Pressure-induced magnetic collapse and metallization of $\mathrm{TlF}{\mathrm{e}}_{1.6}\mathrm{S}{\mathrm{e}}_{2}$

The crystal structure, magnetic ordering, and electrical resistivity of TlFe1.6Se2 were studied at high pressures. Below ~7 GPa, TlFe1.6Se2 is an antiferromagnetically ordered semiconductor with a ThCr2Si2-type structure. The insulator-to-metal transformation observed at a pressure of ~ 7 GPa is accompanied by a loss of magnetic ordering and an isostructural phase transition. In the pressure range ~ 7.5 - 11 GPa a remarkable downturn in resistivity, which resembles a superconducting transition, is observed below 15 K. We discuss this feature as the possible onset of superconductivity originating from a phase separation in a small fraction of the sample in the vicinity of the magnetic transition.

cond-mat.supr-con↗

arXiv2016

Pressure effect on superconductivity in FeSe0.5Te0.5

Due to the simple layered structure, isostructural FeSe and FeSe0.5Te0.5 are clue compounds for understanding the principal mechanisms of superconductivity in the family of Fe-based superconductors. High-pressure magnetic, structural and Mössbauer studies have been performed on single-crystalline samples of superconducting FeSe0.5Te0.5 with Tc = 13.5 K. Susceptibility data have revealed a strong increase of Tc up to 19.5 K for pressures up to 1.3 GPa, followed by a plateau in the Tc(p) dependence up to 5.0 GPa. Further pressure increase leads to a disappearance of the superconducting state around 7.0 GPa. X-ray diffraction and Mössbauer studies explain this fact by a tetragonal-to-hexagonal structural phase transition. Mössbauer parameters of the non-superconducting high-pressure phase indicate less covalency of Fe-Se bonds. Based on structural and susceptibility data we conclude about a common character of Tc(p) diagrams for both FeSe and FeSe0.5Te0.5 superconductors.

cond-mat.supr-con↗