arXiv2022

Nanometers-thick Ferromagnetic Surface Produced by Laser Cutting of Diamond

In this work, we demonstrate that cutting diamond crystals with a laser (532~nm wavelength, 0.5~mJ energy, 200~ns pulse duration at 15~kHz) produces a $\lesssim 20~$nm thick surface layer with magnetic order at room temperature. We have measured the magnetic moment of five natural and six CVD diamond crystals of different size, nitrogen content and surface orientations with a SQUID magnetometer. A robust ferromagnetic response at 300~K is observed only for crystals that were cut with the laser along the (100) surface orientation. The magnetic signals are much weaker for the (110) and negligible for the (111) orientations. We attribute the magnetic order to the disordered graphite layer produced by the laser at the diamond surface. The ferromagnetic signal vanished after chemical etching or after moderate temperature annealing. The obtained results indicate that laser treatment of diamond may pave the way to create ferromagnetic spots at its surface.

cond-mat.mtrl-sci↗

arXiv2017

Evidence for room temperature superconductivity at graphite interfaces

In the last 43 years several hints were reported suggesting the existence of granular superconductivity above room temperature in different graphite-based systems. In this paper some of the results are reviewed, giving special attention to those obtained in water and n-heptane treated graphite powders, commercial and natural bulk graphite samples with different characteristics as well as transmission electron microscope (TEM) lamellae. The overall results indicate that superconducting regions exist and are localized at certain internal interfaces of the graphite structure. The existence of the rhombohedral graphite phase in all samples with superconducting-like properties suggests its interfaces with the Bernal phase as a possible origin for the high-temperature superconductivity, as theoretical calculations predict. High precision electrical resistance and magnetization measurements were used to identify a transition at $T_c \gtrsim 350~$K. To check for the existence of true zero resistance paths in the samples we used local magnetic measurements, which results support the existence of superconducting regions at such high temperatures.

cond-mat.supr-con↗

arXiv2016

Identification of a possible superconducting transition above room temperature in natural graphite crystals

Measuring with high precision the electrical resistance of highly ordered natural graphite samples from a Brazil mine, we have identified a transition at $\sim$350~K with $\sim$40~K transition width. The step-like change in temperature of the resistance, its magnetic irreversibility and time dependence after a field change, consistent with trapped flux and flux creep, and the partial magnetic flux expulsion obtained by magnetization measurements, suggest the existence of granular superconductivity below 350~K. The zero-field virgin state can only be reached again after zero field cooling the sample from above the transition. Paradoxically, the extraordinarily high transition temperature we found for this and several other graphite samples is the reason why this transition remained undetected so far. The existence of well ordered rhombohedral graphite phase in all measured samples has been proved by x-rays diffraction measurements, suggesting its interfaces with the Bernal phase as a possible origin for the high-temperature superconductivity, as theoretical studies predicted. The localization of granular superconductivity at these two dimensional interfaces prevents the observation of a zero resistance state or of a full Meissner state.

cond-mat.supr-con↗

arXiv2014

Granular superconductivity below 5~K in SPI-II pyrolytic graphite

We have studied the transport properties of transmission electron microscope (TEM) lamellae obtained from a pyrolytic graphite sample of grade B (SPI-II) with electrical contacts at the edges of the graphene layers. The temperature, magnetic field, input current dependence of the resistance as well as the current-voltage characteristic curves are compatible with the existence of granular superconductivity below 5~K. TEM pictures of the studied lamellae reveal clear differences of the embedded interfaces to those existing in more ordered pyrolytic samples, which appear to be the origin for the relatively lower temperatures at which the granular superconductivity is observed.

cond-mat.supr-con↗