arXiv2021

Dimethylammonium additives alter both vertical and lateral composition in halide perovskite semiconductors

Adding a large A-site cation, such as dimethylammonium (DMA), to the perovskite growth solution has been shown to improve performance and long-term operational stability of halide perovskite solar cells. To better understand the origins of these improvements, we explore the changes in film structure, composition, and optical properties of a formamidinium (FA), Cs, Pb, mixed halide perovskite following addition of DMA to the perovskite growth solution in the ratio DMA0.1FA0.6Cs0.3Pb(I0.8Br0.2)3. Using time-of-flight secondary-ion mass spectrometry (TOF-SIMS) we show that DMA is indeed incorporated into the perovskite, with a higher DMA concentration at the surface. Using a combination of PL microscopy and photo-induced force microscopy-based (PiFM) nanoinfrared (nanoIR), we demonstrate that incorporating DMA into the film leads to increased local heterogeneity in the local bandgap, and clustering of the local formamidinium (CH5N2+) composition. In addition, using nano-X-ray diffraction, we demonstrate that DMA incorporation also alters the local structural composition by changing the local d-spacing distribution and grain size. Our results suggest that compositional variations in the organic cations at the A-site drive the structural heterogeneity observed in case of DMA incorporated films. Our results also suggest that while current-DMA-additive based approaches do have benefits to operational stability and device performance, process optimization to achieve local compositional and structural homogeneity could further boost both of these gains in performance, bringing further gains to solar cells using DMA additives.

physics.app-ph↗

arXiv2020

Approaching the limits of optoelectronic performance in mixed cation mixed halide perovskites by controlling surface recombination

We demonstrate the critical role of surface recombination in mixed-cation, mixed-halide perovskite, FA0.83Cs0.17Pb(I0.85Br0.15)3. By passivating non-radiative defects with the polymerizable Lewis base (3-aminopropyl)trimethoxysilane (APTMS) we transform these thin films. We demonstrate average minority carrier lifetimes > 4 μs, nearly single exponential monomolecular PL decays, and concomitantly high external photoluminescence quantum efficiencies (>20%, corresponding to ~97% of the maximum theoretical quasi-Fermi-level splitting) at low excitation fluence. We confirm both the composition and valence band edge position of the FA0.83Cs0.17Pb(I0.85Br0.15)3 perovskite using multi-institution, cross-validated, XPS and UPS measurements. We extend the APTMS surface passivation to higher bandgap double cation (FA,Cs) compositions (1.7 eV, 1.75 eV and 1.8 eV) as well as the widely used triple cation (FA,MA,Cs) composition and observe significant PL and PL lifetime improvements after surface passivation. Finally, we demonstrate that the average surface recombination velocity (SRV) decreases from ~1000 cm/s to ~10 cm/s post APTMS passivation for FA0.83Cs0.17Pb(I0.85Br0.15)3. Our results demonstrate that surface-mediated recombination is the primary non-radiative loss pathway in MA-free mixed-cation mixed-halide films with a range of different bandgaps, which is a problem observed for a wide range of perovskite active layers and reactive electrical contacts. This study indicates that surface passivation and contact engineering will enable near-theoretical device efficiencies with these materials.

physics.app-ph↗

arXiv2019

Local Crystal Misorientation Influences Non-Radiative Recombination

We use ultrasensitive electron backscatter diffraction (EBSD) to map the local crystal orientations, grains, and grain boundaries in CH3NH3PbI3 (MAPI) perovskite thin films. Although the true grain structure is broadly consistent with the morphology visible in scanning electron microscopy (SEM), the inverse pole figure maps taken with EBSD reveal grain structure and internal misorientation that is otherwise hidden. Local crystal misorientation is consistent with the presence of local strain which varies from one grain to the next. We acquire co-aligned confocal optical photoluminescence (PL) microscopy images on the same MAPI samples used for EBSD. We correlate optical and EBSD data, showing that PL is anticorrelated with the local grain orientation spread, suggesting that grains with higher degrees of crystalline orientational heterogeneity (local strain) exhibit more non-radiative recombination. We find that larger grains tend to have larger grain orientation spread, consistent with higher degrees of strain and non-radiative recombination.

cond-mat.mtrl-sci↗