Correlative Imaging of Individual CsPbBr3 Nanocrystals: Role of Isolated Grains in Photoluminescence of Perovskite Polycrystalline Thin Films

We report on the optical properties of CsPbBr3 polycrystalline thin film on a single grain level. A sample comprised of isolated nanocrystals (NCs) mimicking the properties of the polycrystalline thin film grains that can be individually probed by photoluminescence spectroscopy was prepared. These NCs were analyzed using correlative microscopy allowing the examination of structural, chemical, and optical properties from identical sites. Our results show that the stoichiometry of the CsPbBr3 NCs is uniform and independent of the NCs' morphology. The photoluminescence (PL) peak emission wavelength is slightly dependent on the dimensions of NCs, with the blue shift up to 9 nm for the smallest analyzed NCs. The magnitude of the blueshift is smaller than the emission linewidth, thus detectable only by high-resolution PL mapping. By comparing the emission wavelengths obtained from the experiment and a rigorous effective mass model we can fully attribute the observed variations to the size-dependent quantum confinement effect.

physics.chem-ph↗

arXiv2022

Low temperature 2D GaN growth on Si (111) 7x7 assisted by hypethermal nitrogen ions

As the characteristic dimensions of modern top-down devices are getting smaller, such devices reach their operational limits given by quantum mechanics. Thus, two-dimensional (2D) structures appear as one of the best solutions to meet the ultimate challenges of modern optoelectronic and spintronic applications. The representative of III-V semiconductors, gallium nitride (GaN), is a great candidate for UV and high-power applications at a nanoscale level. We propose a new way of fabrication of 2D GaN on the Si(111) 7x7 surface using post-nitridation of Ga droplets by hyperthermal (E < 50 eV) nitrogen ions at low substrate temperatures (T < 220°C). Both deposition of Ga droplets and their post-nitridation is carried out using a special atom-ion beam source developed in our group. This low-temperature droplet epitaxy (LTDE) approach provides well-defined ultra-high vacuum growth conditions during the whole fabrication process resulting in high purity GaN nanostructures. A sharp interface between the GaN nanostructures and the silicon substrate together with a correct elemental composition of nanostructures was confirmed by TEM. In addition, SEM, X-ray photoelectron spectroscopy (XPS), AFM and Auger microanalysis showed unique characteristics of the fabricated GaN nanostructures.

cond-mat.mtrl-sci↗