Probing bulk superconductivity in centrosymmetric Te-doped PtBi$_2$ single crystals
The Weyl semimetal $γ$-PtBi$_2$ has been shown to be one of the most promising novel materials, recently proposed as a topological i-wave superconductor. A crucial requirement for observing this physics is the absence of inversion symmetry in its trigonal $P31m$ crystal structure. Centrosymmetry has been reported to be readily restored in the $P\overline{3}m1$ structure upon electron doping, partially substituting Bi with as little as 2% Te. In this work, we synthesized Te-doped PtBi$_{2-x}$Te$_{x}$ samples and thoroughly investigated the bulk superconductivity of selected single crystals with nominal composition PtBi$_{1.96}$Te$_{0.04}$, exhibiting the highest superconducting volume fraction of $\sim100$%. Single crystal XRD measurements confirm the centrosymmetric $P\overline{3}m1$ structure in our samples, whereas bulk superconductivity with a critical temperature of $T_\mathrm{c} \approx 2.4\,$K was observed in magnetization and specific heat measurements. The upper critical fields for two different orientations were determined as $H^{\parallel}_{\mathrm{c2}}(0)\approx 6.3\,$kOe for in-plane and $H^{\perp}_{\mathrm{c2}}(0)\approx 4.7\,$kOe for out-of-plane magnetic fields. Robust superconductivity was also found in resistance and point contact measurements, where the latter showed a slight enhancement of the critical temperature up to $T_\mathrm{c} \sim 3\,$K. Finally, ARPES measurements corroborate the centrosymmetric structure of our samples, showing a single surface termination and the absence of Fermi arcs.