In-situ growth of superconducting NdFeAs(O,F) thin films by Molecular Beam Epitaxy

The recently discovered high temperature superconductor F-doped LaFeAsO and related compounds represent a new class of superconductors with the highest transition temperature (Tc) apart from the cuprates. The studies ongoing worldwide are revealing that these Fe-based superconductors are forming a unique class of materials that are interesting from the viewpoint of applications. To exploit the high potential of the Fe-based superconductors for device applications, it is indispensable to establish a process that enables the growth of high quality thin films. Efforts of thin film preparation started soon after the discovery of Fe-based superconductors, but none of the earlier attempts had succeeded in an in-situ growth of a superconducting film of LnFeAs(O,F) (Ln=lanthanide), which exhibits the highest Tc to date among the Fe-based superconductors. Here, we report on the successful growth of NdFeAs(O,F) thin films on GaAs substrates, which showed well-defined superconducting transitions up to 48 K without the need of an ex-situ heat treatment.

cond-mat.supr-con↗

arXiv2009

Epitaxial Growth of NdFeAsO Thin Films by Molecular Beam Epitaxy

Epitaxial films of NdFeAsO were grown on GaAs substrates by molecular beam epitaxy (MBE). All elements including oxygen were supplied from solid sources using Knudsen cells. The x-ray diffraction pattern of the film prepared with the optimum growth condition showed no indication of impurity phases. Only (00l) peaks were observed, indicating that NdFeAsO was grown with the c-axis perpendicular to the substrate. The window of optimum growth condition was very narrow, but the NdFeAsO phase was grown with a very good reproducibility. Despite the absence of any appreciable secondary phase, the resistivity showed an increase with decreasing temperature.

cond-mat.supr-con↗