arXiv2012

Effect of starting materials on the superconducting properties of SmFeAsO1-xFx tapes

SmFeAsO1-xFx tapes were prepared using three kinds of starting materials. It shows that the starting materials have an obvious effect on the impurity phases in final superconducting tapes. Compared with the other samples, the samples fabricated by SmAs, FeO, Fe2As, and SmF3 have the smallest arsenide impurity phase and voids. As a result, these samples possess much denser structure and better grain connectivity. Moreover, among the three kinds of samples fabricated in this work, this kind of sample has the highest zero-resistivity temperature ~40 K and largest critical current density ~4600 A/cm^2 in self-field at 4.2 K. This is the highest Jc values reported so far for SmFeAsO1-xFx wires and tapes.

cond-mat.supr-con↗

arXiv2011

High transport critical current densities in textured Fe-sheathed Sr1-xKxFe2As2+Sn superconducting tapes

We report the realization of grain alignment in Sn-added Sr1-xKxFe2As2 superconducting tapes prepared by ex-situ powder-in-tube method. At 4.2 K, high transport critical current densities Jc of 2.5x10^4 A/cm^2 (Ic = 180 A) in self-field and 3.5x10^3 A/cm^2 (Ic = 25.5 A) in 10 T have been measured. These values are the highest ever reported so far for Fe-based superconducting wires and tapes. We believe the superior Jc in our tape samples are due to well textured grains and strengthened intergrain coupling achieved by Sn addition. Our results demonstrated an encouraging prospect for application of iron based superconductors.

cond-mat.supr-con↗

arXiv2011

Synthesis and properties of La-doped CaFe2As2 single crystals with Tc = 42.7 K

Large single crystals of La-doped CaFe2As2 were successfully synthesized by the FeAs self-flux method. The x-ray diffraction patterns suggest high crystalline quality and c-axis orientation. By substitution of trivalent La3+ ions for divalent Ca2+, the resistivity anomaly in the parent compound CaFe2As2 is completely suppressed and a superconducting transition reaches the value of 42.7 K, which is higher than that of about 30 K reported in Saha S. R. et al., arXiv:1105.4798v1. The upper critical field has been determined with the magnetic field along ab-plane and c-axis, yielding an anisotropy of about 3.3.

cond-mat.supr-con↗

arXiv2011

Transport properties and anisotropy in rare earth doped CaFe2As2 single crystals with Tc above 40 K

In this paper we report the superconductivity above 40 K in the electron doping single crystal Ca1-xRexFe2As2 (Re = La, Ce, Pr). The x-ray diffraction patterns indicate high crystalline quality and c-axis orientation. the resistivity anomaly in the parent compound CaFe2As2 is completely suppressed by partial replacement of Ca by rare earth and a superconducting transition reaches as high as 43 K, which is higher than the value in electron doping FeAs-122 compounds by substituting Fe ions with transition metal, even surpasses the highest values observed in hole doping systems with a transition temperature up to 38 K. The upper critical field has been determined with the magnetic field along ab-plane and c-axis, yielding the anisotropy of 2~3. Hall-effect measurements indicate that the conduction in this material is dominated by electron like charge carriers. Our results explicitly demonstrate the feasibility of inducing superconductivity in Ca122 compounds via electron doping using aliovalent rare earth substitution into the alkaline earth site, which should add more ingredients to the underlying physics of the iron-based superconductors.

cond-mat.supr-con↗

arXiv2011

Direct observation of nanometer-scale amorphous layers and oxide crystallites at grain boundaries in polycrystalline Sr1-xKxFe2As2 superconductors

We report here an atomic resolution study of the structure and composition of the grain boundaries in polycrystalline Sr0.6K0.4Fe2As2 superconductor. A large fraction of grain boundaries contain amorphous layers larger than the coherence length, while some others contain nanometer-scale particles sandwiched in between amorphous layers. We also find that there is significant oxygen enrichment at the grain boundaries. Such results explain the relatively low transport critical current density (Jc) of polycrystalline samples with respect to that of bicrystal films.

cond-mat.supr-con↗

arXiv2011

Development of Powder-in-Tube Processed Iron Pnictide Wires and Tapes

The development of the PIT fabrication process of iron pnictide superconducting wires and tapes has been carried out in order to enhance their transport properties. Silver was found to be the best sheath material, since no reaction layer was observed between the silver sheath and the superconducting core. The grain connectivity of iron pnictide wires and tapes has been markedly improved by employing Ag or Pb as dopants. At present, critical current densities in excess of 3750 A/cm^2 (Ic = 37.5 A) at 4.2 K have been achieved on Ag-sheathed SrKFeAs wires prepared with the above techniques, which is the highest in iron-based wires and tapes so far. Moreover, Ag-sheathed Sm-1111 superconducting tapes were successfully prepared by PIT method at temperatures as low as 900C, instead of commonly used temperatures of 1200C. These results demonstrate the feasibility of producing superconducting pnictide composite wires, even grain boundary properties require much more attention.

cond-mat.supr-con↗

arXiv2011

Superconductivity induced by doping Rh in CaFe2-xRhxAs2

In this paper we report the synthesis of iron-based superconductors CaFe2-xRhxAs2 using one-step solid state reaction method, which crystallizes in the ThCr2Si2-type structure with a space group I4/mmm. The systematic evolution of the lattice constants demonstrates that the Fe ions are successfully replaced by the Rh. By increasing the doping content of Rh, the spin-density-wave (SDW) transition in the parent compound is suppressed and superconductivity emerges. The maximum superconducting transition temperature is found at 18.5 K with the doping level of x = 0.15. The temperature dependence of DC magnetization confirms superconducting transitions at around 15 K. The general phase diagram was obtained and found to be similar to the case of Rh-doping Sr122 system. Our results explicitly demonstrate the feasibility of inducing superconductivity in Ca122 compounds by higher d-orbital electrons doping, however, different Rh-doping effect between FeAs122 compounds and FeAs1111 systems still remains an open question.

cond-mat.supr-con↗

arXiv2011

Superconducting properties of FeSe wires and tapes prepared by gas diffusion technique

Superconducting FeSe in the form of wires and tapes were successfully fabricated using a novel gas diffusion procedure. Structural analysis by mean of x-ray diffraction shows that themain phase of tetragonal PbO-type FeSe was obtained by this synthesis method. The zero resistivity transition temperature of the FeSe was confirmed to be 9.3 K. The critical current density as high as 137 A/cm^2 (4 K, self field) has been observed. The results suggest that the diffusion procedure is promising in preparing high-quality FeSe wires and tapes.

cond-mat.supr-con↗

arXiv2011

Upper fields and critical current density of K0.58Fe1.56Se2 single crystals grown by one step technique

Single crystals of K0.58Fe1.56Se2 were successfully synthesized by a new single step process with the onset superconducting transition temperatures 31.9 K. The x-ray diffraction patterns suggest that they have high crystalline quality and c-axis orientation. A possible modulation structure of Fe-vacancy along c axis was observed. The upper critical field has been determined with the magnetic field along ab-plane and c-axis, yielding an anisotropy of about 3.3. It has also been shown that the critical current density of the K0.58Fe1.56Se2 is about 1.7x10^4 A/cm^2 at 5 K.

cond-mat.supr-con↗

arXiv2011

Enhanced critical current properties in Ba0.6K0.4+xFe2As2 superconductor by over-doping of potassium

Phase-pure polycrystalline Ba0.6K0.4+xFe2As2 with were prepared using a one-step solid-state reaction method. We found that over-doping of potassium can improve critical current density (Jc). High-field Jc for samples with x = 0.1 is three times higher than that for samples with x = 0. Over-doping of K has minimal effect on the critical transition temperature (Tc). Less than 0.5 K degradations in Tc was measured for samples with x = 0.1. TEM revealed high concentration of dislocations in samples with x = 0.1, resulting in enhanced flux pining. Further analyses on magnetization loops for powder samples confirm that K over-doping can promote intra-grain Jc. Our results indicate that slight excess of K in Ba0.6K0.4Fe2As2 samples is beneficial to high-field applications.

cond-mat.supr-con↗

arXiv2010

Fabrication and some properties of biaxially aligned Sr0.6K0.4Fe2As2 superconductors by processing in high magnetic field

We fabricated the c axis and ab-plane biaxially aligned Sr0.6K0.4Fe2As2 superconductor using a two-step magnetic field procedure. The effect of magnetic fields on the structure and superconducting properties of Sr0.6K0.4Fe2As2 has been investigated by using X-ray diffraction and magnetic measurements. The degree of orientation of the samples was about 0.39 for the c axis and 0.51 for ab-plane orientation, as evaluated from the Lotgering factor of X-ray diffraction. This technology might be useful in a variety of potential applications, including preparing iron based superconducting bulks and wires with high critical currents.

cond-mat.supr-con↗

arXiv2010

One-step method to grow Ba0.6K0.4Fe2As2 single crystals without fluxing agent

Single crystals of Ba0.6K0.4Fe2As2 with excellent quality have been successfully grown without fluxing agent through a simple one-step method for the first time. X-ray diffraction patterns demonstrate that the samples have high crystalline quality and c-axis orientation. The onset transition temperature is up to 38 K with the zero resistivity temperature about 36.7 K. Both the R-T and M-T data show a very sharp superconducting transition with transition width 0.4 K. We also found that the samples possess very large current carrying ability and high upper critical fields, indicating potential applications requiring very high field. The above simple and safe one-step technique of single crystal growth can be effective in other systems of Fe-based superconductors.

cond-mat.supr-con↗

arXiv2010

Heat treatment effects on the superconducting properties of Ag-doped SrKFeAs compound

The superconducting properties of polycrystalline Sr0.6K0.4Fe2As2 were strongly influenced by Ag doping (Supercond. Sci. Technol. 23 (2010) 025027). Ag addition is mainly dominated by silver diffusing, so the annealing process is one of the essential factors to achieve high quality Ag doped Sr0.6K0.4Fe2As2. In this paper, the optimal annealing conditions were studied for Ag doped Sr0.6K0.4Fe2As2 bulks prepared by a one-step solid reaction method. It is found that the annealing temperature has a strong influence on the superconducting properties, especially on the critical current density Jc. As a result, higher heat treatment temperature (~900C) is helpful in diffusing Ag and reducing the impurity phase gathered together to improve the grain connectivity. In contrast, low-temperature sintering is counterproductive for Ag doped samples. These results clearly suggest that annealing at ~900C is necessary for obtaining high Jc Ag-doped samples.

cond-mat.supr-con↗

arXiv2010

Low-temperature synthesis of SmFeAsO0.7F0.3 wires with high transport critical current density

Ag-sheathed SmFeAsO0.7F0.3 (Sm-1111) superconducting wires were prepared by a one-step solid state reaction at temperatures as low as 850~900C, instead of commonly used temperatures of 1150~1250C. The X-ray diffraction pattern of the as-sintered samples is well indexed on the basis of tetragonal ZrCuSiAs-type structure. We characterized transport critical current density Jc of the SmFeAsO0.7F0.3 wires in increasing and subsequently decreasing fields, by a resistive four-probe method. A transport Jc as high as ~1300 A/cm^2 at 4.2 K and self field has been observed for the first time in Sm-1111 type polycrystalline superconductors. The Jc also shows a rapid depression in small applied fields as well as a magnetic-history dependence, indicating weak-linked grain boundaries. The low-temperature synthesis method can be very beneficial to fabricating the RE-1111 iron oxynictides in a convenient and safe way.

cond-mat.supr-con↗

arXiv2010

Influence of Pb addition on the superconducting properties of polycrystalline Sr0.6K0.4Fe2As2

Polycrystalline Sr0.6K0.4Fe2As2 samples with various Pb additions (0-20 wt%) were prepared using a one-step solid state reaction. X-ray diffraction analysis shows no evidence for chemical reaction between the Pb and the FeAs-based superconductor. However, the presence of the Pb can affect the microstructure and superconducting properties of the final products. The critical transition temperature Tc indicates no degradation up to 20 wt% Pb addition, and dramatic improvements of magnetic Jc and irreversibility field Hirr were observed for appropriate Pb concentration. Transport critical current property of pure and Pb-added Sr0.6K0.4Fe2As2 tapes was also measured by a four-probe technique, and a remarkable enhancement of Jc at low fields was detected for the Pb added tapes.

cond-mat.supr-con↗

arXiv2010

Development of Doped MgB2 Wires and Tapes for Practical Applications

A review of current developments in the study of chemical doping effect on the superconducting properties of MgB2 wires and tapes is presented, based on the known literature data and our own results. The critical current density of MgB2 can be improved through various kinds of dopants. Among these dopants, doping with carbon-containing materials seems to be the most effective way to improve the Jc performance. The doping effect of carbon in different forms and carbon-based compounds such as SiC, nano-C, metal carbides, as well as aromatic hydrocarbon and carbohydrate on the Jc-B characteristics of MgB2 was discussed in detail. The C can be incorporated into the MgB2 crystal lattice by replacing boron, and thus Bc2 is significantly enhanced due to selective tuning of impurity scattering of two bands in the two-band MgB2. Besides the efforts of increasing Bc2 by carbon doping, the fine grain size and nano-size inclusions caused by doping would create many flux pinning centres improving the Jc-B property of MgB2. Based on these considerations, we suggested some principles for the selection of dopants.

cond-mat.supr-con↗

arXiv2009

The role of silver addition on the structural and superconducting properties of polycrystalline Sr0.6K0.4Fe2As2

The effect of Ag addition (0-20 wt%) on polycrystalline Sr0.6K0.4Fe2As2 superconductor has been investigated. It is found that the critical transition temperature Tc was not depressed, and the irreversibility field Hirr and hysteresis magnetization were significantly enhanced upon Ag addition. Characterization study reveals that larger grains are observed in the Ag-added samples. Moreover, the formation of glassy phase as well as amorphous layer, which are present in almost all the grain edges and boundaries in pure samples, are suppressed by Ag addition. The improvement of superconducting properties in Ag-added samples may originate from the enlargement of grains as well as better connections between grains

cond-mat.supr-con↗

arXiv2009

Large transport critical currents of powder-in-tube Sr0.6K0.4Fe2As2/Ag superconducting wires and tapes

We report significant transport critical currents firstly achieved in Sr0.6K0.4Fe2As2 wires and tapes with a Tc = 34 K, which were fabricated through an in-situ powder-in-tube process. Silver was used as a chemical addition as well as a sheath material. Transport measurements were performed by a standard four-probe resistive method. All the wire and tape samples have shown transport properties. Critical current density Jc was enhanced upon silver addition, and at 4.2 K, a best Jc of ~1200 A/cm^2 (Ic = 9 A) was achieved for 20 % silver added tapes, which is the highest in iron-based wires and tapes so far. The Jc is almost field independent between 1 T and 10 T, exhibiting a strong vortex pinning. Such a high transport critical current density is attributed to the absence of reaction layer between the silver sheath and superconducting core, as well as an improved connectivity between grains. We also identify a weak-link behavior from the creep drop of Jc at low fields and a hysteretic phenomenon. Finally, we found that compared to Fe, Ta and Nb tubes, Ag was the best sheath material for the fabrication of high-performance 122 type pnictide wires and tapes.

cond-mat.supr-con↗