Growth of Ni and Ni-Cr Alloy Thin Films on MgO(001): Effect of Alloy Composition on Surface Morphology

Abstract

The effects of substrate treatment, temperature and composition on the surface morphology of Ni-Cr thin films grown on MgO(001) are studied by scanning tunneling microscopy (STM) and atomic force microscopy (AFM). A combination of acid-etching and high temperature deposition (400C) will result in smooth films and terraces (up to 30 nm wide) suitable for the study of progression of chemical reactions on the surface. Two different treatments are used to prepare the MgO substrates for deposition and they introduce characteristic differences in film surface morphology. Thin films that are grown on the phosphoric acid-treated substrates present reduced nucleation density during the initial stages of film growth which results in long and wide terraces. Due to the about 16 percent lattice mismatch in the Ni(001)/MgO(001) system, film growth at 400C yields discontinuous films and a two-step growth process is necessary to obtain a continuous layer. Ni films are deposited at 100C and subjected to a post-growth anneal at 300C for 2 hours to obtain a smoother surface. The addition of just 5 wt. percent Crchanges the growth processes and yields continuous films at 400C without de-wetting in contrast to pure Ni films. With increasing Cr content, the films become progressively smoother with wider terraces. Ni5Cr alloy thin films have an rms surface roughness of 3.63+/-0.75 nm while Ni33Cr thin film is smoother with an rms roughness of only 0.29 +/-0.13 nm. The changes in film growth initiated by alloying with Cr are due to changes in the interfacial chemistry which favorably alters the initial adsorption of the metal atoms on MgO surface and suggests a reduction of the Ehrlich-Schwoebel barrier. The growth of smooth Ni-Cr thin films with well-defined surface structure opens up a new pathway for a wide range of surface science studies related to alloy performance.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Gopalakrishnan Ramalingam, Petra Reinke. 2016-11-16. Growth of Ni and Ni-Cr Alloy Thin Films on MgO(001): Effect of Alloy Composition on Surface Morphology. https://doi.org/10.1063/1.4971261

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Measuring chiral phonons

Chiral phonons are quantized vibrations where the atomic motion in a solid breaks improper rotation symmetries. In many cases, chiral phonons possess angular momenta and are therefore selective to circularly polarized light. Both fundamental and applied research efforts on chiral phonons have been gaining increasing attention owing to their importance in a variety of fields including spintronics, spin-selective chemical reactions, thermal transport, quantum information processing and biosensing, where the bi-directional spin-lattice coupling enabled by chiral phonons can be harnessed in new ways, and potentially lead to new functionalities. Thus far, the studies of chiral phonons across diverse materials platforms have evolved largely independently within these fields, but the experimental techniques are often interrelated. In this perspective, we present a detailed description, as well as advantages and disadvantages of the current approaches for experimentally measuring chiral phonons in chiral and achiral materials. We conclude with a discussion of new methods for measuring chiral phonons. Ultimately, this work seeks to offer an experimental guide for systematically investigating the properties of chiral phonons in various materials systems and applications.

cond-mat.mtrl-sci

A model of grain growth in UN integrating molecular dynamics, phase-field modeling, and uncertainty quantification

Grain growth kinetics and grain-boundary (GB) properties in uranium mononitride (UN) are investigated through an integrated multiscale framework combining molecular dynamics (MD), phase-field modeling, and surrogate-assisted uncertainty quantification. MD simulations yield GB energies for 27 symmetric tilt boundaries from 0--2000~K, which are consistent with available DFT values. The average GB energy is nearly temperature-independent below 1000~K and increases at higher temperatures. A mechanistic pore-drag model applied to the only available grain growth dataset for actinide nitrides yields a mobility reduction factor of $s \approx 0.93$--$0.99$, statistically indistinguishable from unity, confirming that pore drag is negligible under the experimental conditions. The intrinsic GB mobility is therefore extracted directly from the effective mobility, yielding $M_0 = 2.05\times10^{-15}$~m$^4$/(J$\cdot$s) and $Q_M = 0.89$~eV. Phase-field simulations conducted from 1500--2000~K confirm normal curvature-driven grain growth, with grain size distributions converging to the Hillert-like form. A surrogate-assisted global sensitivity analysis---combining principal component analysis, Gaussian process regression, and Sobol decomposition---reveals that the mobility prefactor $M_0$ dominates output variance at all times, followed by the activation energy $Q_M$, while the GB energy $\gamma$ contributes minimally. These results establish the first quantitative grain growth framework for UN and identify the reduction of uncertainty in $M_0$ and $Q_M$ as the highest-priority target for future experimental efforts.

cond-mat.mtrl-sci

Silicon Solar Cell Design for >30% Efficiency via Singlet Fission

Singlet fission (SF) materials convert high-energy photons into multiple charge carriers, providing a route to exceed the efficiency limits of single-junction silicon solar cells without many of the complexities of multi-junction tandem designs. Following the first demonstration of an SF-enhanced silicon solar cell in 2025, there is a need to understand how SF materials can be effectively integrated into high-efficiency industrial silicon devices and translated from proof of concept to a manufacturable technology. Using coupled optical and electrical simulations, we assess the efficiency potential of several industrially relevant silicon cell architectures combined with SF materials. Interdigitated back-contact (IBC) cells offer the greatest potential for improvement due to unrestricted front-surface access and can achieve efficiencies exceeding 33%. However, performance is highly sensitive to front-surface passivation quality. Appropriate silicon design, particularly controlled surface doping and fixed interfacial charge, can mitigate recombination losses and relax passivation requirements for ultra-thin exciton-transfer layers.

cond-mat.mtrl-sci