Effects of irradiation by protons, neutrons, and gamma particles on electrical properties of 4H-SiC diodes and LGAD sensors
4H-SiC is a wide-bandgap semiconductor with high displacement threshold energy, large critical electric field, and low intrinsic carrier concentration, making it attractive for radiation-hard detector applications. In this work, we investigate the electrical characteristics of 4H-SiC P$^{+}$-in-N (PN) diodes and Low-Gain Avalanche Detectors (LGADs) fabricated by onsemi before and after irradiation by 24 GeV/c protons, reactor neutrons, and $^{60}$Co gamma rays. Current-voltage (IV) and capacitance-voltage (CV) measurements were performed at room temperature for proton fluences up to $1\times10^{16}\;\mathrm{protons/cm^2}$, neutron fluences up to $1\times10^{18}\;\mathrm{1\;MeV\;n_{eq}/cm^2}$, and total ionizing doses up to 300 kGy. Hadron irradiation induces pronounced changes in both leakage current and bulk capacitance, consistent with radiation-induced formation of deep acceptor-like defects and strong compensation of the originally N-type material. For high proton fluences, the leakage current decreases and the bulk capacitance becomes bias-independent, indicating effective compensation of the epitaxial layer. Extreme neutron fluences lead to a substantial expansion of the depleted region into the originally highly doped substrate, as inferred from the measured capacitance values. Gamma irradiation up to 300 kGy results in significantly modified capacitance behavior, suggesting reduction of the effective doping concentration in the epitaxial and multiplication layers. The results demonstrate that radiation-induced compensation strongly modifies the effective space charge in 4H-SiC devices at high hadron fluences, while the leakage current is influenced by the enlarged depletion volume together with field-enhanced and surface-related generation mechanisms. In contrast, ionizing damage primarily affects the effective doping and electric-field distribution.