arXiv2016

Superconductivity in CeOBiS2 with cerium valence fluctuation

Resistivities of single-crystalline as well as poly-crystalline samples of CeOBiS2 without fluorine doping were measured at temperatures down to 0.13 K, and were compared with those of poly-crystalline LaOBiS2 and PrOBiS2. Both poly-crystalline and single-crystalline CeOBiS2 exhibited zero resistivity below 1.2 K while poly-crystalline LaOBiS2 and PrOBiS2 did not show zero resistivity down to 0.13 K. Superconducting transition temperature of CeOBiS2 was reduced by increasing the applied current density. The superconductivity of CeOBiS2 without chemical doping is likely triggered by the carriers induced by the valence fluctuation between Ce3+ and Ce4+.

cond-mat.supr-con↗

arXiv2015

C-axis electrical resistivity of PrO$_{1-a}$F$_a$BiS$_2$ single crystals

The high anisotropy in RO1-aFaBiS2 (R denotes a rare-earth element) superconductors demonstrates their potential use as intrinsic Josephson junctions, considering the weak coupling among BiS2-PrO(F)-BiS2 (superconducting-normal-superconducting) layers along the c-axis. We grew PrO1-aFaBiS2 single crystals using CsCl/KCl flux. The superconducting anisotropies of the grown single crystals were estimated to be approximately 40-50 from the effective mass model. The c-axis transport properties were characterized using single-crystal s-shaped intrinsic Josephson junctions with a focused ion beam. Along the c-axis, the crystals showed zero resistivity at 2.7 K and a critical current density of 1.33*10^3 A/cm2 at 2.0 K. The current-voltage curve along the c-axis displayed hysteresis. The c-axis transport measurements under a magnetic field parallel to the ab-plane revealed a "lock-in" state due to the Josephson vortex flow, indicating that BiS2 superconductors are promising candidates for intrinsic Josephson junctions.

cond-mat.supr-con↗

arXiv2014

Growth and superconducting anisotropies of F-substituted LaOBiSe2 single crystals

F-substituted LaOBiSe2 single crystals were grown using CsCl flux. The obtained single crystals showed a plate-like shape with a size of about 1.0 mm square. The c-axis lattice constant of the grown crystals was determined to be 14.114(3) Å. The superconducting critical temperature of the single crystal was approximately 3.5 K. The superconducting anisotropies were determined to be 49 and 24 using the upper critical field and the effective mass model, respectively.

cond-mat.supr-con↗

arXiv2014

Crystal structures of LaO1-xFxBiS2 (x~0.23, 0.46): effect of F doping on distortion of Bi-S plane

The crystal structures of superconducting LaO1-xFxBiS2 (x ~ 0.23, 0.46) were determined by single-crystal X-ray diffraction analysis. Their space group was P4/nmm. Distortion of the Bi-S plane changed when the F content was increased from 0.23 to 0.46, and a nearly flat Bi-S plane was formed at x ~ 0.46. Computational calculations supported this effect of F doping on distortion of Bi-S plane. LaO1-xFxBiS2 with higher F contents were computationally predicted to be thermodynamically more unstable under ambient pressure. We discussed the bonding, conductivities, and synthetic routes of LaO1-xFxBiS2.

cond-mat.supr-con↗

arXiv2013

Growth and superconducting properties of F-substituted ROBiS2 (R = La, Ce, Nd) single crystals

F-substituted ROBiS2 (R = La, Ce, Nd) superconducting single crystals with different F concentration were grown successfully using CsCl/KCl flux. All the obtained single crystals had a plate-like shape with a well-developed ab-plane of 1-2 mm in size. The flux components of Cs, K, and Cl were not detected in the obtained single crystals by electron probe microanalysis. The grown single crystals of F-substituted LaOBiS2 and CeOBiS2 showed superconducting at about 3 K while the Tc of the F-substituted NdOBiS2 exhibited approximately 5 K. The superconducting anisotropy of the single crystals of F-substituted LaOBiS2 and NdOBiS2 was estimated to be 30-45 according to the effective mass model whereas those values were 13-21 for the F-substituted CeOBiS2 single crystals. The F-substituted CeOBiS2 single crystals exhibited magnetic order at about 7 K that apparently coexisted with superconductivity below around 3 K.

cond-mat.supr-con↗

arXiv2013

Structural Analysis and Superconducting Properties of F-Substituted NdOBiS2 Single Crystals

F-substituted NdOBiS2 superconducting single crystals were grown using CsCl/KCl flux. This is the first example of the single-crystal growth of a BiS2-based superconductor. The obtained single crystals had a plate-like shape with a size of 1-2 mm and a well-developed ab-plane. The crystal structure of the grown crystals was determined by single-crystal X-ray diffraction analysis to be the tetragonal space group P4/nmm (#129) with a = 3.996(3) A and c = 13.464(6) A. The chemical formula of the grown crystals was approximately Nd0.98(0.06)O0.7(0.1)F0.3(0.1)Bi0.98(0.04)S2, and Cs, K, and Cl were not detected in the grown crystals by electron probe microanalysis. The grown crystals had a critical temperature of approximately 5 K. The superconducting anisotropy of the single crystals was estimated to be about 30 from the effective mass model and the upper critical field.

cond-mat.supr-con↗

arXiv2012

Inducement of superconductivity in Fe(Te,S) by sulfuric acid treatment

Superconductivity of Fe0.95Te0.85S0.15 was induced and enhanced by immersing the as-grown (non-superconducting) sample into sulfuric acid. Dissolved Fe was detected in the sulfuric acid treatment, indicating that excess Fe was removed from the Fe0.95Te0.85S0.15 sample.

cond-mat.supr-con↗

arXiv2010

Growth and Anisotropic Properties of RBa_2Cu_3O_x Single-Crystal Whiskers

Single-crystal whiskers of RBa2Cu3Ox (R-123, R = Sm, Eu, Gd, Dy, Ho, Er, Tm, Yb, and Y) were successfully grown from Sb- or Te-doped precursors with a nominal composition of R1.5Ba2.75-3.00Cu3M0.5Ox (M: Sb,Te). The whiskers were grown parallel to the ab-plane with the following typical dimensions: 2-8 mm in length, 20-80 \mum in width, and 10-30 \mum in thickness. In the case of rare-earth ions (R3+) with a small ionic radius (Dy, Ho, Er, Tm, Yb, and Y), R-123 whiskers were grown from Te-doped precursors. The growths of Y-123 and Ho-123 whiskers were confirmed using both Te-doped and Sb-doped precursors. On the other hand, for rare-earth ions (R3+) with a large ionic radius (Sm, Eu, and Gd), R-123 whiskers were grown only from Sb-doped precursors. Sb and Te were not detected in the grown whiskers by electron probe microanalysis. The anisotropies of R-123 single-crystal whiskers in the flux liquid state were estimated to be 6.0-33 from the angular dependence of their resistivities under various magnetic fields. The anisotropy increased with decreasing superconducting transition temperature.

cond-mat.supr-con↗

arXiv2004

Dissipationless Anomalous Hall Current in the Ferromagnetic Spinel CuCr$_2$Se$_{4-x}$Br$_x$

In a ferromagnet, an applied electric field $\bf E$ invariably produces an anomalous Hall current ${\bf J}_H$ that flows perpendicular to the plane defined by $\bf E$ and $\bf M$ (the magnetization). For decades, the question whether ${\bf J}_H$ is dissipationless (independent of the scattering rate), has been keenly debated without experimental resolution. In the ferromagnetic spinel CuCr$_2$Se$_{4-x}$Br$_x$, the resistivity $ρ$ (at low temperature) may be increased 1000 fold by varying $x$(Br), without degrading the $\bf M$. We show that ${\bf J}_H/E$ (normalized per carrier, at 5 K) remains unchanged throughout. In addition to resolving the controversy experimentally, our finding has strong bearing on the generation and study of spin-Hall currents in bulk samples.

cond-mat.str-el↗

arXiv2004

Charge-ordering, commensurability and metallicity in the phase diagram of layered Na(x)CoO(2)

The phase diagram of non-hydrated Na(x)CoO(2) has been determined by changing the Na content x using a series of chemical reactions. As x increases from 0.3, the ground state goes from a paramagnetic metal to a charge-ordered insulator (at x=1/2) to a `Curie-Weiss metal' (around 0.70), and finally to a weak-moment magnetically ordered state (x>0.75). The unusual properties of the state at 1/2 (including particle-hole symmetry at low T and enhanced thermal conductivity) are described. The strong coupling between the Na ions and the holes is emphasized.

cond-mat.supr-con↗