Irradiation-induced amplification of electric fields at oxide interfaces as revealed by correlative DPC-STEM and DFT

Heterointerfaces are ubiquitous in modern devices, found in technologies ranging from microelectronics to structural components for energy applications. Many of these emerging technologies are found in applications such as satellites, batteries, and next generation nuclear reactors, that are subject to harsh environments. In some scenarios, multiple extreme conditions, such as irradiation and corrosion, act on the material simultaneously. Extending the lifetime of these technologies is dependent on a detailed understanding of how their component materials platforms and interfaces respond in extreme environments, where irradiation and corrosion may couple in unique ways, distinct from corrosion under ambient conditions. Oxides, which form readily over metal underlayers, can act as protective coatings; enhancing the robustness of oxide overlayers to protect underlying metal alloys is a potential avenue towards corrosion mitigation. Here we study the impact of irradiation-induced non-equilibrium defects on charge segregation and electric fields at and near multi-phase oxide heterointerfaces. We perform a detailed study of irradiated Fe2O3-Cr2O3 thin film heterostructures using first-principles DFT electronic structure modeling paired with 4D-STEM DPC and EELS techniques to measure nanoscale changes in electric fields. Our results show clear evidence that irradiation drives substantial modulation of interfacial electric fields that can be tailored by controlling the atomistic chemical structure of the oxide interface. We show that irradiation can selectively induce built-in electric fields, thereby altering their direction; this suggests a pathway to engineering protective oxide heterostructure overlayers that can electrically control the spatial distribution of defects, with significant implications for the design of corrosion-resistant materials for extreme environments.

cond-mat.mtrl-sci

Heat treatment - microstructure - hardness relationships of new nickel-rich nickel-titanium-hafnium alloys developed for tribological applications

The effects of various heat treatments on the microstructure and hardness of new Ni56Ti41Hf3 and Ni56Ti36Hf8 (atomic %) alloys were studied to evaluate the suitability of these materials for tribological applications. A solid-solution strengthening effect due to Hf atoms was observed for the solution annealed (SA) Ni56Ti36Hf8 alloy (716 HV), resulting in a comparable hardness to the Ni56Ti41Hf3 alloy containing 54 vol.% of Ni4Ti3 precipitates (707 HV). In the Ni56Ti41Hf3 alloy, the maximum hardness (752 HV), achieved after aging at 300C for 12 h, was attributed to dense, semi-coherent precipitation of the Ni4Ti3 phase. Unlike the lenticular morphology usually observed within binary NiTi alloys, a blocky Ni4Ti3 morphology formed within Ni56Ti36Hf3 due to a smaller lattice mismatch in the direction normal to the habit plane at the precipitate/matrix interface. The maximum hardness for Ni56Ti36Hf8 (769 HV) was obtained after applying an intermediate aging step (300C for 12 h) followed by normal aging (550C for 4 h). This two-step aging treatment induces dense nanoscale precipitation of two interspersed precipitate phases, namely H-phase and a new cubic Ni-rich precipitate phase, resulting in the highest hardness exhibited yet by this family alloys. The composition of cubic Ni-rich precipitates was measured using atom probe tomography to be approximately Ni61.5Ti31Hf7.5, while HAADF-STEM revealed a 54 atom motif cubic structure (a= 8.87 Angstroms), and electron diffraction showed that the structure belongs to the pm-3m (No. 221) space group.

cond-mat.mtrl-sci

Rolling contact fatigue deformation mechanisms of nickel-rich nickel-titanium-hafnium alloys

The tribological performance and underlying deformation behavior of Ni55Ti45, Ni54Ti45Hf1 and Ni56Ti36Hf8 alloys were studied using rolling contact fatigue (RCF) testing and transmission electron microscopy (TEM). TEM results of the as-machined RCF rods, prepared using focus ion beam, revealed some damage very close to the surface. TEM results after initial RCF cycling showed that additional damage was mainly confined to deformation bands that propagated several microns into the sample. These bands formed via localized dislocation slip, possibly on multiple slip systems, within the B2 matrix and/or within transformed B19 prime martensite phase under repeated applied contact stress. Further cycling of Ni55Ti45 and Ni54Ti45Hf1 led to shearing and dissolution of the strengthening precipitates within the deformation bands, followed by formation of nanocrystalline grains and finally amorphization of the remaining matrix material within the bands. The Ni56Ti36Hf8 alloy exhibited a notable increase in RCF performance and a smaller damage zone (1.5 microns) compared to the Ni55Ti45 and Ni54Ti45Hf1 alloys (over 6 microns). This was attributed to the low fraction of B2 matrix phase (less than or equal to 13 %) in the Ni56Ti36Hf8 alloy, leading to formation of narrow deformation bands (less than 11 nm) that were incapable of dissolving the much larger precipitates. Instead, the deformation bands were restricted to narrow channels between the dense cubic NiTiHf and H-phase precipitates. In contrast, broad deformation bands accompanied by shearing and eventual dissolution of the Ni4Ti3 precipitates were observed in the Ni55Ti45 and Ni54Ti45Hf1 alloys due to the high area fractions of B2 matrix phase (~49 %).

cond-mat.mtrl-sci