arXiv2012

Evolution of superconductivity in LaO1-xFxBiS2 prepared by high pressure technique

Novel BiS2-based superconductors LaO1-xFxBiS2 prepared by the high pressure synthesis technique were systematically studied. It was found that the high pressure annealing strongly the lattice as compared to the LaO1-xFxBiS2 samples prepared by conventional solid state reaction at ambient pressure. Bulk superconductivity was observed within a wide F-concentration range of x = 0.2 ~ 0.7. On the basis of those results, we have established a phase diagram of LaO1-xFxBiS2.

cond-mat.supr-con↗

arXiv2012

Fermiological Interpretation of Superconductivity/Non-superconductivity of FeTe_{1-x}Se_{x} Thin Crystal Determined by Quantum Oscillation Measurement

We have successfully observed quantum oscillation (QO) for FeTe_{1-x}Se_{x}. QO measurements were performed using non-superconducting and superconducting thin crystals of FeTe_{0.65}Se_{0.35} fabricated by the scotch-tape method. We show that the Fermi surfaces (FS) of the non-superconducting crystal are in good agreement with the rigid band shift model based on electron doping by excess Fe while that of the superconducting crystal is in good agreement with the calculated FS with no shift. From the FS comparison of both crystals, we demonstrate the change of the cross-sectional area of the FS, suggesting that the suppression of the FS nesting with the vector Q_{s} = (π, π) due to excess Fe results in the disappearance of the superconductivity.

cond-mat.supr-con↗

arXiv2012

Phase diagram and oxygen annealing effect of FeTe1-xSex iron-based superconductor

Phase diagrams of as-grown and O2-annealed FeTe1-xSex determined from magnetic susceptibility measurement were obtained. For as-grown samples, the antiferromagnetic order was fully suppressed in the range region x \geq 0.15, and weak superconductivity appeared when x \geq 0.1. Beginning at x = 0.5, weak superconductivity was found to evolve into bulk superconductivity. Interestingly, for O2-annealed samples, complete suppression of magnetic order and the occurrence of bulk superconductivity were observed when x \geq 0.1. We found that O2-annealing induces bulk superconductivity for FeTe1-xSex. Oxygen probably plays a key role in the suppression of the magnetic order and the appearance of bulk superconductivity.

cond-mat.supr-con↗

arXiv2012

Evidence of Inhomogeneous Superconductivity in FeTe$_{1-x}$Se$_x$ Thin Film Using Scotch-Tape Method

We have fabricated thin films of FeTe$_{1-x}$Se$_x$ using a scotch-tape method. The superconductivities of the thin films are different from each other although these films were fabricated from the same bulk sample. The result clearly presents the inhomogeneous superconductivity in FeTe$_{1-x}$Se$_x$. The difference comes from inhomogeneity due to the excess Fe concentration. The resistivity of a thin film with low excess Fe shows good superconductivity with the sharp superconducting-transition width and more isotropic superconductivity.

cond-mat.supr-con↗

arXiv2012

Clarification as to why alcoholic beverages have the ability to induce superconductivity in Fe_{1+d}Te_{1-x}S_x

To elucidate the mechanism as to why alcoholic beverages can induce superconductivity in Fe_{1+d}Te_{1-x}S_x samples, we performed component analysis and found that weak acid such as organic acid has the ability to induce superconductivity. Inductively-coupled plasma spectroscopy was performed on weak acid solutions post annealing. We found that the mechanism of inducement of superconductivity in Fe_{1+d}Te_{1-x}S_x is the deintercalation of excess Fe from the interlayer sites.

cond-mat.supr-con↗