arXiv2010

Upper critical fields and critical current density of BaFe2(As0.68P0.32)2 single crystal

The transport properties, upper critical fields, superconducting anisotropy, and critical current density in an iso-valent phosphorus-doped BaFe2As2 single crystal close to optimum doping are investigated in this report. Temperature dependent resistivity and susceptibility show a superconducting transition temperature, Tc, just below 31 K both with sharp transitions. The upper critical field parallel to the ab-plane, Hc2^ab, is above 77 Tesla while that along the c-axis direction, Hc2^c, is just above 36 Tesla, yielding a low superconducting anisotropy ratio ~ 2. The estimated inter-plane coherence length based on the Ginzburg-Landau (G-L) theory indicates BaFe2(As0.68P0.32)2 is still above the point for a dimensional crossover inferring the superconducting layers are not weakly-coupled in this system. The critical current density at 5 K obtained from magnetization loops measurement show a modest Jc as high as 10^5 A/cm2.

cond-mat.supr-con↗

arXiv2008

Superconductivity in Yttrium Iron Oxyarsenide System

Iron-based oxypnictides substituted with yttrium have been prepared via a conventional solid state reaction. The product after first 50 hours of reaction showed diamagnetic-like transition at around 10 K but was not superconducting, while additional 72 hours of high temperature heat treatment was required to yield superconducting sample which was doped with fluoride. Temperature dependence of the susceptibility shows both screening and Meissner effect at around 10 K, while resistance as a function of temperature displayed a drop at around the same temperature.

cond-mat.supr-con↗

arXiv2008

Superconductivity and Magnetism in REFeAsO1-xFx (RE=Rare Earth Elements)

Fluoride-doped iron-based oxypnictides containing rare-earth gadolinium (GdFeAsO0.8F0.2) and co-doping with yttrium (Gd0.8Y0.2FeAsO0.8F0.2) have been prepared via conventional solid state reaction at ambient pressure. The non-yttrium substituted oxypnictide show superconducting transition as high as 43.9 K from temperature dependent resistance measurements with the Meissner effect observed at a lower temperature of 40.8 K from temperature dependent magnetization measurements. By replacing a small amount of gadolinium with yttrium Tc was observed to be lowered by 10 K which might be caused by a change in the electronic or magnetic structures since the crystal structure was not altered.

cond-mat.supr-con↗