Stress Drops Associated with Surface Crack Formation in Photo-aged Polypropylene during Three-Point Bending

Kazuya Haremaki·Yusuke Koide·Takashi Uneyama·Yuichi Masubuchi·Takato Ishida
View original source ↗Read source document ↗Export metadata ↓

Abstract

Using three-point bending, this study investigates surface-crack formation in photo-aged polypropylene (PP) that has a depth-dependent aging gradient. PP undergoes embrittlement under ultraviolet (UV) irradiation, and because the photo-oxidation proceeds inward from the irradiated surface, the embrittlement develops non-uniformly across the specimen thickness. PP specimens were mildly photo-aged by UV irradiation and had not yet developed visible surface cracks. Each specimen was bent in two configurations: with the UV-irradiated ("aged") surface on the tensile side, and with the opposite ("reverse") surface on the tensile side. When the aged surface was on the tensile side, the stress-strain curves exhibited several discrete stress drops, and in-situ side-view observation confirmed that the formation of each new surface crack coincided with a stress drop. In contrast, no clear stress drops were observed when the reverse surface was on the tensile side. These results show that the through-thickness gradient of embrittlement is directly reflected in the bending stress-strain response. Uniaxial tensile testing, the standard method for evaluating mechanical properties, formally assumes a nominally uniform deformation across the cross-section and therefore reflects the spatially averaged response. Three-point bending, by contrast, imposes the largest tensile strain at the specimen surface and thus selectively probes the embrittled surface layer, making it an effective method for detecting the surface embrittlement of photo-aged polymers.

Explore related subjects

cond-mat.soft

Keep this discovery

BibTeXRIS

Kazuya Haremaki, Yusuke Koide, Takashi Uneyama, Yuichi Masubuchi, Takato Ishida. 2026-07-28. Stress Drops Associated with Surface Crack Formation in Photo-aged Polypropylene during Three-Point Bending. https://arxiv.org/abs/2607.25582

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

arXiv2026

Slow Dynamics and the Geometry of Jammed Packings

Saddle points in the energy landscape of granular packings dominate the discrete steepest descent dynamics and ultimately determine the path that an out of mechanical equilibrium packing will follow and the resulting stable minimum that it will find. The saddle points that ultimately determine the resulting minima tend to be low-index saddle points. For models with an analytic energy landscape, such as the $p$-spin model, the steepest descent minimization path is affected by higher-index saddle points, which pull the system towards saddle points of decreasing index before arriving at the minima. Here, we examine the steepest descent minimization path of granular packings and compare them to the $p$-spin model. We show that the granular packing steepest descent minimization paths act like their smooth energy landscape counterparts and get attracted by saddle points. The index versus time curves for all models follow a shifted, stretched exponential. We further show that the shape parameter for the granular packings is unchanged when the energy landscape is modified to become analytic (Gaussian potential in a harmonic well) or non-local (Mari-Krzakala-Kurchan). The $p$-spin, on the other hand, has a significantly larger shape parameter. The reason is not due to the dimensionality, packing fraction, nonanalyticity, or the locality of the Hamiltonian of the models. The exact reason for the discrepancy in the shape parameter is \st{still} an unsolved mystery.

cond-mat.soft↗
arXiv2026

A Phase-Field Study of Desiccation Crack Pattern Maturation under Drying-Wetting Cycles

The characteristic intersection angle of the desiccation crack relaxes from near \ang{90} toward \ang{120} under repeated drying--wetting cycles. However, the theoretical understanding of this relaxation is insufficient, especially the modeling of the drying--wetting cycles. Here we introduce a phase-field model of desiccation fracture, extending the model proposed in previous studies by adding crack healing and a scar effect left by past cracks. By repeating drying--wetting cycles in a finite element simulation, we find that the angle distribution develops a growing peak near \ang{120} as the cycle number increases, consistent with experiments. The standard deviation of the intersection angle from \ang{120} relaxes exponentially with a characteristic time of about 2.85 cycles. These results are consistent with experiments, except that the characteristic time is slightly smaller than the experimental value. Crack energy dominates the total energy and also relaxes exponentially with nearly the same characteristic cycle as the angle relaxation. This decay is driven mainly by a shortening of the effective crack length rather than a change in effective fracture toughness.

cond-mat.soft↗
arXiv2026

Kinetics of ferritin crystal formation and melting in acoustically levitated droplets

Understanding protein crystallization pathways is essential for controlling crystallization in structural biology, materials science, and pharmaceutical applications. Classical nucleation theory does not fully capture crystallization processes for several proteins, including ferritin. Here, we combine acoustic levitation with small- and wide-angle X-ray scattering (SAXS and WAXS) to monitor ferritin crystallization in evaporating aqueous polyethylene glycol (PEG) solutions. Acoustic levitation rapidly drives the droplets through a broad range of protein and polymer concentrations, enabling time-resolved measurements of crystallization during evaporation. The scattering data show that ferritin crystals form during evaporation and subsequently lose their crystalline order upon further dehydration. Varying the PEG molecular weight switches between distinct crystallization pathways: one dominated by attractive protein-protein interactions and another dominated by repulsive interactions and excluded-volume effects. Furthermore, we find that lower molecular weight PEG (1000 g/mol) suppresses the dehydration-induced loss of crystalline order observed for higher molecular weight PEG (6000 g/mol), providing a simple strategy for improving protein crystal stability.

cond-mat.soft↗