arXiv2021

Structural behaviour of BiFeO3/SrRuO3 superlattices: an X-ray diffraction and Raman spectroscopy investigation

Epitaxial BiFeO3/SrRuO3 superlattices have been grown by pulsed laser deposition on a (001) oriented LaAlO3 substrate and probed by X-ray diffraction and Raman spectroscopy. To investigate the structural competition between rhombohedral BiFeO3 and orthorhombic SrRuO3 the total thickness of all SLs was kept constant and the bilayer thickness (period) Λ was varied. The interlayer strain effects are therefore tuned from large strain effects (short Λ period) to quasi-relaxed structure (large Λ). A complementary investigation using X-ray diffraction and phonon dynamics hints to change from a rhombohedral to a tetragonal structure in the superlattices with the increase of the interlayer strain effect.

cond-mat.mtrl-sci↗

arXiv2021

Impedance spectroscopy and conduction mechanism of a BiFe$_{0.95}$Mn$_{0.05}$O$_3$ thin film

Dielectric response and conduction mechanism were investigated for a multiferroic BiFe$_{0.95}$Mn$_{0.05}$O$_3$ epitaxial thin film. A contribution from a thermally activated interface (0.37 eV) and the bulk of the film on the dielectric response were observed through the comparison between experimental results and equivalent circuit model. The low frequency interface relaxation signatures strongly suggest a Maxwell-Wagner space charge origin. The alternative current conductivity deduced from the model follows a power law frequency dependence suggesting a polaronic hopping mechanism while the low frequency limit is in perfect agreement with the direct current conduction mechanism. The current-voltage characteristics were indeed correlated with Schottky-Simmons interface limited transport with activation energy of 0.36 eV, close to the one extracted from the impedance analysis. Such analysis of the electrostatic landscape and dielectric behaviour may help to further understanding the anomalous photo-induced properties in the BiFeO$_3$ system.

cond-mat.mtrl-sci↗

arXiv2020

Tailoring the photovoltaic effect in (111) oriented BiFeO3/LaFeO3 superlattices

Ferroelectric and photovoltaic properties of BiFeO3/LaFeO3 superlattices grown by pulsed laser deposition have been investigated being the bilayer thickness). For a high concentration of BiFeO3 a ferroelectric state is observed simultaneously with a switchable photovoltaic response. In contrast for certain concentration of LaFeO3 a non-switchable photovoltaic effect is evidenced. Such modulation of the PV response in the superlattices is attributed to the ferroelectric to paraelectric phase transition which is controlled with the increase of x. Remarkably, concomitant to this change of PV mechanism, a change of the conduction mechanism also seems to take place from a bulk-limited to an interface-limited transport as x increases.

cond-mat.mtrl-sci↗

arXiv2019

Conduction mechanism and switchable photovoltaic effect in (111) oriented BiFe$_{0.95}$Mn$_{0.05}$O$_{3}$ thin film

Epitaxial 200nm BiFe$_{0.95}$Mn$_{0.05}$O$_{3}$ (BFO) film was grown by pulsed laser deposition on (111) oriented SrTiO3 substrate buffered with a 50nm thick SrRuO$_{3}$ electrode. The BFO thin film shows a rhombohedral structure and a large remnant polarization of Pr = 104 $μ$C/cm$^{2}$. By comparing I(V) characteristics with different conduction models we reveal the presence of both bulk limited Poole-Frenkel and Schottky interface mechanisms and each one dominates in a specific range of temperature. At room temperature and under 10mW laser illumination, the as grown BFO film presents short-circuit current density (Jsc) and open circuit voltage (Voc) of 2.25mA/cm$^{2}$ and -0.55V respectively. This PV effect can be switched by applying positive voltage pulses higher than the coercive field. For low temperatures a large Voc value of about -4.5V (-225kV/cm) is observed which suggests a bulk non-centrosymmetric origin of the PV response.

cond-mat.mtrl-sci↗

arXiv2019

Structural investigation of (111) oriented (BiFeO3)(1-x)Λ/(LaFeO3)xΛ superlattices by X-ray diffraction and Raman spectroscopy

(BiFeO3)(1-x)Λ/(LaFeO3)xΛ superlattices (SLs) with varying x have been grown by pulsed laser deposition on (111) oriented SrTiO3 substrates. In order to obtain good epitaxy and flat samples a conducting SrRuO3 buffer has been deposited prior to the superlattices to screen the polar mismatch for such (111) SrTiO3 orientation. X-ray diffraction reciprocal space mapping on different family of planes were collected and evidenced a room temperature structural change at x=0.5 from a rhombohedral/monoclinic structure for rich BiFeO3 to an orthorhombic symmetry for rich LaFeO3. This symmetry change has been confirmed by Raman spectroscopy and demonstrates the different phase stability compared to similar SLs grown on (100) SrTiO3. The strongly anisotropic strain and oxygen octahedral rotation/tilt system compatibility at the interfaces probably explain the orientation dependence of the phase stability in such superlattices.

cond-mat.mtrl-sci↗