arXiv2010

Systematic Comparison of Eight Substrates in the Growth of FeSe$_{0.5}$Te$_{0.5}$ Superconducting Thin Films

We have investigated the crystal structures and superconducting properties of thin films of FeSe$_{0.5}$Te$_{0.5}$ grown on eight different substrates. Superconductivity is not correlated with the lattice mismatch; rather it is correlated with the degree of in-plane orientation and with the lattice parameter ratio $c/a$. The best superconducting properties were observed in films on MgO and LaAlO$_3$ ($T_\mathrm{c}^\mathrm{zero}$ of 9.5 K). TEM observation showed that the presence or absence of an amorphous-like layer at the substrate surface plays a key role in determining the structural and superconducting properties of the grown films.

cond-mat.supr-con↗

arXiv2009

Superconductivity of FeSe0.5Te0.5 Thin Films Grown by Pulsed Laser Deposition

FeSe0.5Te0.5 thin films with PbO-type structure are successfully grown on MgO(100) and LaSrAlO4(001) substrates from FeSe0.5Te0.5 or FeSe0.5Te0.75 polycrystalline targets by pulsed-laser deposition. The film deposited on the MgO substrate (film thickness ~ 55 nm) shows superconductivity at 10.6 K (onset) and 9.2 K (zero resistivity). On the other hand, the film deposited on the LaSrAlO4 substrate (film thickness ~ 250 nm) exhibits superconductivity at 5.4 K (onset) and 2.7 K (zero resistivity). This suggests the strong influence of substrate materials and/or the c-axis length to superconducting properties of FeSe0.5Te0.5 thin films.

cond-mat.supr-con↗

arXiv2009

Superconductivity of FeSe$_{1-x}$Te$_{x}$ Thin Films Grown by Pulsed Laser Deposition

FeSe$_{1-x}$Te$_{x}$ thin films with PbO-type structure are successfully grown on MgO(100) and LaSrAlO$_{4}$(001) substrates from FeSe$_{1-x}$Te$_{x+d}$ polycrystalline targets by pulsed-laser deposition. The film deposited on the MgO substrate (film thickness $\sim$ 63 nm) shows superconductivity at 6.7 K (onset) and 5.5 K (zero resistivity). On the other hand, the film deposited on the LaSrAlO$_{4}$ substrate (film thickness $\sim$ 52 nm) exhibits only the onset of superconducting transition at 2.6 K, but does not show zero resistivity. This indicates the strong influence of epitaxial strain to superconducting properties of FeSe$_{1-x}$Te$_{x}$ thin films.

cond-mat.supr-con↗