Y(Ni, Mn)O3 epitaxial thin films prepared by pulsed laser deposition

High–quality epitaxial YNixMn1-xO3 thin films have been successfully grown on SrTiO3 (100) (STO) by pulsed laser deposition. X-ray diffraction studies showed that the films deposited on STO are fully c-axis oriented and exhibit in-plane alignment. The magnetic transition temperatures (Tc) of the films (both x=0.33 and 0.5) are equivalent to the values of the corresponding bulk samples. However, when x=0.5, the films show magnetic properties quite different from those of bulk samples. This difference may be caused by the structure distortion in these films.

cond-mat.str-el↗

arXiv2003

Improvement of critical current density in Fe-sheathed MgB2 tapes by ZrSi2, ZrB2 and WSi2 doping

Fe-sheathed MgB2 tapes were prepared through the in situ powder-in-tube technique by 5 at.% ZrSi2, ZrB2 and WSi2 doping, respectively. The doping effect of these compounds on the microstructure and superconducting properties of MgB2 tapes has been investigated by using x-ray diffraction, scanning electron microscope, transport measurements and DC susceptibility measurements. Compared to the undoped samples, Jc for all the doped samples were much improved; the best result in terms of Jc was achieved for ZrSi2 doping, by up to a factor of 3.4 at 4.2 K in magnetic fields up to 12 T. Moreover, these dopants did not significantly decrease the transition temperature. The Jc-B curves of WSi2-doped tapes show better performance in higher magnetic fields in comparison to undoped tapes, suggesting that pinning centers effective in a high-field region were possibly introduced.

cond-mat.supr-con↗