arXiv2016

Effects of Pnictogen Atmosphere Annealing in Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$

It has been clarified that bulk superconductivity in Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ can be induced by annealing in an appropriate atmosphere to remove the harmful effects of excess iron. In order to clarify the details of the annealing process, we studied the changes in the physical properties and reaction products of Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ annealed in pnictogen (P, As, Sb) atmospheres. Crystals annealed in a pnictogen atmosphere show bulk superconductivity and the values of $T_{c}$ and $J_{c}$ are about $14~$K and 2-4 $\times 10{^5}~$A/cm$^2$ ($2~$K, self-field), respectively. It is also found that the reaction rate increases with the increase in the saturated vapor pressure of the pnictogen. Unexpectedly, the reaction products of Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ after annealing in a P atmosphere mainly consist of FeTe$_2$. In addition, the amount of P required to obtain the optimal $T_{c}$ is much smaller than the amount of excess iron, which is similar to the case of oxygen annealing. P, oxygen, and to some extent As could serve as catalysts to form FeTe$_2$ to remove excess iron.

cond-mat.supr-con↗

arXiv2016

Slow phonon vortices and defect modes in periodic nano-waveguides

We identify a broad class of phonon modes with persistent vortex fluxes at arbitrarily slow propagating velocities in periodic nano-waveguides. Such phonon vortices are associated with the split band-edges in dispersion dependencies, which can be engineered by waveguide design. Modulations introduced in such waveguides can support a pair of defect cavity phonon modes with an arbitrarily small frequency splitting. These features can find applications for sensing and nano-manipulation.

physics.optics↗

arXiv2016

Recombination processes in CuInS$_{2}$/ZnS Nanocrystals during steady-state photoluminescence

We report on temperature- and excitation-power-dependent photoluminescence (PL) study of CuInS$_{2}$/ZnS nanocrystals dispersed on a SiO$_{2}$/Si substrate with a confocal micro-PL system. With increasing the excitation power at 22 K and room temperature, the PL spectra are blue-shifted because of the state filling. At low temperature, a small peak is observed at the low energy side of the spectrum, which could be due to the F$\ddot{o}$rster resonance energy transfer between different nanocrystals. The integrated PL intensity increases sublinearly as a function of excitation power with a power factor of around 2/3, which demonstrates the Auger recombination dominated process in the nanocrystals, especially under the high excitation power.

cond-mat.mtrl-sci↗

arXiv2015

Observation of coupling between zero- and two-dimensional semiconductor systems based on anomalous diamagnetic effects

We report the direct observation of coupling between a single self-assembled InAs quantum dot and a wetting layer, based on strong diamagnetic shifts of many-body exciton states using magneto-photoluminescence spectroscopy. An extremely large positive diamagnetic coefficient is observed when an electron in the wetting layer combines with a hole in the quantum dot; the coefficient is nearly one order of magnitude larger than that of the exciton states confined in the quantum dots. Recombination of electrons with holes in a quantum dot of the coupled system leads to an unusual negative diamagnetic effect, which is five times stronger than that in a pure quantum dot system. This effect can be attributed to the expansion of the wavefunction of remaining electrons in the wetting layer or the spread of electrons in the excited states of the quantum dot to the wetting layer after recombination. In this case, the wavefunction extent of the final states in the quantum dot plane is much larger than that of the initial states because of the absence of holes in the quantum dot to attract electrons. The properties of emitted photons that depend on the large electron wavefunction extents in the wetting layer indicate that the coupling occurs between systems of different dimensionality, which is also verified from the results obtained by applying a magnetic field in different configurations. This study paves a new way to observe hybrid states with zero- and two-dimensional structures, which could be useful for investigating the Kondo physics and implementing spin-based solid-state quantum information processing.

cond-mat.mes-hall↗

arXiv2015

Enhancement of critical current density and mechanism of vortex pinning in H$^+$-irradiated FeSe single crystal

In this report, we comprehensively study the effect of H$^+$ irradiation on the critical current density, $J_c$, and vortex pinning in FeSe single crystal. It is found that the value of $J_c$ for FeSe is enhanced more than twice after 3-MeV H$^+$ irradiation. The scaling analyses of the vortex pinning force based on the Dew-Hughes model reveal that the H$^+$ irradiation successfully introduce point pinning centers into the crystal. We also find that the vortex creep rates are strongly suppressed after irradiation. Detailed analyses of the critical current dependent pinning energy based on the collective creep theory and extend Maley's method show that the H$^+$ irradiation enhances the value of $J_c$ before the flux creep, and also reduces the size of flux bundle, which will further reduce the field dependence of $J_c$ due to vortex motion.

cond-mat.supr-con↗

arXiv2015

Critical current density, vortex dynamics, and phase diagram of FeSe single crystal

We present a comprehensive study of the vortex pinning and dynamics in a high-quality FeSe single crystal, which is free from doping introduced inhomogeneities and charged quasi-particle-scattering because of its innate superconductivity. Critical current density, $J_c$, is found to be almost isotropic, and reaches a value $\sim$ 3 $\times$ 10$^4$ A/cm$^2$ at 2 K (self-field) for both $H$ $\|$ $c$ and $ab$. The normalized magnetic relaxation rate $S$ (= $\mid$dln$M$/dln$t$$\mid$) shows a temperature insensitive plateau behavior in the intermediate temperature range with a relatively high creep rate ($S$ $\sim$ 0.02 under zero field), which is interpreted in the framework of the collective creep theory. A crossover from the elastic to plastic creep is observed, while the fish-tail effect is absent for both $H$ $\|$ $c$ and $ab$. Based on this observation, the origin of the fish-tail effect is also discussed. Combining the results of $J_c$ and $S$, vortex motion in FeSe single crystal is found to be dominated by sparse strong point-like pinning from nm-sized defects or imperfections. The weak collective pinning is also observed and proved in the form of large bundles. Besides, the vortex phase diagram of FeSe is also constructed and discussed.

cond-mat.supr-con↗

arXiv2015

Social Data Offloading in D2D-Enhanced Cellular Networks by Network Formation Games

Recently, cellular networks are severely overloaded by social-based services, such as YouTube, Facebook and Twitter, in which thousands of clients subscribe a common content provider (e.g., a popular singer) and download his/her content updates all the time. Offloading such traffic through complementary networks, such as a delay tolerant network formed by device-to-device (D2D) communications between mobile subscribers, is a promising solution to reduce the cellular burdens. In the existing solutions, mobile users are assumed to be volunteers who selfishlessly deliver the content to every other user in proximity while moving. However, practical users are selfish and they will evaluate their individual payoffs in the D2D sharing process, which may highly influence the network performance compared to the case of selfishless users. In this paper, we take user selfishness into consideration and propose a network formation game to capture the dynamic characteristics of selfish behaviors. In the proposed game, we provide the utility function of each user and specify the conditions under which the subscribers are guaranteed to converge to a stable network. Then, we propose a practical network formation algorithm in which the users can decide their D2D sharing strategies based on their historical records. Simulation results show that user selfishness can highly degrade the efficiency of data offloading, compared with ideal volunteer users. Also, the decrease caused by user selfishness can be highly affected by the cost ratio between the cellular transmission and D2D transmission, the access delays, and mobility patterns.

cs.GT↗

arXiv2015

Evolution of superconducting and transport properties in annealed FeTe$_{1-x}$Se$_x$ (0.1 $\leq$ $x$ $\leq$ 0.4) multiband superconductors

We investigated the superconducting and transport properties in FeTe$_{1-x}$Se$_{x}$ (0.1 $\leq$ $x$ $\leq$ 0.4) single crystals prepared by O$_2$-annealing. Sharp superconducting transition width observed in magnetization measurement and the small residual resistivity prove the high quality of the crystals. All the crystals manifest large, homogeneous, and isotropic critical current density \emph{J}$_c$ with self-field value over 10$^5$ A/cm$^2$ at 2 K. The large and field-robust critical current densities prove that the superconductivity in FeTe$_{1-x}$Se$_{x}$ (0.1 $\leq$ $x$ $\leq$ 0.4) is in bulk nature. The values of anisotropy parameter close to $T_c$ for crystals with different Se doping levels all reside in the range of 2 - 3. Hall coefficients $R_H$ keeps positive and almost constant value at high temperatures, followed by a sudden decreases before reaching $T$$_c$, which indicates that the electron-type charge carriers become dominant at low temperatures. Furthermore, the characteristic temperature for the sudden decrease in $R_H$ gradually increases with Se doping.

cond-mat.supr-con↗

arXiv2015

Longitudinal wave function control in single quantum dots with an applied magnetic field

Controlling single-particle wave functions in single semiconductor quantum dots is in demand to implement solid-state quantum information processing and spintronics. Normally, particle wave functions can be tuned transversely by an perpendicular magnetic field. We report a longitudinal wave function control in single quantum dots with a magnetic field. For a pure InAs quantum dot with a shape of pyramid or truncated pyramid, the hole wave function always occupies the base because of the less confinement at base, which induces a permanent dipole oriented from base to apex. With applying magnetic field along the base-apex direction, the hole wave function shrinks in the base plane. Because of the linear changing of the confinement for hole wave function from base to apex, the center of effective mass moves up during shrinking process. Due to the uniform confine potential for electrons, the center of effective mass of electrons does not move much, which results in a permanent dipole moment change and an inverted electron-hole alignment along the magnetic field direction. Manipulating the wave function longitudinally not only provides an alternative way to control the charge distribution with magnetic field but also a new method to tune electron-hole interaction in single quantum dots.

cond-mat.mes-hall↗

arXiv2014

Magneto-optical characterizations of FeTe$_{0.5}$Se$_{0.5}$ thin films with critical current density over 1 MA/cm$^2$

We performed magneto-optical (MO) measurements on FeTe$_{0.5}$Se$_{0.5}$ thin films grown on LaAlO$_3$ (LAO) and Yttria-stabilized zirconia (YSZ) single-crystalline substrates. These thin films show superconducting transition temperature, ${T_c}$ $\sim$ 19 K, 4 K higher than the bulk sample. Typical roof-top patterns can be observed in the MO images of thin films grown on LAO and YSZ, from which a large and homogeneous critical current density, ${J_c}$, over 1 $\times$ 10$^6$ A/cm$^2$ at 5 K was obtained. Magnetic flux penetration measurement reveals that the current is almost isotropically distributed in the two thin films. Compared with bulk crystals, FeTe$_{0.5}$Se$_{0.5}$ thin film demonstrates not only higher ${T_c}$, but also much larger ${J_c}$, which is attractive for applications.

cond-mat.supr-con↗

arXiv2014

Charge state control in single InAs/GaAs quantum dots by external electric and magnetic fields

We report a photoluminescence (PL) spectroscopy study of charge state control in single self-assembled InAs/GaAs quantum dots by applying electric and/or magnetic fields at 4.2 K. Neutral and charged exciton complexes were observed under applied bias voltages from -0.5 V to 0.5 V by controlling the carrier tunneling. The highly negatively charged exciton emission becomes stronger with increasing pumping power, arising from the fact that electrons have a smaller effective mass than holes and are more easily captured by the quantum dots. The integrated PL intensity of negatively charged excitons is affected significantly by a magnetic field applied along the sample growth axis. This observation is explained by a reduction in the electron drift velocity caused by an applied magnetic field, which increases the probability of non-resonantly excited electrons being trapped by localized potentials at the wetting layer interface, and results in fewer electrons distributed in the quantum dots. The hole drift velocity is also affected by the magnetic field, but it is much weaker.

cond-mat.mes-hall↗

arXiv2014

Bulk Superconductivity in Fe1+yTe0.6Se0.4 Induced by Removal of Excess Fe

Experimental evidences from transport, magnetic, and magneto-optical (MO) image measurements confirmed that arsenic (As) vapor annealing was another effective way to induce bulk superconductivity with isotropic, large, and homogenous superconducting critical current density (Jc) in Fe1+yTe0.6Se0.4 single crystal. Since As is an exotic and easily detectable heavy element to Fe1+yTe0.6Se0.4 single crystal, As vapor annealing is very advantageous for the study of annealing mechanism. Detailed micro-structural and elemental analyses exclude the possibility that intercalating or doping effect may happen in the other post-annealing methods, proving that Fe reacts with As on the surface of the crystal and the reaction itself acts as a driving force to drag excess Fe out. The removal of excess Fe results in the good superconductivity performance.

cond-mat.supr-con↗

arXiv2014

Anisotropic Superconductivity of Ca1-xLaxFeAs2 (x ~ 0.18) Single Crystal

Anisotropic superconducting properties including the upper critical field Hc2, thermal activation energy U0, and critical current density Jc are systematically studied in a large Ca1-xLaxFeAs2 single crystal (x ~ 0.18). The obtained Hc2 bears a moderate anisotropy gamma of approximately 2-4.2, located between those of '122' Ba1-xKxFe2As2 (1 < gamma < 2) and '1111' NdFeAsO1-xFx (5 < gamma < 9.2). Both the magnitude of U0 and its field dependence are very similar to those of NdFeAsO1-xFx, also indicating anisotropic superconductivity. Moreover, high and anisotropic Jc's exceeding 10^5 A/cm2 have been calculated from the magnetization hysteresis loops, indicating the existence of strong bulk-dominated pinning in the present superconducting material.

cond-mat.supr-con↗

arXiv2014

Multiband Effect and Possible Dirac Fermions in Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$

We investigated the transport properties of Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ single crystals with different amounts of excess Fe prepared by O$_2$ annealing. The O$_2$ annealing remarkably improves transport properties. In particular, a strongly nonlinear Hall resistivity was observed only in the fully-annealed crystal, and the magnetoresistance (MR) is drastically enhanced after annealing, reaching a value larger than 17% at 16 K and 14 T. The obvious change of transport properties after the annealing indicates that the band structure of Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ is affected by the excess Fe. The nonlinear Hall resistivity and violation of (modified) Kohler's scaling of the large MR prove the multiband effects in the Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ single crystal. The MR for the fully-annealed crystal develops linearly against magnetic field from intermediate field (e. g. 2 T at 16 K) to the measurement limit of 14 T. This phenomenon is interpreted by the existence of Dirac cone state, in which all the Dirac fermions occupy only the lowest Landau level in the quantum limit.

cond-mat.supr-con↗

arXiv2014

Dynamics and mechanism of oxygen annealing in Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ single crystal

Iron chalcogenide Fe(Te,Se) attracted much attention due to its simple structure, which is favorable for probing the superconducting mechanism. Its less toxic nature compared with iron arsenides is also advantageous for applications of iron-based superconductors. By intercalating spacer layers, superconducting transition temperature has been raised over 40 K. On the other hand, the presence of excess Fe is almost unavoidable in Fe(Te,Se) single crystals, which hinders the appearance of bulk superconductivity and causes strong controversies over its fundamental properties. Here we report a systematical study of O$_2$-annealing dynamics in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ by controlling the amount of O$_2$, annealing temperature, and time. Bulk superconductivity can be gradually induced by increasing the amount of O$_2$ and annealing time at suitable temperatures. The optimally annealed crystals can be easily obtained by annealing with ~ 1.5% molar ratio of oxygen at 400 $^{\circ}$C for more than 1 hour. Superconductivity was witnessed to evolve mainly from the edge of the crystal to the central part. After the optimal annealing, the complete removal of excess Fe was demonstrated via STM measurements. Some fundamental properties were recharacterized and compared with those of as-grown crystals to discuss the influence of excess Fe.

cond-mat.supr-con↗

arXiv2013

Bulk Superconductivity in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ Induced by Annealing in Se and S Vapor

We reported that bulk superconductivity in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ can be induced by annealing in Se and S vapor. The well-annealed samples show a large critical current density, emph{J}$_c$ $\sim$ 2 - 4 $\times$ 10$^5$ A/cm$^2$. Combined with our previous reports about O$_2$ and Te annealing effects, we proved that bulk superconductivity can be successfully induced in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ by annealing in atmosphere of all chalcogens, such as O, S, Se and Te.

cond-mat.supr-con↗

arXiv2013

Magnetic relaxation and collective vortex creep in FeTe$_{0.6}$Se$_{0.4}$ single crystal

We study the vortex dynamics in high-quality FeTe$_{0.6}$Se$_{0.4}$ single crystal by performing magnetization measurements of the screening current density \emph{J}$_s$ and flux creep rate \emph{S}. Temperature dependence of \emph{S} shows a plateau in the intermediate temperature region with a high creep rate $\sim$ 0.03, which is interpreted in the framework of the collective creep theory. A crossover from elastic to plastic creep is observed. The glassy exponent and barrier height for flux creep are directly determined by extended Maley's method. \emph{J}$_s$ with flux creep, obtained from magnetic hysteresis loops, is successfully reproduced based on the collective creep analysis. We also approach critical current density without flux creep by means of the generalized inversion scheme, which proves that the $δ$\emph{l} and $δ$\emph{T}$_c$ pinning coexist in FeTe$_{0.6}$Se$_{0.4}$ single crystal.

cond-mat.supr-con↗

arXiv2013

Evolution of Superconductivity in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ Annealed in Te Vapor

We report a detailed study of the Te vapor annealing effect in Fe$_{1+y}$Te$_{0.6}$Se$_{0.4}$ single crystals. Bulk superconductivity can be gradually induced by annealing with increasing amount of Te, until the molar ratio of Te to the sample reaches 1 : 10. By further increasing Te molar ratio, superconducting volume is gradually reduced. Resistivity and Hall effect measurements manifest that annealing in Te vapor delocalizes the charge carriers by removing excess Fe. The optimally Te annealed crystal shows homogeneous critical current densities with a large value of $\sim$ 4.3 $\times$ 10$^5$ A/cm$^2$, which proves that the Te annealing is effective to induce bulk superconductivity in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$.

cond-mat.supr-con↗