering in the temperature range 5-40 K. Hall measurements confirmed the semimetallic nature of the films with electron dominated charge carrier density near 7.15*10^21 cm^-3 at 5 K.

cond-mat.mtrl-sci↗

arXiv2020

Transport characteristics of type II Weyl semimetal MoTe2 thin films grown by chemical vapor deposition

Theoretical calculations and experimental observations show MoTe2 is a type II Weyl semimetal, along with many members of transition metal dichalcogenides family. We have grown highly crystalline large-area MoTe2 thin films on Si/SiO2 substrates by chemical vapor deposition. Very uniform, continuous, and smooth films were obtained as confirmed by scanning electron microscopy and atomic force microscopy analyses. Measurements of the temperature dependence of longitudinal resistivity and current-voltage characteristics at different temperature are discussed. Unsaturated, positive quadratic magnetoresistance of the as-grown thin films has been observed from 10 K to 200 K. Hall resistivity measurements confirm the majority charge carriers are hole.

physics.app-ph↗