Y. M. Xiong

Publications and source records attributed to Y. M. Xiong.

23 records · Page 2Linked to original sources

arXiv2004

Effect of oxygen content on the transport properties and magnetoresistance in [Ca$_{2}$CoO$_{3-δ}$]$_{0.62}$[CoO$_{2}$] single crystals

Transport property is investigated in [Ca$_{2}$CoO$_{3-δ}$]$_{0.62}$[CoO$_{2}$] single crystals obtained by varying annealing conditions. The $ρ_{ab}(T)$ exhibits a resistivity minimum, and the temperature corresponding to this minimum increases with the loss of oxygen content, indicative of the enhancement of spin density wave (SDW). Large negative magnetoresistance (MR) was observed in all single crystals [Ca$_{2}$CoO$_{3-δ}$]$_{0.62}$[CoO$_{2}$], while a magnetic-field-driven insulator-to-metal (IM) transition in oxygen annealed samples. These results suggest a ferromagnetic correlation in system enhanced by oxygen content. In addition, a low temperature thermal activation resistivity induced by fields was observed in single crystals annealed in oxygen atmosphere.

cond-mat.str-el↗

arXiv2004

Magnetic and Transport Properties in $CoSr_2Y_{1-x}Ca_xCu_2O_7$ ($x$=0$\sim$0.4)

Magnetic and transport properties of $Co Sr_2 Y_{1-x} Ca_x Cu_2 O_7$ ($x=0 \sim 0.4$) system have been investigated. A broad maximum in M(T) curve, indicative of low-dimensional antiferromagnetic ordering originated from $CoO_{1+δ}$ layers, is observed in Ca-free sample. With increasing Ca doping level up to 0.2, the M(T) curve remains almost unchanged, while resistivity is reduced by three orders. Higher Ca doping level leads to a drastic change of magnetic properties. In comparison with the samples with $x=0.0 \sim 0.2$, the temperature corresponding to the maximum of M(T) is much lowered for the sample $x$=0.3. The sample $x$=0.4 shows a small kink instead of a broad maximum and a weak ferromagnetic feature. The electrical transport behavior is found to be closely related to magnetic properties for the sample $x$=0.2, 0.25, 0.3, 0.4. It suggests that $CoO_{1+δ}$ layers are involved in charge transport in addition to conducting $CuO_2$ planes to interpret the correlation between magnetism and charge transport. X-ray photoelectron spectroscopy studies give an additional evidence of the the transfer of the holes into the $CoO_{1+δ}$ charge reservoir.

cond-mat.str-el↗

arXiv2004

Raman spectra in epitaxial thin films $La_{1-x}Ca_xMnO_3$ (x = 0.33, 0.5) grown on different substrates

Raman spectra of LCMO films grown on LAO (001), STO (001), and MgO (001) substrates were studied at different temperatures. The effect of temperature, doping level and strain on Raman spectra are discussed in detail. With decreasing temperature, the changes of Raman spectra are correlated with the disorder-order transition, shuch as: paramagnetism to ferromagnetism, and charge-ordering. The strain induced by lattice-substrate mismatch affects the Raman spectra strongly. The mode induced by disorder of oxygen defects is apparently observed in $La_{0.67}Ca_{0.33}MnO_3$ film on STO due to the larger tensile strain. While this mode can not be seen in the Raman spectra for the films on LAO and MgO. A strong unsigned mode at about 690 $cm^{-1}$ is observed in all films except for $La_{0.67}Ca_{0.33}MnO_3$ film on LAO, which is not observed in bulk sample easily. It suggests that the mode is closely related to the strain.

cond-mat.str-el↗

arXiv2001

Thermopower and thermal conductivity of superconducting perovskite $MgCNi_3$

The thermopower and thermal conductivity of superconducting perovskite $MgCNi_3$ ($T_c \approx$ 8 K) have been studied. The thermopower is negative from room temperature to 10 K. Combining with the negative Hall coefficient reported previously, the negative thermopower definetly indicates that the carrier in $MgCNi_3$ is electron-type. The nonlinear temperature dependence of thermopower below 150 K is explained by the electron-phonon interaction renormalization effects. The thermal conductivity is of the order for intermetallics, larger than that of borocarbides and smaller than $MgB_2$. In the normal state, the electronic contribution to the total thermal conductivity is slightly larger than the lattice contribution. The transverse magnetoresistance of $MgCNi_3$ is also measured. It is found that the classical Kohler's rule is valid above 50 K. An electronic crossover occures at $T^* \sim 50 K$, resulting in the abnormal behavior of resistivity, thermopower, and magnetoresistance below 50 K.

cond-mat.supr-con↗

arXiv2001

Normal state resistivity, upper critical field and Hall effect in superconducting perovskite $MgCNi_3$

The normal state resistivtity, upper critical field $H_{c2}$ and Hall coefficient $R_H$ in superconducting perovskite $MgCNi_3$ ($T_c \approx 8 K$) have been studied. Above 70 K, $ρ(T)$ fits well curve predicted by Bloch-Grüneisen theory consistently with electron-phonon scattering. $H_{c2}(0)$ was estimated to be about 15.0 Tesla within the weak-coupling BCS theory, and the superconducting coherence length $ξ(0)$ is approximately 47 Å. $R_H$ of $MgCNi_3$ is negative for the whole temperature range which definitely indicates that the carrier in $MgCNi_3$ is electron-type. $R_H$ is temperature independent between $T_c$ and $\sim$ 140 K. Above $\sim$ 140 K, the magnitude of $R_H$ decreases as temperature rises. At T = 100 K, the carrier density is $1.0 \times 10^{22}/cm^3$, which is comparable with that in perovskite $(Ba,K)BiO_3$, and less than that of the metallic binary $MgB_2$.