Nanoindentation stress-strain for Fracture Analysis and computational modeling for hardness and modulus
Stress-strain plots based on nanoindentation load-depth curves reflected cracking phenomenon. A transition from ductile to brittle fracture was observed on increasing the depth or load of indenter penetration. A new approach with shape factors in the fracture studies based on radial crack branching and micro-cracking was done. Hardness and modulus plots were fitted with polynomials. The coefficients were varied to obtain different hardness and modulus responses.
cond-mat.mtrl-sci↗